Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
43 results
Search Results
Item Electrodeposition of Sn-Ni alloy coatings and their characterization(Trans Tech Publications Ltd ttp@transtec.ch, 2015) Shetty, S.; Hegde, A.C.A new alkaline bath has been proposed for deposition of bright Sn-Ni alloy coatings on mild steel (MS). Depositions were carried out at different current densities (c.d.) and their corrosion behaviors were studied in 5% NaCl solution by electrochemical AC and DC methods. Sn-Ni coating, deposited at low c.d. i.e. at 1.0 A/dm2 was found to be the most corrosion resistant compared to those at other higher c.d., even up to 4.0 A/dm2. This least corrosion rate (CR) is attributed to high wt. % Sn in the deposit. Increase of CR at high c.d. range is due to decrease of wt. % Sn, explained by the observed anomalous type of codeposition, followed by the bath. Regardless of the deposition c.d., the bath developed bright coatings, inherent of Sn-Ni alloy. Experimental results are discussed taking in account of the phase structure, composition and surface morphology of the coatings, evidenced by X-ray diffraction (XRD), Energy Dispersive X-ray (EDX) and Scanning Electron Microscopy (SEM) analysis. © (2015) Trans Tech Publications, Switzerland.Item Electrodeposited Ni-P alloy thin films for alkaline water splitting reaction(Institute of Physics Publishing michael.roberts@iop.org, 2016) Elias, L.; Damle, V.H.; Hegde, A.Ni-P alloy thin films was developed as a robust electrode material for alkaline water splitting for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER), through electrodeposition technique. The influence of alloy composition, achieved through induced codeposition of the reluctant non-metal, i.e. phosphorous (P) on its electrocatalytic activity was studied, and arrived at the best composition of alloy for HER and OER. The water splitting efficacy of the alloy films was tested in 1.0 M KOH using electrochemical methods such as cyclic voltammetry and chronopotentiometry. The experimental observation shows that the alloy thin film with 9.0 wt.% of P and 4.2 wt.% of P are the best electrode materials for HER and OER, respectively. The electrocatalytic performance of alloy films towards HER and OER were related to its surface topography, composition and crystal structure through field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) analyses, respectively. © Published under licence by IOP Publishing Ltd.Item A comparative study on the electrocatalytic activity of electrodeposited Ni-W and Ni-P alloy coatings(Elsevier Ltd, 2018) Elias, L.; Hegde, A.Bright Ni-W and Ni-P alloy coatings were synthesized through direct electrolysis from an aqueous alkaline citrate bath. The effect of alloying elements, W and P, on the electrocatalytic activity of Ni was studied, based on their induced codeposition behavior and related to the composition, structure and surface morphology of the developed coatings. The electrocatalytic activity of the alloy coatings towards hydrogen evolution reaction (HER) was studied using electrochemical techniques such as cyclic voltammetry (CV) and chronopotentiometry (CP), in 1. M KOH medium. A comparison of the electrocatalytic efficiencies of these Ni-based alloys was made in consideration with its physical and electrochemical characteristics. The obtained results showed that the alloying of Ni with W gives superior properties towards HER, attributed by its better hydrogen adsorption energy than in Ni-P alloy. The surface appearance, chemical composition and phase structure of the coatings were studied using SEM, EDS and XRD analyses, respectively. © 2018 Elsevier Ltd. All rights reserved.Item Optimization of electrophoretic deposition of alumina onto steel substrates from its suspension in iso-propanol using statistical design of experiments(2008) Mohanty, G.; Besra, L.; Bhattacharjee, S.; Singh, B.P.Statistical design of experiments was used to investigate the effect the process parameters on electrophoretic deposition (EPD) of alumina onto steel substrates from its suspension in iso-propanol. The process parameters considered were (i) concentration of particles in the suspension (solid loading), (ii) electrode separation, (iii) applied potential, and (iv) deposition time on the quantity of ceramic particles electrophoretically deposited. A 24 full factorial matrix, with four repetitions of the center point, was used to develop the predictive regression equation for deposition of alumina per unit area of the electrode in the design space. The results show that particle concentration has the most dominant effect with more than 50% contribution to the deposited amount. A good