    Effect of aging and protective coating on the corrosion behavior of 6061 Al / SiCp composite in chloride solutions
    (Trans Tech Publications Ltd ttp@transtec.ch, 2011) Rajasekaran, S.; Udayashankar, N.K.; Nayak, J.
    Metal matrix composites considered especially for marine application are typically aluminum-based. Utilization of the composites in marine environments requires adequate corrosion resistance. In this work, the effect of aging and aluminum as resistive coating on the corrosion behavior of 6061 Al / SiC p composite in 1N and 3.5N NaCl solution in the temperature range of 30°C-50°C is studied by means of electrochemical techniques, scanning electron microscope (SEM) and weight loss measurements. Aging results in precipitation of intermetallics in the matrix, this in turn leads to galvanic and pitting corrosion. Pitting initiation and propagation as the main corrosion mechanism was driven by the aging kinetics which is ruled by the reduction in the retained vacancy concentration and at the same time by dislocation density due to the presence of SiCp. Sputtered aluminum coating on the composite effectively resists the pitting initiation and propagation and hence corrosion process. Also the intermetallic precipitates are unexposed to the Chloride solution by the presence of aluminum coating. Hence aluminum coating acts as corrosion resistive coating for the 6061 Al / SiCp aged composites. © (2011) Trans Tech Publications.
  • No Thumbnail Available
    Item
    Effect of SiC Reinforcement on Microstructure and Mechanical Properties of Aluminum Metal Matrix Composite
    (Institute of Physics Publishing helen.craven@iop.org, 2018) Ajagol, P.; Anjan, B.N.; Marigoudar, R.N.; Preetham Kumar, G.V.
    Aluminum reinforced with silicon carbide composites areextensively used in automobile industries and aerospaceowing to their favourable microstructure and improved mechanical behaviour with respect to pure aluminium but at a lower cost. Aluminium is remarkable for the low density and its ability to resist corrosion. The aim of present study istoevaluate the mechanical and microstructural properties of aluminum with silicon carbide (average particle size 30-45μm) reinforced in varying weight percentages (wt %) ranging from 0-15 wt% in a step of 5% each. Ultimate tensile strength, micro hardness and density of the fabricated composites were investigated as a function of varying SiC wt%. Microstructure analysis was carried out on casted composites using optical microscopy and scanning electron microscopy. From micrographs it is clear that fair distribution of reinforcing particles in the matrix and also observed some clustering and porosity in the cast material. Results revealed that, the addition of SiC reinforcement in the aluminum matrix increases the hardness and ultimate tensile strength gradually from 23 HV to 47 HV and 84 MPa to 130 MPa respectively. © Published under licence by IOP Publishing Ltd.