    Item
    Microstructural characterization and mechanical properties of cast Al-15Zn-2Mg alloy subjected to severe plastic deformation
    (Elsevier Ltd, 2018) Manjunath, G.K.; Udaya Bhat, K.; Preetham Kumar, G.V.
    In the present work, Al-15Zn-2Mg alloy was processed by ECAP technique for grain refinement. The ECAP processing was conducted at 150 °C. Microstructural characterization was carried out in OM, SEM, TEM and XRD. To evaluate the mechanical properties, hardness measurement and tensile tests were conducted at room temperature. Microstructural characterization showed that, ECAP processing leads to decrease in the grain size of the alloy. Also, small amount of dislocations were also observed in the ECAP processed material. After ECAP processing, precipitates nucleation in the material was identified in the XRD analysis. The strength and the hardness values were increased after ECAP processing. After ECAP processing, microhardness of the material is increased from 173 Hv to 252 Hv and the UTS of the material is increased from 166 MPa to 362 MPa. After tensile testing, fracture surface of the cast material showed dendritic structure and the fracture surface of the ECAP processed material showed dimples. © 2018 Elsevier Ltd. All rights reserved.
  • No Thumbnail Available
    Item
    Effect of equal channel angular pressing on the microstructure and mechanical properties of Al-10Zn-2Mg alloy
    (American Institute of Physics Inc. subs@aip.org, 2018) Manjunath, G.K.; Preetham Kumar, G.V.; Bhat, K.U.
    The current investigation is focused on evaluating the mechanical properties and the microstructure of cast Al-10Zn-2Mg alloy processed through equal channel angular pressing (ECAP). The ECAP processing was attempted at minimum possible processing temperature. Microstructural characterization was carried out in optical microscopy, scanning electron microscopy, transmission electron microscopy and X-ray diffraction analysis. Hardness measurement and tensile tests were employed to estimate the mechanical properties. Experimental results showed that, ECAP processing leads to noticeable grain refinement in the alloy. Reasonable amount of dislocations were observed in the ECAP processed material. After ECAP processing, precipitates nucleation in the material was detected in the XRD analysis. ECAP leads to considerable enhancement in the mechanical properties of the material. After ECAP processing, microhardness of the material is increased from 144 Hv to 216 Hv. Also, after ECAP processing the UTS of the material is increased from 140 MPa to 302 MPa. The increase in the mechanical properties of the alloy after ECAP processing is due to the dislocation strengthening and grain refinement strengthening. Finally, fracture surface morphology of the tensile test samples also studied. © 2018 Author(s).
  • No Thumbnail Available
    Item
    Severe plastic deformation of Al-15Zn-2Mg alloy: Effect on wear properties
    (Trans Tech Publications Ltd ttp@transtec.ch, 2019) Manjunath, G.K.; Bhat, K.U.; Preetham Kumar, G.V.
    In the present work, Al-Zn-Mg alloy having highest zinc content was deformed by one of the severe plastic deformation (SPD) technique, equal channel angular pressing (ECAP) and effect of ECAP on the microstructure evolution and the wear properties were studied. ECAP was performed in a split die and the channels of the die are intersecting at an angle of 120°. ECAP was attempted at least possible temperature and the alloy was successfully ECAPed at 423 K. Below this temperature samples were failed in the first pass itself. After ECAP, significant drop in the grain size was reported. Also, ECAP leads to significant raise in the microhardness of the alloy. Predominantly, after ECAP, upsurge in the wear resistance of the alloy was noticed. To figure out the response of ECAP on the wear properties of the alloy; worn surfaces of the wear test samples were analyzed in SEM. © 2019 Trans Tech Publications Ltd, Switzerland.