Influence of friction and back stresses evolution on cyclic softening of laser powder bed fusion Ti-6Al-4V ELI alloy

Abstract

Laser Powder Bed Fusion (LPBF) of Ti-6Al-4V ELI enables the fabrication of complex and individualized load-bearing patient-specific implants (PSI). These PSI are subjected to cyclic loading, which necessitates their fatigue performance evaluation. In this work, the fatigue properties of LPBF Ti-6Al-4V ELI in heat-treated conditions were characterized by studying the low cycle fatigue (LCF) behavior and underlying deformation mechanism. The fully reversed strain-controlled fatigue tests were performed at various strain amplitudes at room temperature. The ratio of fatigue life of conventional wrought alloy and LPBF Ti-6Al-4V ELI at the lowest (0.8 %) and the highest (1.8 %) strain amplitudes were found to be approximately 2.7 and 4.5, respectively. Further, the softening response during fatigue loading was correlated to the variation in the back and friction stresses. The TEM observations revealed that the dislocation pileup along α/β interfaces caused an increase in dislocation density, which drives the increase in back stress. However, the ease of slip transmission at high strain amplitude (1.8 %) reduced the heterogeneity between α and β phases, causing a decrease in the back stress. The TEM observations further suggested that the dislocation annihilation and subsequent rise in dislocation-free zones in α-phase reduced the friction stress at all strain amplitudes, which resulted in cyclic softening of LPBF Ti-6Al-4V ELI. © 2024 Elsevier B.V.