Item An investigation was carried out to examine the influence of chromium content on the plane strain fracture toughness of austempered ductile iron (ADI). ADIs containing 0, 0.3 and 0.5 wt.% chromium were austempered over a range of temperatures to produce different microstructures. The microstructures were characterized by optical microscopy and X-ray diffraction. Plane strain fracture toughness of all these materials was determined and correlated with microstructure and chromium content. The chromium content was found to influence the fracture toughness through its influence on the processing window. Since the chromium addition shifts the processing window to shorter durations, the higher chromium alloys at higher austempering temperatures tend to fall outside of the processing window, resulting in less than optimum microstructure and inferior fracture toughness. A small chromium addition of 0.3 wt.% was found to be beneficial for the fracture toughness of ADI. © 2002 Elsevier Science B.V. All rights reserved.(Elsevier BV, Investigations on the fracture toughness of austempered ductile iron alloyed with chromium) Prasad Rao, P.; Putatunda, S.K.2003Item Influence of austenitising temperature on the formation of strain induced martensite in austempered ductile iron(2008) Daber, S.; Ravishankar, K.S.; Prasad Rao, P.P.The present work was taken up to study the influence of austenitising temperature on the formation of strain-induced martensite in austempered ductile iron. Ductile iron containing 1.5 wt.% nickel, 0.3 wt.% molybdenum and 0.5 wt.% copper was subjected to austempering treatments which consisted of three austenitising temperatures, namely 850, 900 and 950 °C, and three austempering temperatures, namely 300, 350 and 400 °C. Tensile tests were carried out under all the heat-treatment conditions and strain-hardening behaviour was studied by applying Hollomon equation. Microstructures were studied by optical microscopy and X-ray diffraction. It was found that increasing austenitising temperature increased the tendency for the formation of strain-induced martensite at all the austempering temperatures. © 2008 Springer Science+Business Media, LLC.