    Evaluation of microstructure and mechanical properties of multi axial forged lm2 aluminum alloy
    (Trans Tech Publications Ltd ttp@transtec.ch, 2019) Sajjan, S.S.; Kulkarni, M.V.; Ramesh, S.; Sharath, P.C.; Sangamesh, R.; Kumar, A.; Rajesh, R.
    Light metal Al alloys are presently used in aerospace and industrial applications. Hence, in the present study choice of material will be LM2 aluminum alloy and processed by multi-axial forging (MAF) technique at ambient temperature for different number of passes with an equivalent strain of 0.18, 0.36 and 0.54. Microstructural analysis was carried out on unprocessed and processed samples with scanning electron microscopy (SEM). As the number of MAF pass increases the average grain size was reduced because of plastic deformation by plane strain condition. Mechanical properties like Vickers hardness (VHN), tensile and compression test were carried out. Ultimate tensile strength (UTS) was increased after each pass of MAF due to strain hardening effect. After 3 MAF passes the compression strength was reached to maximum of 495 MPa as compared to as received sample 315 MPa and hardness, increased to 81 VHN as compared to 55 VHN for the received samples. The fractography analysis was explained using SEM images. As the number of passes increases dimple size reduces as compared to as received samples and which will be revealing the ductile mode of fracture. © 2019 Trans Tech Publications Ltd, Switzerland.
  • No Thumbnail Available
    Item
    Effect of Mechanical properties on Multi Axially Forged LM4 Aluminium Alloy
    (Elsevier Ltd, 2020) Sajjan, S.S.; Kulkarni, M.V.; Ramesh, S.; Sharath, P.C.; Kumar, V.; Rajole, S.
    Commercially available LM4 Aluminum alloy was subjected through Severe Plastic Deformation (SPD) method by Multi-Axial Forging Process (MAF) in ambient temperature. In this process, the material was processed successfully up to 5 Passes and mechanical properties such as tensile strength, compression strength and hardness of the as received and processed samples at ambient temperature were evaluated. The MAF processed sample result showed that the ultimate strength, percentage elongation and compression strength improved by 55 MPa, 3.75% and 162 MPa respectively as compared with the unprocessed sample. Hardness also increased with the increase in the number of passes. In the case of microstructure, grain size reduced from 110 μm to 8 μm after subjecting the sample to MAF. Fractography explains the nature of the fracture from received to processed samples by decreasing the size of the dimple and the type of fracture observed was ductile in nature. Improvement in strength and hardness of processed samples was observed due to the grain refinement and high amount of density dislocation in the material during MAF. © 2018 Elsevier Ltd.