Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
36 results
Search Results
Item Electrodeposition and characterization Zn-Co alloy(2009) Hegde, A.; Thangaraj, V.The present work details optimization of a stable acid chloride bath for electroplating of bright Zn-Co alloy on mild steel using gelatin and glycine as additives. It was found that the addition of gelatin along with glycine changed the deposition pattern markedly. A suitable bath has been formulated using conventional Hull cell experiments. The bath under plating conditions were found to exhibit anomalous codeposition with preferential deposition of less noble (zinc) over more noble (cobalt) as characterized by Zn-Fe group metal alloys. Investigation revealed that the current density (c.d.), temperature, and pH of the bath have strong effect on the composition of the deposit. Influence of bath constituents and operating parameters on appearance and composition of deposits were studied as measure of their performance against corrosion. A variety of deposits were obtained and their corrosion resistances were measured by Tafel method with/without chrome passivation. Experimental results demonstrated the fact that the corrosion resistances of Zn-Co alloys increased with percent of Co in the deposit except at very high c.d. This is due to the fact at very high c.d. the deposit becomes very porous and thick as evidenced by SEM image. The formation of Zn-Co alloy is confirmed by EDAX analysis. A stable chloride bath for Zn-Co alloy deposition has been proposed and discussed. The formation of passive film on chromatization is indicated by almost same E corr value of all Zn-Co electroplates irrespective of the current densities at which they have been deposited. © 2009 Pleiades Publishing, Ltd.Item Electroplating and characterization of Zn-Ni, Zn-Co and Zn-Ni-Co alloys(2010) Eliaz, N.; Venkatakrishna, K.; Hegde, A.C.Zn-Ni, Zn-Co and Zn-Ni-Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency was higher than 90%. As the current density was increased or the bath temperature was decreased, the concentration of the nobler metal in the coating increased. Both concentrations of Ni and Co in the ternary alloy increased as the applied current density was increased. Nickel and cobalt were found to have a synergistic catalytic effect. The thickness of all coatings increased as the applied current density was increased. The hardness increased with current density to a peak value, and then decreased. The rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, while the rates of Ni and Co deposition were not. The anomalous codeposition was explained by the great difference between the exchange current densities of Zn and the iron-group metal. Potentiodynamic polarization scans and electrochemical impedance spectroscopy showed that the corrosion resistance of the ternary Zn-Ni-Co alloy coatings was approximately 10 times higher than that of Zn-Ni and 7 times higher than that of Zn-Co. The improved corrosion resistance of the ternary alloy was attributed to its surface chemistry, phase content, texture, and surface morphology. The ternary Zn-Ni-Co coating may thus replace the conventional Zn-Ni and Zn-Co coatings in a variety of applications. © 2010 Elsevier B.V.Item Magnetically induced electrodeposition of Zn-Ni alloy coatings and their corrosion behaviors(Elsevier B.V., 2013) Rao, V.R.; Bangera, K.V.; Hegde, A.C.The less magnetic features of Zn-Ni alloy compared to Fe-Ni and Fe-Co alloys made it interesting to develop them under the influence of applied magnetic field. In this regard, the effects of a magnetic field (B) applied in a direction parallel and perpendicular to the nominal current, during electrodeposition process of Zn-Ni alloy have been investigated by means of X-ray diffraction and EDX analysis. The modification of crystal orientation by superimposition of a varying magnetic field is studied for alloys of constant nickel content (8 a %.), deposited at optimal current density (j) of 3.0 A dm-2. The effect of magnetic field on crystallographic orientation and hence the corrosion behaviors of the coatings were studied. The preferential orientations (101) and (002) of the zinc phase and (330) ?-Ni 5Zn21 phase are always favored to exist with parallel and perpendicular magnetic field. The preferential (321) ?-Ni 5Zn21 orientation is found to be the characteristic of perpendicular magnetic field. Further, Zn (100) orientation is found to be non-responsive to the effect of parallel magnetic field. The coatings developed using perpendicular magnetic field is more corrosion resistant compare to that for parallel magnetic field. This is attributed to the additional (321) ?