Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item A comparative study on enhancer and inhibitor of glycine–nitrate combustion ZnO screen-printed sensor: detection of low concentration ammonia at room temperature(Springer, 2020) Manjunath, G.; Pothukanuri, P.; Mandal, S.We report a comparative study on enhancing and inhibiting the sensing performance of Sr-doped ZnO (Sr0.01 Zn0.99O) and RuO2-activated Sr-doped ZnO heterostructured sensors towards the low concentration (? 50 ppm) of ammonia gas at ambient. Sub-microns sized with high specific surface area, high reactive, oxygen-deficient Sr-doped ZnO particles were synthesized at low temperature (196 °C) through facile glycine–nitrate solution combustion synthesis (SCS) method. Porous, adhered screen-printed film of Sr-doped ZnO with optical bandgap (3.22 eV) was dip-coated using 0.02 M RuCl3 aqueous solution to obtain RuO2 activation. Smaller crystallite size and lesser lattice distortion obtained with Sr-doping in ZnO enhance the gas response (S = 71) towards the 50 ppm of ammonia gas at room temperature. RuO2-activated Sr-doped ZnO sensor associated with lesser oxygen vacancies and a lower concentration of chemisorbed oxygen species due to passivation layer and no-spill-over activity of RuO2, which inhibits the gas response from 71 to 3. Sr-doped ZnO-based sensor shows high selectivity towards ammonia against 50 ppm of volatile organic compound (VOCs) vapor. Expeditious sensor kinetics (response time and recovery time) in the Sr-doped ZnO sensor was observed, in which smaller crystallite size offers a shorter distance for the diffusion of oxygen vacancies (Vo). Ultra-high-sensitive and selective sensors with ease and economical fabrication offer feasibility in industries and domestic applications where detection of the less concentration ammonia vapor is crucial. © 2020, Springer Science+Business Media, LLC, part of Springer Nature.Item Room-temperature detection of ammonia and formaldehyde gases by La xBa1?xSnO3?? (x = 0 and 0.05) screen printed sensors: effect of ceria and ruthenate sensitization(Springer Science and Business Media Deutschland GmbH, 2021) Manjunath, G.; Vardhan, R.V.; Praveen, L.L.; Pothukanuri, P.; Mandal, S.In the present work, gas sensing properties of the screen printed ceria and ruthenate-sensitized BaSnO3 (BSO) with La doping heterostructure sensors towards the detection of ammonia and formaldehyde gases at room temperature were studied. Adhered, porous screen printed films with different morphologies were obtained by depositing the LaxBa1?xSnO3?? (x = 0 and 0.05) powder particles prepared by the polymerized complex method. Ceria and ruthenate sensitization for screen printed LaxBa1?xSnO3?? (x = 0.05) film was processed through dip-coating in the 0.03 M aqueous solution of CeCl3 and RuCl3, respectively. La-doped BaSnO3 (LBSO) sensor with smaller crystallites, needle-like morphology and high concentration of oxygen vacancies exhibited superior gas response of 65 and 29 towards 50 ppm of ammonia and formaldehyde gases, respectively. Superabundant sensitization of ceria and ruthenate reduced the oxygen vacancy and structural open porosity in the LBSO sensor; therefore, the ammonia gas response was decreased from 65 to 14 and 3, respectively, whereas the formaldehyde gas response was reduced to less than 1/6th times the LBSO sensor. Limit of detection of LBSO sensors was estimated to be ~ 1 and ~ 2 ppm against ammonia and formaldehyde, respectively. The presence of fluorite structured phase ceria with high oxygen atoms storage capacity facilitates the rapid oxidization of analyte gases and caused the expeditious response (75 s) and recovery (60 s) in CeOx-sensitized LBSO sensor. This study might give a new insight into the development of doped and sensitized BSO-based gas sensors operating at ambient conditions. © 2021, The Author(s), under exclusive licence to Springer-Verlag GmbH, DE part of Springer Nature.Item Ammonia gas detection by solution combustion-processed pristine & Ti-doped ZnO transparent films: a reverse effect of doping on gas response(Springer, 2023) Vardhan, R.V.; Manjunath, G.; Pothukanuri, P.; Mandal, S.In this contribution, pure, polycrystalline wurtzite crystal structured, spin-coated pristine ZnO and Ti-doped (1, 2, and 3 wt%) ZnO transparent films were accomplished at 400 °C through a facile solution combustion synthesis method. Crystallinity, roughness, and porosity in the pristine film were relatively higher than in the doped films. The demonstrated films were transparent, with ~ 70 to 90% in the visible region. The room temperature detection of ammonia (NH3) gas (25–100 ppm) was recognized in all the films. The pristine film revealed a superior gas response at every concentration of NH3 gas in contrast to all the doped films; it is probably due to comparatively high crystallinity, porosity, more oxygen vacancy concentration (1.788), and high fraction of adsorbed oxygen (20.55%). The film exhibited the highest gas response of 34.7 at 100 ppm of NH3 gas and a limit of detection of ~ 10.7 ppm with superior selectivity towards NH3 gas. Although doping enhanced the transparency but diminished the NH3 gas response due to the combined effect of deterioration in the mentioned properties achieved in pristine film. © 2023, The Author(s), under exclusive licence to Springer Science+Business Media, LLC, part of Springer Nature.Item Tracing of Ammonia Gas by Solution-Combustion-Derived Pristine and Nb-Doped TiO2 Films: Beneficial Impact of Crystallinity and Adsorbed Oxygen on the Gas Response(Springer, 2023) Vardhan, R.V.; Manjunath, G.; Pothukanuri, P.; Mandal, S.The current work delivers room-temperature ammonia (NH3) gas-detectable pristine, Nb-doped TiO2 air- and vacuum-annealed films obtained through the solution-combustion process. Polycrystalline anatase crystal structured films without any dopant oxide phases were processed at 400°C on glass substrates. The crystallinity was higher in pristine films than in doped films; the morphological features were similar in all the films. The films were > 50% transparent, and the estimated optical energy band gap was greater in doped films than in pristine films. All the films detected NH3 gas (25 ppm to 100 ppm) at room temperature, and the gas response was highly dependent on the crystallinity and relative area fraction of adsorbed oxygen (% of OA). The vacuum-annealed pristine film exhibited a better gas response than the other films at all NH3 gas concentrations due to high crystallinity and % of OA (10.15%). The film demonstrated maximum gas response of ~16 towards 100 ppm of NH3 gas and displayed good selectivity. Even though the doping reduced the crystallite size from ~17 nm to ~9 nm, it also diminished the crystallinity of the films, which significantly impacted the deterioration of their gas response. © 2023, The Minerals, Metals & Materials Society.