correlation was obtained between predicted and experimental values suggesting that the model can predict data accurately in the experimental matrix. © 2007 Elsevier Ltd. All rights reserved.Item Development of Zn-Co alloy coatings by pulsed current from chloride bath(2008) Thangaraj, V.; Udayashankar, N.K.; Hegde, A.Zinc-M (where M = Ni, Co and Fe) alloy is of great interest owing to their better mechanical and corrosion properties compared with pure zinc coatings. Corrosion resistance of Zn-Co alloy coatings can be improved considerably by pulse plating. The paper details the optimization of Zn-Co alloy bath using pulsed current and details the superiority of pulse plating over direct current plating. Electroplating of Zn-Co alloys over mild steel was carried out under different conditions of pulse parameters like duty cycle, frequency and peak current density. The production and properties of the deposits were found to be influenced by pulse parameters employed. Within the ranges studied, the bath follows anomalous codeposition with preferential deposition of less noble zinc. The influence of current density on %wt. of Co in the deposit and cathode current efficiencies was studied. It was observed that the deposit at average current density of 5.0 A.dm-2, 50% duty cycle and 100 Hz frequency showed excellent corrosion resistance with fine structure. The peak performance of pulse electrodeposit against corrosion was attributed to the change in the surface homogeneity as evidenced by scanning electron microscope (SEM) image. The drastic decrease of corrosion rate in pulse electrodeposit was attributed to the formation of semiconductor films on the surface as supported by impedance spectroscopy signals.Item Corrosion behavior of composition modulated multilayer Zn-Co electrodeposits produced using a single-bath technique(2009) Thangaraj, V.; Eliaz, N.; Hegde, A.Composition modulated alloy (CMA) electrodeposits of Zn-Co were produced from acid chloride baths by the single-bath technique. Their corrosion behavior was evaluated as a function of the switched cathode current densities and the number of layers. The process was optimized with respect to the highest corrosion resistance. Enhanced corrosion resistance was obtained when the outer layer was slightly richer with cobalt. At the optimum switched current densities 40/55 mA cm-2, a coating with 600 layers showed ~6 times higher corrosion resistance than monolithic Zn-Co electrodeposit having the same thickness. The CMA coating exhibited red rust only after 1,130 h in a salt-spray test. The increased corrosion resistance of the multilayer alloys was related to their inherent barrier properties, as revealed by Electrochemical Impedance Spectroscopy. The corrosion resistance was explained in terms of n-type semiconductor films at the interface as supported by Mott-Schottky plots. © 2008 Springer Science+Business Media B.V.Item Electrodeposition and characterization Zn-Co alloy(2009) Hegde, A.; Thangaraj, V.The present work details optimization of a stable acid chloride bath for electroplating of bright Zn-Co alloy on mild steel using gelatin and glycine as additives. It was found that the addition of gelatin along with glycine changed the deposition pattern markedly. A suitable bath has been formulated using conventional Hull cell experiments. The bath under plating conditions were found to exhibit anomalous codeposition with preferential deposition of less noble (zinc) over more noble (cobalt) as characterized by Zn-Fe group metal alloys. Investigation revealed that the current density (c.d.), temperature, and pH of the bath have strong effect on the composition of the deposit. Influence of bath constituents and operating parameters on appearance and composition of deposits were studied as measure of their performance against corrosion. A variety of deposits were obtained and their corrosion resistances were measured by Tafel method with/without chrome passivation. Experimental results demonstrated the fact that the corrosion resistances of Zn-Co alloys increased with percent of Co in the deposit except at very high c.d. This is due to the fact at very high c.d. the deposit becomes very porous and thick as evidenced by SEM image. The formation of Zn-Co alloy is confirmed by EDAX analysis. A stable chloride bath for Zn-Co alloy deposition has been proposed and discussed. The formation of passive film on chromatization is indicated by almost same E corr value of all Zn-Co electroplates irrespective of the current densities at which they have been deposited. © 2009 Pleiades Publishing, Ltd.Item Electrodeposition of high performance multilayer coatings of Zn-Co using triangular