-Ni5Zn21 orientations. The changes in the phase structure of the coatings deposited at different magnetic field are attributed to the effect caused by the magnetic convection induced in the electrolytic solution, called MHD effect (magneto-hydrodynamic effect). The chemical composition of the alloy was found to be same in both natural and magnetically induced deposition due to constant Ni content in the bath. The variation in the surface morphology of the coatings was studied by scanning electron microscopy (SEM). The Zn-Ni alloy coating deposited at 0.8 T perpendicular B showed the highest corrosion resistance (with corrosion rate=0.26 × 10-2 mm y-1) compared to the one with no B (corrosion rate = 14.46 × 10-2 mm y-1). The improved corrosion resistance of the coatings was discussed in the light of magnetic field effect on crystallographic orientation. © 2013 Elsevier B.V. All rights reserved.Item Additive manufacturing of an aluminum matrix composite reinforced with nanocrystalline high-entropy alloy particles(Elsevier Ltd, 2017) Karthik, G.M.; Panikar, S.; Janaki Ram, G.D.J.; Kottada, R.S.In the present work, a metal-metal composite consisting of aluminum-magnesium alloy AA5083 matrix and nanocrystalline CoCrFeNi high-entropy alloy reinforcement particles in 12 vol% was successfully friction deposited in multiple layers. The layer interfaces or the reinforcement/matrix interfaces showed no brittle intermetallic formation – thanks to the inert nature as well as the high strength and hardness of the high-entropy alloy reinforcement particles. The composite showed significantly higher tensile and compressive strengths as compared to standard wrought-processed alloy AA5083-H112 and offered a much better combination of strength and ductility when compared to conventional aluminum matrix composites reinforced with ceramic particles. The current study establishes friction deposition as a viable technique for additive manufacturing of novel high-performance composite materials. © 2016 Elsevier B.V.Item Ultrasound induced multilayer Ni-Co alloy coatings for better corrosion protection(Elsevier B.V., 2017) Shetty, A.R.; Hegde, A.Ultrasound induced multilayer Ni-Co alloy coatings have been developed galvanostatically by periodic modulation of ultrasound effect, parallel to the process of conventional electroplating. Multilayer Ni-Co alloy having alternative layers of different composition were developed by turning the sonicator probe, ON and OFF periodically, while keeping the current density (c.d.) constant. The deposition conditions, in terms of pulsing power density (p.d.) and degree of layering have been optimized for the highest performance of coating against corrosion, evaluated by electrochemical testing methods. Corrosion data revealed that under optimal conditions, multilayer Ni-Co alloy coating having 150 layers, represented as (Ni-Co)2/2/150 is about 11 times more corrosion resistant than its homogeneous coating, represented as (Ni-Co)4.0 A dm ? 2, deposited from the same bath for same duration of time. Improved corrosion resistance of multilayer Ni-Co alloy coatings was attributed to an increase in the number of interfaces, separating the layers of alloys of different composition, affected due to periodic pulsing of the sonicator. The dependence of corrosion behaviors at different combination of c.d. and p.d., on surface morphology, composition and phase structures were analyzed, using scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS) and X-ray diffraction (XRD) technique, respectively. Experimental results are compared, and discussed. © 2017 Elsevier B.V.Item ANN and RSM modeling methods for predicting material removal rate and surface roughness during WEDM of Ti50Ni40Co10 shape memory alloy(AMSE Press 16 Avenue Grauge Blanche Tassin-la-Demi-Lune 69160, 2017) Soni, H.; Narendranath, S.; Ramesh, M.R.Present study exhibits the comparison between experimental and predicted values. Where response surface method (RSM) and artificial neural network (ANN) were used as predictor for the prediction of wire electro discharge machining (WEDM) responses such as the material removal rate (MRR) and surface roughness (SR) during the machining of Ti50Ni40Co10 shape memory alloy. It has been noticed from the literature survey that pulse on time and servo voltage are most important process parameters for the machining of TiNiCo shape memory alloy, hence there are five levels of these process parameters were chosen for the present study. For the present study selected alloy has been developed through vacuum arc melting and L-25 orthogonal array has been created by using Taguchi design of experiment (DOE) for experimental plan. During the present study ANN predicted values have been found to very close to experimental values compare to RSM predicted values, hence it can be say that ANN predictor gives more accurate values compare to RSM predicted values. © 2017 AMSE Press. All rights reserved.Item Shape induced magnetic vortex state in hexagonal ordered cofe nanodot arrays using ultrathin alumina shadow mask(Elsevier B.V., 2018) Boominathasellarajan, B.; Saravanan, P.; Ghosh, S.K.; Nagaraja, H.S.; Barshilia, H.C.; Chowdhury, P.The magnetization reversal process of hexagonal ordered CoFe nanodot arrays was investigated as a function of nanodot thickness (td) varying from 10 to 30 nm with fixed diameter. For this