Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
6 results
Search Results
Item Wetting behavior of lead-free solders on copper substrates(Institution of Engineering and Technology jbristow@theiet.org, 2013) Satyanarayan, S.; Prabhu, K.N.The effect of substrate surface roughness on the wetting behavior of Sn-0.7Cu and Sn-0.3Ag-0.7Cu solder alloys on copper (Cu) substrates was investigated. The contact angles of both solder alloys decreased with increase in substrate surface roughness. The exponential power law (EPL), φ = exp (-KÏ„n), was used to model the relaxation behaviour of solders. Solder spreading kinetics was successfully represented by the (EPL). EPL parameters (K and n) alloy decreased with an increase in surface roughness. Spreading of solder alloys on both substrates exhibited capillary, gravity and viscous regimes. High spreading rates in the capillary regime, moderate in gravity regime and almost constant rates in viscous regimes were observed.Item Wetting behaviour and evolution of microstructure of Sn-Ag-Zn solders on copper substrates with different surface textures(2010) Satyanarayan, S.; Prabhu, K.N.The effect of surface roughness on wetting behaviour and evolution of microstructure of two lead-free solders (Sn-2.625Ag-2.25Zn and Sn-1.75Ag-4.5Zn) on copper substrate was investigated. Both solders exhibited good wettability on copper substrates having rough surface and lower wettabilty on smooth surfaces. The contact angles of solders decreased linearly with increase in surface roughness of the substrate. The exponential power law, ?=exp(-K ?n), was used to model the relaxation behaviour of solders. A high intermetallic growth was observed at the interface particularly on copper substrates with rough surface texture. A thin continuous interface showing scallop intermetallic compounds (IMC) was obtained on smooth surfaces. With an increase in surface roughness, the IMC morphology changed from scallop shaped to needle type at the Sn-2.625Ag-2.25Zn solder/substrate interface and nodular to plate like IMCs for Sn-1.75Ag-4.5Zn solder matrix. Copyright © 2010 by ASTM International.Item Wetting behaviour and evolution of microstructure of Sn-Ag-Zn solders on copper substrates with different surface textures(ASTM International, 2011) Satyanarayan, S.; Prabhu, K.N.The effect of surface roughness on wetting behaviour and evolution of microstructure of two lead-free solders (Sn-2.625Ag-2.25Zn and Sn-1.75Ag-4.5Zn) on copper substrate was investigated. Both solders exhibited good wettability on copper substrates having rough surface and lower wettabilty on smooth surfaces. The contact angles of solders decreased linearly with increase in surface roughness of the substrate. The exponential power law, ?=exp(-KT -1), was used to model the relaxation behaviour of solders. A high intermetallic growth was observed at the interface particularly on copper substrates with rough surface texture. A thin continuous interface showing scallop intermetallic compounds (IMC) was obtained on smooth surfaces. With an increase in surface roughness, the IMC morphology changed from scallop shaped to needle type at the Sn-2.625Ag-2.25Zn solder/ substrate interface and nodular to plate like IMCs for Sn-1.75Ag-4.5Zn solder matrix. Copyright © 2010 by ASTM International.Item Effect of cooling rate during solidification of Sn-9Zn lead-free solder alloy on its microstructure, tensile strength and ductile-brittle transition temperature(Elsevier Ltd, 2012) Prabhu, K.N.; Deshapande, P.; Satyanarayan, S.Solidification rate is an important variable during processing of materials, including soldering, involving solidification. The rate of solidification controls the metallurgical microstructure at the solder joint and hence the mechanical properties. A high tensile strength and a lower ductile-brittle transition temperature are necessary for reliability of solder joints in electronic circuits. Hence in the present work, the effect of