Title: | Hot dip aluminizing of 9Cr-1Mo steels and their heat treatment |
Authors: | Patel, J. Huilgol, P. Jamnapura, N. Udaya, Bhat, K. |
Issue Date: | 2015 |
Citation: | Materials Science Forum, 2015, Vol.830-831, , pp.143-146 |
Abstract: | Coupons of 9Cr-1Mo steels of type SA 387 Grade 9 class 2 were hot dip aluminized using Al bath at a temperature of 700 �C for 30 seconds. The samples were further heat treated at 750 �C for durations of 1, 3 and 5 hours, respectively. The samples were characterized using X-ray diffractometry, scanning electron microscopy and energy dispersive spectroscopy. The investigation showed that as coated samples contain an aluminum top coat, a reaction layer and substrate material. Within the reaction layer, two distinct regions corresponding to Fe2Al5 and Fe4Al13 were identified. Chromium up to 2 at% was observed. After heat treatment Al coat was not existing. Two distinct layers, corresponding to a thick Fe2Al5 and a thin FeAl were observed at shorter heat treatment duration. Under longer heat treatment durations, multiple phases, namely, Fe2Al5, FeAl, Fe3Al and solid solution of Al in Fe were observed. � (2015) Trans Tech Publications, Switzerland. |
URI: | http://idr.nitk.ac.in/jspui/handle/123456789/8211 |
Appears in Collections: | 2. Conference Papers |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.