Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
5 results
Search Results
Item Corrosion behavior of composition modulated multilayer Zn-Co electrodeposits produced using a single-bath technique(2009) Thangaraj, V.; Eliaz, N.; Hegde, A.Composition modulated alloy (CMA) electrodeposits of Zn-Co were produced from acid chloride baths by the single-bath technique. Their corrosion behavior was evaluated as a function of the switched cathode current densities and the number of layers. The process was optimized with respect to the highest corrosion resistance. Enhanced corrosion resistance was obtained when the outer layer was slightly richer with cobalt. At the optimum switched current densities 40/55 mA cm-2, a coating with 600 layers showed ~6 times higher corrosion resistance than monolithic Zn-Co electrodeposit having the same thickness. The CMA coating exhibited red rust only after 1,130 h in a salt-spray test. The increased corrosion resistance of the multilayer alloys was related to their inherent barrier properties, as revealed by Electrochemical Impedance Spectroscopy. The corrosion resistance was explained in terms of n-type semiconductor films at the interface as supported by Mott-Schottky plots. © 2008 Springer Science+Business Media B.V.Item Electrodeposition and characterization Zn-Co alloy(2009) Hegde, A.; Thangaraj, V.The present work details optimization of a stable acid chloride bath for electroplating of bright Zn-Co alloy on mild steel using gelatin and glycine as additives. It was found that the addition of gelatin along with glycine changed the deposition pattern markedly. A suitable bath has been formulated using conventional Hull cell experiments. The bath under plating conditions were found to exhibit anomalous codeposition with preferential deposition of less noble (zinc) over more noble (cobalt) as characterized by Zn-Fe group metal alloys. Investigation revealed that the current density (c.d.), temperature, and pH of the bath have strong effect on the composition of the deposit. Influence of bath constituents and operating parameters on appearance and composition of deposits were studied as measure of their performance against corrosion. A variety of deposits were obtained and their corrosion resistances were measured by Tafel method with/without chrome passivation. Experimental results demonstrated the fact that the corrosion resistances of Zn-Co alloys increased with percent of Co in the deposit except at very high c.d. This is due to the fact at very high c.d. the deposit becomes very porous and thick as evidenced by SEM image. The formation of Zn-Co alloy is confirmed by EDAX analysis. A stable chloride bath for Zn-Co alloy deposition has been proposed and discussed. The formation of passive film on chromatization is indicated by almost same E corr value of all Zn-Co electroplates irrespective of the current densities at which they have been deposited. © 2009 Pleiades Publishing, Ltd.Item Electroplating and characterization of Zn-Ni, Zn-Co and Zn-Ni-Co alloys(2010) Eliaz, N.; Venkatakrishna, K.; Hegde, A.C.Zn-Ni, Zn-Co and Zn-Ni-Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency was higher than 90%. As the current density was increased or the bath temperature was decreased, the concentration of the nobler metal in the coating increased. Both concentrations of Ni and Co in the ternary alloy increased as the applied current density was increased. Nickel and cobalt were found to have a synergistic catalytic effect. The thickness of all coatings increased as the applied current density was increased. The hardness increased with current density to a peak value, and then decreased. The rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, while the rates of Ni and Co deposition were not. The anomalous codeposition was explained by the great difference between the exchange current densities of Zn and the iron-group metal. Potentiodynamic polarization scans and electrochemical impedance spectroscopy showed that the corrosion resistance of the ternary Zn-Ni-Co alloy coatings was approximately 10 times higher than that of Zn-Ni and 7 times higher than that of Zn-Co. The improved corrosion resistance of the ternary alloy was attributed to its surface chemistry, phase content, texture, and surface morphology. The ternary Zn-Ni-Co coating may thus replace the conventional Zn-Ni and Zn-Co coatings in a variety of applications. © 2010 Elsevier B.V.Item Electrodeposition of Zn-Ni, Zn-Fe and Zn-Ni-Fe alloys(2010) Hegde, A.C.; Venkatakrishna, K.; Eliaz, N.Zn-Fe, Zn-Ni and Zn-Ni-Fe coatings were electrodeposited galvanostatically on mild steel from acidic baths (pH 3.5) consisted of ZnCl2, NiCl2, FeCl2, gelatin, sulfanilic (p-aminobenzenesulfonic) acid and ascorbic acid. Cyclic voltammetry showed that the effect of gelatin was more pronounced than that of sulfanilic acid, and that the deposition of the ternary alloy behaved differently from the deposition of the binary alloys. In all three systems, the Faradaic efficiency was higher than 88%, the rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, and the deposition was of anomalous type. For each applied current density, the concentrations of Ni and Fe in the ternary alloy were higher than the corresponding concentrations in the binary alloys. The hardness of Zn-Ni coatings was the highest, while that of Zn-Fe coatings was the lowest. The Zn-Ni-Fe coatings were the smoothest, had distinguished surface morphology, and contained ZnO in the bulk, not just on the surface. The lowest corrosion rate in each alloy system (214, 325 and 26?m year-1 for Zn-Ni, Zn-Fe and Zn-Ni-Fe, respectively) was characteristic of coatings deposited at 30, 30 and 40mAcm-2, respectively. The higher corrosion resistance of the ternary alloy was also reflected by a higher corrosion potential, a higher impedance and a higher slope of the Mott-Schottky line. The enhanced corrosion behavior of the ternary alloy was thus attributed to its chemical composition, phase content, roughness and the synergistic effect of Ni and Fe on the n-type semiconductor surface film. © 2010 Elsevier B.V.Item Anomalous codeposition of NiCo alloy coatings and their corrosion behaviour(Elsevier Ltd, 2022) Raveendran, M.N.; Hegde, A.C.Here, we report the electrodeposition NiCo alloy coatings from a new bath using the glycine, as additive. A bright and uniform coatings NiCo alloy have been developed at different current densities and their corrosion performances have been evaluated. The surface morphology, composition and phase structure of alloy coatings have been analyzed using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscopy (EDS) and X-ray diffraction (XRD) techniques, respectively. The compositional information of NiCo alloy coatings revealed that the proposed bath follows anomalous type of codeposition over range of current density studied (1.0–4.0 A dm−2), by demonstrating more Wt. % of Co in the deposits, than in the bath. A constant increase in the Wt. % of Ni with current density was found, supported by XRD analyses; and it may be attributed to the depletion of more readily depositable Co+2 ions at cathode film by following the principle of codeposition of NiCo alloy. The corrosion study revealed that NiCo alloy deposited at 4.0 A dm−2, represented as (NiCo) 4.0 A dm-2 coating is the most corrosion resistant compared to all other coatings. The highest corrosion stability of (NiCo) 4.0 A dm-2 alloy attributed to its highest Ni content (38.6 wt%) and increased surface smoothness, supported by EDS and SEM study. © 2022