Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
15 results
Search Results
Item Microstructure and mechanical properties of ZA27 based SiC reinforced composite processed by multi directional forging(Institute of Physics Publishing helen.craven@iop.org, 2018) Anjan, B.N.; Preetham Kumar, G.V.P.Influence of multi directional forging (MDF) on microstructural and mechanical properties of ZA27/SiC 5 weight percentage (Wt%) composites were investigated. Stir casting technique followed by squeezing process was adopted for synthesis of composite. MDF process was conducted at 100 °C and 200 °C upto strain of 0.54 and 1.09 respectively. Microstructure analysis was carried out using optical microscopy, scanning electron microscopy and energy dispersive spectrometry. SiC particles were fairly distributed and some clusters were also observed. Density of composite decreased with the reinforcement of SiC particles as compared with ZA27 alloy, however porosity which was existing as casting defect was reduced by MDF process. Average grain size of 200-250 nm and 1 ?m was achieved for MDF processed sample at 100 °C upto 3 passes and at 200 °C upto 6 passes respectively. Addition of SiC particles and adoption of MDF technique improved the vickers hardness of composites. Ultimate tensile strength of ZA/SiC composite has increased from 380 MPa to 395 and 432 MPa respectively with 54 and 37 percentage of elongation to failure. Improvement in hardness and tensile strength is due to strain hardening and grain refinement. Ductility of MDF processed ZA27/SiC composite is attributed to uniform distribution of ultrafine equiaxed grain and micro constituents. © 2018 IOP Publishing Ltd.Item Investigation of microstructure and mechanical properties of the Cu-3% Ti alloy processed by multiaxial cryo-forging(Cambridge University Press, 2018) Ramesh, S.; Shivananda Nayaka, H.; Gopi, K.R.; Sahu, S.; Kuruveri, U.B.A Cu-3%Ti (wt%) alloy was processed by multiaxial forging (MAF) at cryogenic temperature up to 3 cycles, imposing a total strain of 1.6. Microstructure and mechanical properties of the unprocessed and cryo-forged samples were analyzed. X-ray diffraction results showed deviation in peak broadening and peak intensity of the cryo-forged samples in comparison to that of unprocessed, which are due to texture modification caused by grain refinement during the MAF process. Microstructural analysis showed reduction in grain size from 80 m in the as-received condition to 250 nm after 3 cycles. Electron backscatter diffraction results indicated the transformation of high angle grain boundaries to low angle grain boundaries in all 3 cycles when compared to the as-received condition. Reduction in ductility was observed after 1 cycle, but with an increase in the number of cycles, both strength and ductility increased. After 3 cycles, ultimate tensile strength and hardness reached 1126 MPa and 427 Hv as compared to 528 MPa and 224 Hv for the as-received condition. Fractography analysis showed decrement in dimple size after 1 cycle, in comparison to that of the as-received condition. However, it kept on increasing for higher number of cycles. © © Materials Research Society 2018.Item Effects of combined multiaxial forging and rolling process on microstructure, mechanical properties and corrosion behavior of a Cu-Ti alloys(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.; Sahu, S.; Arya, S.Combined multiaxial forging (MAF) and rolling was performed on Cu-3% Ti (wt%) alloy at room temperature with emphasis on microstructural evolution, improvement in mechanical properties, and corrosion resistance. Microstructural changes were confirmed from various characterization techniques, and co-related with mechanical properties. TEM analysis revealed high shear band density in the 3 pass MAF + 90% rolled sample appearing due to high strain. EBSD analysis revealed transformation to low angle grain boundaries from high angle grain boundaries. Maximum microhardness and UTS reached to 340 HV and 960 MPa, respectively in the processed samples. Significant grain refinement was observed in MAF processed Cu-3%Ti alloy, and after combined MAF + rolling, higher dislocation density and refinement of shear bands were observed. In addition, potentio-dynamic polarization test was