purpose, ordered CoFe nanodots with a diameter of 80 ± 4 nm were grown by sputtering using ultra-thin alumina mask. The vortex annihilation and the dynamic spin configuration in the ordered CoFe nanodots were analyzed by means of magnetic hysteresis loops in complement with the micromagnetic simulation studies. A highly pinched hysteresis loop observed at 20 nm thickness suggests the occurrence of vortex state in these nanodots. With increase in dot thickness from 10 to 30 nm, the estimated coercivity values tend to increase from 80 to 175 Oe, indicating irreversible change in the nucleation/annihilation field of vortex state. The measured magnetic properties were then corroborated with the change in the shape of the nanodots from disk to hemisphere through micromagnetic simulation. © 2017 Elsevier B.V.Item Elevated temperature solid particle erosion behaviour of carbide reinforced CoCrAlY composite coatings(Institute of Physics Publishing helen.craven@iop.org, 2018) Nithin, H.S.; Desai, V.; Ramesh, M.R.CoCrAlY+WC-Co and CoCrAlY+Cr3C2-NiCr coatings are deposited on nickel based alloy using atmospheric plasma spray technique. Mechanical properties such as microhardness, adhesion strength and fracture toughness of coatings are evaluated. Elevated temperature solid particle erosion behaviour of these coatings are investigated at 600 °C using alumina erodent at 30 and 90° impact angle. Coatings are characterized utilizing Scanning electron microscope (SEM), x-ray diffraction (XRD) and Energy dispersive spectroscopy (EDS). CoCrAlY+WC-Co coating shows higher hardness, adhesion strength and fracture toughness than CoCrAlY+Cr3C2-NiCr coating. CoCrAlY+WC-Co coating exhibited approximately 3 times higher erosion resistance than CoCrAlY+Cr3C2-NiCr coating at 90° and 30° impact angles. SEM images of eroded surfaces of coatings reveals the combination of ductile and brittle fracture. CoCrAlY+Cr3C2-NiCr coating shows severe cracks, craters, carbide pull out and chipping than CoCrAlY+WC-Co coating. High temperature erosion is a combination of simultaneous building up of material by oxidation and removal of material by erosion process. Thus reforming the erosion process to oxidation modified erosion process. © 2018 IOP Publishing Ltd.Item Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating(Institute of Physics Publishing helen.craven@iop.org, 2018) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi superalloy powder (Tribaloy-T400) consists of intermetallic laves phase and primary eutectic phase of Co-rich solid solution. Processing of Tribaloy-T400 powder is carried out through high-energy ball milling (HEBM) technique to obtain a higher volume fraction of intermetallic laves phases. The feedstock is sprayed using high-velocity-oxy-fuel (HVOF) process on titanium grade-15 substrate. The coating microstructure is homogenized by microwave hybrid heating technique. Characterization of feedstock, as-sprayed and microwave fused coatings is done by using Scanning Electron Microscopy (SEM), Energy dispersive spectroscopy (EDS) and x-ray Diffraction (XRD). Porosity, surface roughness, microhardness, and bond strength are measured. Adhesive wear behavior of the coatings under the dry sliding condition is evaluated at an applied load of l0 and 20 N and temperature of 200, 400 and 600 °C Fused coating exhibit higher wear resistance than the as-sprayed coatings and substrate. The hard intermetallic laves phases which are amorphous (bulk metallic glass) in nature strengthen the coating at high temperatures. © 2018 IOP Publishing Ltd.Item Cyclic Oxidation and Hot Corrosion Behavior of Plasma-Sprayed CoCrAlY + WC-Co Coating on Turbine Alloys(Springer New York LLC barbara.b.bertram@gsk.com, 2018) Nithin, H.S.; Vijay, D.; Ramesh, M.R.Components in energy-producing systems suffer a variety of degradation processes such as oxidation and molten salt-induced corrosion as a consequence of complex multi-component gaseous environment. Coatings provide a composition that will grow the protective scale at high temperatures having long-term stability. Plasma spraying was used to deposit CoCrAlY + WC-Co composite coatings on turbine alloys of Hastelloy X and AISI 321. The thermocyclic oxidation behavior of coated alloys was investigated in static air and in molten salt (Na2SO4-60%V2O5) environment at 700 °C. The thermogravimetric technique was used to approximate the kinetics of oxidation in 50 cycles, each cycle consisting of heating and cooling. X-ray diffraction and SEM/EDAX techniques are used to characterize the oxide scale formed. Coated alloys showed a lower corrosion rate as compared to uncoated alloys. The coatings subjected to oxidation and hot corrosion showed slow scale growth kinetics. Preferential oxidation of Co, Cr, W and its spinel blocks the transport of oxygen and corrosive species into the coating by providing a barrier, thereby making the oxidation rate to reach steady state. As compared to the substrate alloys, coatings show better hot corrosion resistance. © 2018, ASM International.