Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
5 results
Search Results
Item Austempered ductile iron containing 0.9 Ni and 0.3 Mo and subject to low stress dry sand abrasive testing shows that wear behaviour is very sensitive to heat treatment conditions. It is concluded that large retained austenite content promotes wear resistance.(Inst of Engineers (India), Low stress dry sand abrasive wear behaviour of austempered ductile iron) Prasad Rao, P.1995Item Study of wear behaviour of austempered ductile iron(2009) Kumari, U.R.; Prasad Rao, P.P.An investigation was carried out to examine the influence of austempering temperature on microstructural parameters and the wear behaviour of austempered ductile iron. Ductile iron was austenitised at 900 °C for 30 min and austempered for 2 h at 260, 280, 300, 320, 350, 380 and 400 °C. Resulting microstructures were characterised through optical microscopy and X-ray diffraction. Wear test was carried out using a pin-on-disc machine with sliding speed of 289 m min-1. Coarse ausferrite microstructure exhibited higher wear rate than fine ausferrite microstructure. At high austempering temperature large amounts of austenite was instrumental in improving the wear resistance through formation of deformation induced martensite. Study of the wear surface under scanning electron microscope showed that, under dry sliding condition, wear occurred mainly due to adhesion and delamination. Wear rate was found to be dependent on the yield strength, austenite content and its carbon content. © 2008 Springer Science+Business Media, LLC.Item Study of wear behaviour of ductile iron subjected to two step austempering(2010) Kumari, R.; Prasad Rao, P.P.An investigation was carried out to examine the influence of two step austempering on microstructural parameters and the wear behaviour of austempered ductile iron. Ductile iron was austenitised at 900 °C for 30 min, and then austempered successively at two different temperatures. It was first austempered at 300 °C for different durations from 2 min to 30 min and subsequently austempered at 400°C for 2 h, after which it was quenched to room temperature. Resulting microstructures were characterised through optical microscopy and X-ray diffraction. Mechanical properties were studied through hardness measurement and tensile testing. Wear studies were carried out using a pin-on-disc machine. Wear rate was found to decrease with increasing time at the first step temperature of 300 °C. At short austempering times at 300 °C, the amount of austenite was instrumental in improving the wear resistance through formation of deformation induced martensite. Wear rate was found to depend on yield strength, austenite content and its carbon content. © Carl Hanser Verlag GmbH & Co. KG.Item Improvement in fracture toughness of austempered ductile iron by two-step austempering process(2010) Ravishankar, K.S.; Prasad Rao, P.P.; Udupa, K.R.Ductile cast iron samples were austenitised at 900°C and subjected to two types of austempering called as conventional austempering and two-step austempering. Five different temperatures, 280, 300, 320, 350, 380 and 400°C, with an austempering time of 2 h, were chosen for conventional austempering. For two-step austempering process, the first step temperatures were 280, 300 and 320°C. The samples were austempered at each of these temperatures for different times, i.e. 10, 20, 30, 45 and 60 min, and then upquenched to higher temperature of 400°C for 2 h. Fracture toughness and tensile studies were carried out under all these austempering conditions. During conventional austempering, the fracture toughness initially increased with increasing austempering temperature, reached a peak value of 63 MPa m 1/2 and dropped with further increase in temperature. During the two-step austempering, fracture toughness was found to increase with increasing first step time. The curve shifted to higher values of fracture toughness as the first step temperature was decreased and the maximum value of 78 MPa m 1/2 was obtained. The results of the fracture toughness study and the fractographic examination were correlated with microstructural features such as bainitic morphology, the volume fraction of retained austenite, and its carbon content. Ferrite lath size and stability of the retained austenite were found to influence the fracture toughness. © 2010 W. S. Maney & Son Ltd.Item Corrosion behavior of high and low temperature austempered ductile iron (ADI) in iron ore slurry(ASTM International, 2017) Aithal, P.M.; Vijayan, V.; Surendranathan, A.O.; Udupa, K.R.; Samuel, K.G.Corrosion behavior of austempered ductile iron (ADI) and forged EN31 steel balls in a ground iron ore slurry was studied as a function of time in the slurry, while the microstructure of ADI developed due to different tempering temperature and tempering time. The corrosion rates of the grinding balls immersed in the iron ore slurry were determined using electrochemical analysis and weight loss methods. It was found that the pH of the iron ore slurry increased with time and the corrosion behavior was influenced by the pH of the slurry. The corrosion rate of forged EN31 steel balls increased with the increase in time and pH of the slurry, whereas the corrosion rate of ADI balls depended on the austempering treatment. In general, the forged EN31 steel ball offered better corrosion resistance than ADIs during the early stages of exposure in the slurry (low pH values of the slurry), but at higher pH values of the slurry, the ADIs yielded better corrosion resistance than forged EN31 steel balls. The ADI austempered at higher temperatures showed better corrosion resistance than the ones austempered at lower temperatures. © © 2017 by ASTM International.