Naik, G.M.Gote, G.D.Narendranath, S.2020-03-302020-03-302018Materials Today: Proceedings, 2018, Vol.5, 9, pp.17763-17768https://idr.nitk.ac.in/handle/123456789/8723This research paper investigates the microstructure evolution and hardness variation of wrought AZ80 magnesium alloy after each ECAP passes. The strengthening effect of AZ80 alloy was examined after post-ECAP aging treatment. Alloys were severely deformed through equal channel angular press at 533K using route Bc with a die channel angle (?) 1100 and corner angle (?) 300. Subsequently, the microstructural characterization was studied using optical microscope (OM) and scanning electron microscope (SEM). Further, post-ECAP aging treatment at 523K for 6h and 12h was performed and microhardness of the specimens was measured. It was found that the grain refinement through thermo-mechanical processing of ECAP and Post-ECAP treatment significantly improves the microhardness of the Mg alloy, which directly influences the properties of wrought AZ80 magnesium alloy. � 2018 Elsevier Ltd. All rights reserved.Book chapter