cooling rate during solidification on microstructure, impact and tensile properties of Sn-9Zn lead-free solder alloy was investigated. Four different cooling media (copper and stainless steel moulds, air and furnace cooling) were used for solidification to achieve different cooling rates. Solder alloy solidified in copper mould exhibited higher cooling rate as compared to other cooling media. The microstructure is refined as the cooling rate was increased from 0.03 to 25 °C/s. With increase in cooling rate it was observed that the size of Zn flakes became finer and distributed uniformly throughout the matrix. Ductile-to-brittle transition temperature (DBTT) of the solder alloy increased with increase in cooling rate. Fractured surfaces of impact test specimens showed cleavage like appearance and river like pattern at very low temperatures and dimple like appearance at higher temperatures. The tensile strength of the solder alloy solidified in Cu and stainless moulds were higher as compared to air and furnace cooled samples. It is therefore suggested that the cooling rate during solidification of the solder alloy should be optimum to maximize the strength and minimize the DBTT. © 2011 Elsevier B.V.Item Comparison of spreading behaviour and interfacial microstructure in Sn-0·7Cu, Sn-0·3Ag-0·7Cu and Sn-2·5Ag-0·5Cu lead free solder alloys on Fe-42Ni substrate(Maney Publishing michael.wagreich@univie.ac.at, 2013) Satyanarayan, S.; Prabhu, K.In the present work, spreading behaviour and development of interfacial microstructure in Sn- 0·7Cu, Sn-0·3Ag-0·7Cu and Sn-2·5Ag-0·5Cu lead free solder alloys on Fe-42Ni substrates having two different surface textures were investigated. Smooth textured surfaces yielded better wettability than rough surfaces particularly for Sn-0·7Cu solder alloy. Wettability of Sn-0·7Cu solder on rough textured surfaces was found to be poor compared to other solder alloys. Spreading of Sn-0·7Cu solder on substrate surface showed longer viscous regime, Sn-2·5Ag- 0·5Cu solder exhibited shortest viscous regime. Sn-0·3Ag-0·7 solder showed intermediate behaviour. Sn-Cu solder alloy exhibited needle and coarse shaped (Cu,Ni)6Sn5 intermetallics at the interface and in the matrix of the solder alloy on smooth substrate, whereas on rough substrate, formation of only coarse shaped (Cu,Ni)6Sn5 intermetallic compounds (IMCs) was observed. For Sn-0·3Ag-0·7Cu solder alloy, Fe-Ni-Sn and FeSn2 IMCs identified at the interface. (Cu,Ni)6/Sn5 IMCs were found to be less coarser than as observed at Sn-0·7Cu/substrate interface. Sn-2·5Ag-0·5Cu alloy exhibited (Cu,Ni) 3Sn4 and (Cu,Ni)6 Sn5 IMCs at the interface and in the bulk of solder alloy. © 2013 Institute of Materials, Minerals and Mining.Item Effect of purging gas on wetting behavior of Sn-3.5Ag lead-free solder on nickel-coated aluminum substrate(Springer Science and Business Media, LLC, 2013) Prabhu, K.; Varun, M.; Satyanarayan, S.The wetting characteristics of Sn-3.5Ag lead-free solder alloy on nickel-coated aluminum substrates in air (ambient), nitrogen, and argon atmospheres were investigated. The contact angles for the solder alloy obtained under air and argon atmospheres were in the range of 36 -38. With nitrogen atmosphere the contact angle was found to be significantly lower at about 26. Solder solidifying in air exhibited needle-shaped tin-rich dendrites surrounded by a eutectic matrix. The amount of tin dendrites decreased in argon atmosphere. However, the morphology of tin dendrites transformed from needle-shaped to nearly non-dendritic shape as the soldering atmosphere was changed from air to nitrogen. The interfacial microstructures revealed the presence of Ni 3Sn and Ni3Sn4 IMCs at the interface. The enhanced wettability observed under nitrogen atmosphere is attributed to the higher thermal conductivity of nitrogen gas and the formation of higher amount of Ni3Sn IMCs at the interface compared to air and argon atmospheres. © 2012 ASM International.