current pulses(2010) Yogesha, S.; Hegde, A.C.Compositionally modulated alloy (CMA) coatings of Zn-Co were electrodeposited on to mild steel from an acid chloride bath containing thiamine hydrochloride, as an additive. Electroplating was carried out galvanostatically from a single bath containing Zn2+ and Co2+ ions. Gradual change in composition in each layer was effected by triangular current pulses, cycling between two cathode current densities. Compositionally modulated alloy coatings were developed under different conditions of cyclic cathode current density and number of layers, and their corrosion resistances were evaluated by potentiodynamic polarisation and electrochemical impedance spectroscopy. The formation of multilayer and corrosion mechanism was analysed using scanning electron microscopy. The corrosion resistances of CMA and monolithic alloy coatings were compared with that of the base metal. Compositionally modulated alloy coating at optimal configuration, represented as (Zn-Co) 2•0/4•0/300, was found to exhibit ?80 times better corrosion resistance compared with monolithic (Zn-Co)3•0 alloy, deposited for the same length of time from the same bath. Improved corrosion resistance was attributed to the formation of n-type semiconductor film at the interface, supported by Mott-Schottky plots. Decrease in corrosion resistance at high degree of layering was found, and is due to lower relaxation time for redistribution of solutes in the diffusion double layer, during plating. © 2010 Maney Publishing.Item Electroplating and characterization of Zn-Ni, Zn-Co and Zn-Ni-Co alloys(2010) Eliaz, N.; Venkatakrishna, K.; Hegde, A.C.Zn-Ni, Zn-Co and Zn-Ni-Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency was higher than 90%. As the current density was increased or the bath temperature was decreased, the concentration of the nobler metal in the coating increased. Both concentrations of Ni and Co in the ternary alloy increased as the applied current density was increased. Nickel and cobalt were found to have a synergistic catalytic effect. The thickness of all coatings increased as the applied current density was increased. The hardness increased with current density to a peak value, and then decreased. The rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, while the rates of Ni and Co deposition were not. The anomalous codeposition was explained by the great difference between the exchange current densities of Zn and the iron-group metal. Potentiodynamic polarization scans and electrochemical impedance spectroscopy showed that the corrosion resistance of the ternary Zn-Ni-Co alloy coatings was approximately 10 times higher than that of Zn-Ni and 7 times higher than that of Zn-Co. The improved corrosion resistance of the ternary alloy was attributed to its surface chemistry, phase content, texture, and surface morphology. The ternary Zn-Ni-Co coating may thus replace the conventional Zn-Ni and Zn-Co coatings in a variety of applications. © 2010 Elsevier B.V.Item Electrodeposition of Zn-Ni, Zn-Fe and Zn-Ni-Fe alloys(2010) Hegde, A.C.; Venkatakrishna, K.; Eliaz, N.Zn-Fe, Zn-Ni and Zn-Ni-Fe coatings were electrodeposited galvanostatically on mild steel from acidic baths (pH 3.5) consisted of ZnCl2, NiCl2, FeCl2, gelatin, sulfanilic (p-aminobenzenesulfonic) acid and ascorbic acid. Cyclic voltammetry showed that the effect of gelatin was more pronounced than that of sulfanilic acid, and that the deposition of the ternary alloy behaved differently from the deposition of the binary alloys. In all three systems, the Faradaic efficiency was higher than 88%, the rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, and the deposition was of anomalous type. For each applied current density, the concentrations of Ni and Fe in the ternary alloy were higher than the corresponding concentrations in the binary alloys. The hardness of Zn-Ni coatings was the highest, while that of Zn-Fe coatings was the lowest. The Zn-Ni-Fe coatings were the smoothest, had distinguished surface morphology, and contained ZnO in the bulk, not just on the surface. The lowest corrosion rate in each alloy system (214, 325 and 26?m year-1 for Zn-Ni, Zn-Fe and Zn-Ni-Fe, respectively) was characteristic of coatings deposited at 30, 30 and 40mAcm-2, respectively. The higher corrosion resistance of the ternary alloy was also reflected by a higher corrosion potential, a higher impedance and a higher slope of the Mott-Schottky line. The enhanced corrosion behavior of the ternary alloy was thus attributed to its chemical composition, phase content, roughness and the synergistic effect of Ni and Fe on the n-type semiconductor surface film. © 2010 Elsevier B.V.