Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
Search Results
Item Comparison of spreading behaviour and interfacial microstructure in Sn-0·7Cu, Sn-0·3Ag-0·7Cu and Sn-2·5Ag-0·5Cu lead free solder alloys on Fe-42Ni substrate(Maney Publishing michael.wagreich@univie.ac.at, 2013) Satyanarayan, S.; Prabhu, K.In the present work, spreading behaviour and development of interfacial microstructure in Sn- 0·7Cu, Sn-0·3Ag-0·7Cu and Sn-2·5Ag-0·5Cu lead free solder alloys on Fe-42Ni substrates having two different surface textures were investigated. Smooth textured surfaces yielded better wettability than rough surfaces particularly for Sn-0·7Cu solder alloy. Wettability of Sn-0·7Cu solder on rough textured surfaces was found to be poor compared to other solder alloys. Spreading of Sn-0·7Cu solder on substrate surface showed longer viscous regime, Sn-2·5Ag- 0·5Cu solder exhibited shortest viscous regime. Sn-0·3Ag-0·7 solder showed intermediate behaviour. Sn-Cu solder alloy exhibited needle and coarse shaped (Cu,Ni)6Sn5 intermetallics at the interface and in the matrix of the solder alloy on smooth substrate, whereas on rough substrate, formation of only coarse shaped (Cu,Ni)6Sn5 intermetallic compounds (IMCs) was observed. For Sn-0·3Ag-0·7Cu solder alloy, Fe-Ni-Sn and FeSn2 IMCs identified at the interface. (Cu,Ni)6/Sn5 IMCs were found to be less coarser than as observed at Sn-0·7Cu/substrate interface. Sn-2·5Ag-0·5Cu alloy exhibited (Cu,Ni) 3Sn4 and (Cu,Ni)6 Sn5 IMCs at the interface and in the bulk of solder alloy. © 2013 Institute of Materials, Minerals and Mining.Item Effect of purging gas on wetting behavior of Sn-3.5Ag lead-free solder on nickel-coated aluminum substrate(Springer Science and Business Media, LLC, 2013) Prabhu, K.; Varun, M.; Satyanarayan, S.The wetting characteristics of Sn-3.5Ag lead-free solder alloy on nickel-coated aluminum substrates in air (ambient), nitrogen, and argon atmospheres were investigated. The contact angles for the solder alloy obtained under air and argon atmospheres were in the range of 36 -38. With nitrogen atmosphere the contact angle was found to be significantly lower at about 26. Solder solidifying in air exhibited needle-shaped tin-rich dendrites surrounded by a eutectic matrix. The amount of tin dendrites decreased in argon atmosphere. However, the morphology of tin dendrites transformed from needle-shaped to nearly non-dendritic shape as the soldering atmosphere was changed from air to nitrogen. The interfacial microstructures revealed the presence of Ni 3Sn and Ni3Sn4 IMCs at the interface. The enhanced wettability observed under nitrogen atmosphere is attributed to the higher thermal conductivity of nitrogen gas and the formation of higher amount of Ni3Sn IMCs at the interface compared to air and argon atmospheres. © 2012 ASM International.Item Solder joint reliability of Sn-0·7Cu and Sn-0·3Ag- 0·7Cu lead-free solder alloys solidified on copper substrates with different surface roughnesses(2013) Satyanarayan, S.; Prabhu, K.The bond shear test was used to assess the integrity of Sn-0·7Cu and Sn-0·3Ag-0·7Cu lead-free solder alloy drops solidified on copper substrates with smooth and rough surface finishes. Solder alloys solidified on smooth substrates required higher shear force compared to that on rough substrates. Sn-0·3Ag-0·7Cu alloy required higher shear energy than Sn-0·7Cu alloy. Solder alloys solidified on smooth substrate surfaces exhibited complete ductile failure. On rough copper surfaces, solder alloys showed a transition ridge characterized by sheared intermetallic compounds (IMCs) and the presence of dimples. The peak shear strength decreased with increase in contact area of the solder bond on the substrate. Smooth surface and the presence of minor amount of Ag in the solder alloy enhance the integrity of the solder joint. © 2013 Institute of Materials, Minerals and Mining.