Book Chapters
Permanent URI for this collectionhttps://idr.nitk.ac.in/handle/123456789/28507
Browse
2 results
Search Results
Item Durability studies on glass fiber reinforced concrete(Springer, 2019) George, R.M.; Das, B.B.; Goudar, S.K.In the present experimental study, glass fibers were used in varying dosages of 0.5, 1.0, and 1.5% of cement content (by weight) as partial cement replacement to cement in concrete mix. The effect of different dosage of glass fibers on the bond strength between steel and concrete in reinforced concrete was investigated. As a part of durability study, the combined effect of marine environment and varying levels of pH on the ultimate bond strength retention and compressive strength retention of glass fiber reinforced concrete was also studied. Durability studies were carried out by exposing the 28-day cured cubical specimens into marine environment having different pH levels (1, 4, 7, 10 and 13). The salt solution was simulated in the laboratory by adding 3.5% NaCl to the tap water. Calculated amount of sulphuric acid was added to salt solution to maintain pH of 1 and 4 in marine environment. Similarly, calculated amount of sodium hydroxide was added to salt solution to maintain pH of 10 and 13 in marine environment. The specimens were exposed to aggressive environment for a period of 60 and 90 days. As the fiber dosage increased the workability reduced, and 1.5% fiber dosage had the least slump value. The addition of glass fibers had very minimal influence on compressive strength of glass fiber reinforced concrete. The ultimate bond strength of concrete increased due to the addition of glass fibers. The increase in ultimate bond strength was confirmed through SEM images which shows proper bonding between cement paste and glass fibers. As for as the exposure studies are concerned, 1.0% fiber dosage of glass fiber reinforced concrete had shown better compressive strength and ultimate bond strength retention compared to 0.5 and 1.5% fiber dosage. The pH of the marine environment has a decisive influence on the compressive strength retention and bond strength retention. Exposure to marine environment with pH 1 suffered severe loss in compressive strength and ultimate bond strength with very low strength retention values. However, exposure to marine environment with pH 10 and 13 had minimal strength losses with higher values of compressive strength and ultimate bond strength retention. Increase in exposure period to aggressive media leads to decrease in compressive strength and ultimate bond strength, but the strength retention values for glass fiber reinforced concrete were comparatively better compared to control concrete. © Springer Nature Singapore Pte Ltd. 2019.Item A Review on Mechanical and Microstructure Properties of Reinforced Concrete Exposed to High Temperatures(Springer, 2021) Goudar, S.K.; Santhosh, S.K.; Das, B.B.This paper presents the recent research progress on the response of concrete exposed to fire or high temperatures. The main highlight of this review paper is a compilation of previously reported data regarding the variations in mechanical properties and microstructure properties of concrete when exposed to high temperatures. The concrete structures get deteriorated at the macro- and microscopic levels due to high-temperature exposure. The macro-level damages can be measured with degradation in mechanical properties such as the reduction in compressive strength, weight loss, changes in elastic properties, reduction of bond strength in reinforced concrete, etc. The macro-cracks on the surface of concrete causes spalling which can be observed after exposing the concrete samples to more than 300 ℃. The compressive strength of the concrete reduces slightly till 400 ℃, and when the temperature increased to 600 ℃, there was an exponential reduction in the compressive strength of concrete. Another important parameter is bond strength degradation, which plays a crucial role in durability issues. To understand the deterioration phenomenon and changes in mechanical properties, the changes at the level of the microstructure of concrete need to be understood. Dehydration of products causes deterioration of mechanical properties and weight loss of concrete when exposed to high temperatures. At different temperatures, the microstructure changes and the response of hydration products such as calcium hydroxide (CH), CSH gel, unhydrated cement and capillary water reported by previous researchers are compiled and discussed. © 2021, Springer Nature Singapore Pte Ltd.