    Influence of Impact Angle and Temperature on Solid Particle Erosion Behavior of Titanium-31
    (Springer Nature, 2024) Behera, N.; Chandramouli, T.V.; Aprameya, C.R.; Ramesh, M.R.
    The present work shows the effects of impact angles and temperatures on volumetric erosion loss of titanium-31 alloy. An erosion tester was used to perform the erosion tests with temperatures (200, 400, 600, and 800 °C) and impact angles (30°, 60°, and 90°). The alumina particles (Al2O3) are used as an erodent particle with an average particle size of 50 μm. The microhardness, porosity, and surface roughness of titanium-31 alloy are evalu-ated. SEM/EDS and XRD were used to analyze tita-nium-31 alloy eroded samples. The weight loss method and 3D profilometer determined the volumetric erosion loss. The microhardness of titanium-31 alloy is found to be 337 ± 15HV0.3. The Volumetric erosion loss of tita-nium-31 alloy increased with increasing temperatures from 200 to 800 °C, whereas decreased with increasing impact angle from 30° to 90° for all temperatures. The volumetric erosion loss is higher at a 30° impact angle and lower at a 90° impact angle for all temperatures. As a result, titanium-31 alloy shows the ductile erosion mode for all temperatures. The volumetric erosion loss at 30° impact angles is due to micro-cutting and plough-ing, whereas deep crater, groove, and raised lips are for 90° impact angles. The results of volumetric erosion loss obtained by the weight loss method exhibit a good cor-relation with a 3D optical profilometer. © The Author(s), under exclusive license to Springer Nature Switzerland AG 2024.
  • No Thumbnail Available
    Item
    Tribological Performance of Fe-Based Composite Coatings Under Elevated Temperature Conditions
    (Springer, 2025) Chandramouli, T.V.; Joladarashi, S.; Ramesh, M.R.
    The present study investigated the tribological performance of Fe-based coatings reinforced with carbides onto a maraging steel substrate using the HVOF spray technique. These materials are widely used in manufacturing various components in the aerospace and energy sectors. Commercially available SS316L and 17-4PH are reinforced with WC–Co feedstock powders to deposit these composite coatings on maraging steel substrate. The dry sliding wear tests were conducted using the ball-on-disc tribometer at varying temperatures (25 and 300 °C) with 10 N normal load using an alumina ball (Al2O3) as the counter body. The study includes micro-hardness, porosity, density, bond strength, and surface roughness of the coatings. The samples subjected to wear testing were analyzed using SEM/EDS and XRD techniques, and the wear scar volume was measured using a 3D profilometer to calculate the volume metric loss. The wear rate of SS316L30%WC–Co is 64.46% lower than that of 17-4PH30%WC–Co at room temperature and 67.33% lower at 300 °C under a load of 10 N. At room temperature, the worn surface exhibited abrasive wear, while at 300 °C, adhesive wear and oxidative wear were observed owing to the formation of protective layers. Therefore, SS316L-30%WC–Co demonstrates superior wear resistance compared to 17-4PH-30%WC–Co and offers enhanced mechanical strength, particularly in challenging environments. The deposition of these coatings effectively protects the maraging steel substrate. © The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd. 2025.