Title: | Effect of simulated heating of plasma coating and ceramic firing on Ti and Ti-6Al-4V |
Authors: | Kotian, R. Rao, P.P. Bangera, M.K. Madhyastha, P. Srikant, S. |
Issue Date: | 2019 |
Citation: | Journal of Materials Research and Technology, 2019, Vol.8, 5, pp.4699-4704 |
Abstract: | The study was performed to understand the impact of heat in plasma coating and ceramic firing of titanium (Ti) and titanium alloy (Ti-6Al-4V) on their mechanical properties, and microstructure. Standard specimens were prepared to measure tensile strength before and after simulated heating cycles using Instron machine of model 4206 at a crosshead speed of 1 mm/min. Yield strength, ultimate strength, and elongation were recorded. The microstructure was studied using an optical microscope. The mechanical properties, microstructure, and grain size remained the same as that of as-received samples at temperatures of 600 and 700⻰C for both Ti and Ti-6Al-4V. At temperature 800 and 900⻰C decrease in yield strength, and ultimate tensile strength with a change in microstructure was observed. The temperature of plasma coating and ceramic firing that Ti and Ti-6Al-4V metal substrates encounter during the fabrication of coated implants and metal-ceramic restorations do not affect the mechanical properties and microstructure. Above 800⻰C, a significant change in mechanical properties and microstructure is observed. 2019 The Authors. |
URI: | http://idr.nitk.ac.in/jspui/handle/123456789/10850 |
Appears in Collections: | 1. Journal Articles |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.