Conference Papers
Permanent URI for this collectionhttps://idr.nitk.ac.in/handle/123456789/28506
Browse
Search Results
Item Laboratory Investigation of Lateritic Soil Stabilized with Arecanut Coir Along with Cement and Its Suitability as a Modified Subgrade(Springer Science and Business Media Deutschland GmbH, 2023) Chethan, B.A.; Lekha, B.M.; Ravi Shankar, A.U.If a pavement is constructed on weak soil, its lifespan drastically reduces due to the low strength induced by moisture-induced destresses. Such soils may undergo considerable changes in volume. In order to modify these properties, soil stabilization can be done. By stabilizing the soil along with the improvement in strength, its durability can be increased. Stabilization may be of chemical or mechanical type. In this investigation, lateritic soil was stabilized using 0.2–1% arecanut coir, and its compaction characteristics were evaluated. The lateritic soil is found to be nondurable. The reinforcement alone could not improve the strength and durability effectively. Therefore, 3% binding agent ordinary Portland cement (43 grade) was added to the mix. Due to cement stabilization, UCS and CBR values were improved, and the optimum values were observed at 0.6% arecanut coir dosage. The addition of cement has resulted in a change in silica, alumina, and calcium oxide contents, thereby contributing to the formation of hydration products. The samples with 1% coir and cement have completed 12 wet–dry cycles, but the weight loss observed was >14%. All the specimens showed low soil loss under freeze–thaw cycles. The performance of cured specimens under fatigue loading was satisfactory. Since the specimens could not pass wet–dry durability criteria, they can be considered for modified subgrade. © 2023, The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd.Item Alkali Activated Black Cotton Soil with Partial Replacement of Class F Fly Ash and Areca Nut Fiber Reinforcement(Springer Science and Business Media Deutschland GmbH, 2023) Chethan, B.A.; Ravi Shankar, A.U.; Chinnabhandar, R.K.; Kumar, D.H.Alkali activation has received great attention for improving the soil properties with suitable precursor materials. Industrial byproduct class F fly ash was suitably utilized to improve Black Cotton (BC) soil properties along with ordinary Portland cement by various researchers. However, the CO2 emission associated with cement production has enforced the evaluation of alternative binders. Laboratory investigations were conducted on BC soil by admixing various fly ash dosages (0–50%) and reinforcing the mix with 0.5% areca nut fiber. Alkali activator solution prepared using 8 molar sodium hydroxide solution (SH) and sodium silicate solution (SS) at 1.5 SS/SH ratio showed significant improvement in Unconfined Compressive Strength (UCS) of stabilized BC soil on 7 and 28 days curing. The reinforcement was effective in improving the flexural strength of stabilized mixes. Exorbitant unsoaked California Bearing Ratio (CBR) values were observed on 28 days of curing. However, the samples could retain low soaked CBR values despite reinforcement. Scanning Electron Microscope (SEM) images showed the reduction of shrinkage cracks and strong bonding of fibers in the stabilized mix. X-Ray Diffraction (XRD) patterns evidenced the formation of various hydration products due to the alkali reaction, which resulted in the high strength gain of mixes at ambient temperature curing. The leaching of mineral constituents from the set mix lead to the failure of durability samples. Due to nondurability, the alkali activation with a selected precursor cannot suit pavement materials requirements. © 2023, The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd.