Prabhakar, N.Isloor, A.M.Farnood, R.Fauzi Ismail, A.2026-02-032025Separation and Purification Technology, 2025, 358, , pp. -13835866https://doi.org/10.1016/j.seppur.2024.130348https://idr.nitk.ac.in/handle/123456789/20225The bioaccumulation of heavy metal ions is a serious concern for researchers. The dyes and heavy metal ions also aquatic life impacting the biodiversity adversely. Synthesis of novel MIL-53(Fe)-PSBMA particles, and its incorporation into PVDF-based thin-film composite membranes is the crux of this work. Firstly, H<inf>2</inf>N-MIL-53(Fe) was synthesized by metal displacement reaction which was then modified into MIL-53(Fe)-PSBMA brushes. The brushes were synthesized by atom transfer radical polymerization method. The amine groups of the NH<inf>2</inf>-MIL-53(Fe) help connecting the MOF to the polymeric moiety. The as-synthesized material and the fabricated TFCs were characterized by BET, FTIR, XRD, XPS, TGA, AFM, FE-SEM, zeta potential, and DLS particle sizer. The presence of sulphur groups on the XPS spectrum of modified MOF ensured the successful polymer grafting on it. Zwitterionic moieties have both positive and negative charges within a single molecule which gave a resultant zeta potential of ?13.1 mV for the brushes. A pure water flux of 26.32 Lm?2 h?1 and 97.33 %, 95.19 %, 82.06 %, and 78.47 % rejections for Pb2+, Hg2+, As3+, Cd2+ ions and 96.23 % and 94.04 % rejection for 100 ppm reactive black-5 and sunset yellow dyes respectively were obtained for the optimized membrane having 0.035 wt% loading of zwitterionic MOF. This result was attributed to the enhanced membrane hydrophilicity which was also correlated with contact angle and water uptake studies. © 2024 Elsevier B.V.Atom transfer radical polymerizationFourier transform infrared spectroscopyGrafting (chemical)Heavy metalsIronMetal ionsNafion membranesNear infrared spectroscopyStripping (dyes)X ray absorption spectroscopyDye removalHeavy metal ionHeavy metal removalInterfacial polymerizationMetalorganic frameworks (MOFs)P.V.D.FSynthesisedThin film composite membranesZwitterionZwitterionicsComposite membranes