used to study the corrosion behavior of the alloy. Scanning electron microscope (SEM) was used to analyze the corroded surface morphology. © 2019 IOP Publishing Ltd.Item Effect of multiaxial cryoforging on microstructure and mechanical properties of a Cu-Ti Alloy(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Shivananda Nayaka, H.S.; Gopi, K.R.; Sahu, S.Cu-Ti alloy, processed by multiaxial forging (MAF) at cryogenic temperature with a cumulative strain up to 1.64, was investigated for microstructure and mechanical properties. The deformed microstructures were analyzed using optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The average grain size of 2 ?m was achieved in the deformed sample after 3 cycles of MAF. TEM studies indicated that the shear bands width of the deformed sample after 3 cycles reduced to 1 ?m. Tests for mechanical properties indicated an increase in tensile strength and hardness and it was found to be correlated with an increase in dislocation density and grain boundary strengthening mechanism. Ultimate tensile strength (UTS) of 390 MPa, 480 MPa, and 590 MPa was observed in MAF processed samples after 1, 2, and 3 cycles, respectively. Hardness increased from 65 Hv (as-received) to 240 Hv after 3 cycles of MAF. Fractography analysis showed that, with an increase in number of MAF cycles, dimple size reduced up to 1 cycle and percentage elongation increased after 2 cycles of MAF. © 2018 IOP Publishing Ltd.Item Influence of Multidirectional Forging on Microstructural, Mechanical, and Corrosion Behavior of Mg-Zn Alloy(Springer New York LLC barbara.b.bertram@gsk.com, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.S.; Sahu, S.; Ramesh, M.R.Multidirectional forging (MDF) was applied to Mg-6%Zn alloy up to 5 passes successfully at 280 °C. MDF-processed materials were characterized using optical microscope, scanning electron microscope, electron backscatter diffraction, transmission electron microscope, and x-ray diffraction. Obtained results showed a significant reduction in grain size (up to 3.8 ?m) having a large fraction of high-angle grain boundaries after 5 passes of MDF process. Maximum tensile strength of 230 MPa was achieved for 5-pass MDF-processed Mg-6%Zn alloy which is about ~ 2.0 times higher in comparison with that of homogenized alloy (117 MPa) and was attributed to higher dislocations density and grain refinement. Corrosion behavior of the alloy was investigated in 0.1 M NaCl solution using potentiodynamic polarization test, electrochemical impedance spectra analysis, and immersion tests. It was found that the corrosion rate of 5-pass MDF sample improved (0.34 mm/year) ~2.5 times in comparison with that of homogenized Mg-6%Zn alloy (0.86 mm/year) due to fine grain structure, which creates more grain boundaries that act as a corrosion barrier. © 2019, ASM International.Item Investigation of dry sliding wear properties of multi-directional forged Mg–Zn alloys(National Engg. Reaserch Center for Magnesium Alloys zhangdingfei@cqu.edu.cn, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.S.; Sahu, S.; Ramesh, M.R.Effect of multi-directional forging (MDF) on wear properties of Mg–Zn alloys (with 2, 4, and 6 wt% Zn) is investigated. Dry sliding wear test was performed using pin on disk machine on MDF processed and homogenized samples. Wear behavior of samples was analyzed at loads of 10 N and 20 N, with sliding distances of 2000 m and 4000 m, at a sliding velocity of 3 m/s. Microstructures of worn samples were observed under scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and x-ray diffraction (XRD) and the results were analyzed. Mechanical properties were evaluated using microhardness test. After 5 passes of MDF, the average grain size was found to be 30 ± 4 µm, 22 ± 3 µm, and 18 ± 3 µm, in Mg–2%Zn, Mg–4%Zn, and Mg–6%Zn alloys, respectively, with significant improvement in hardness in all cases. Wear resistance was improved after MDF processing, as well as, with increment in Zn content in Mg alloy. However, it decreased when the load and the sliding distance increased. Worn surface exhibited ploughing, delamination, plastic deformation, and wear debris along sliding direction, and abrasive wear was found to be the main mechanism. © 2019Item Surface modification of multi-directional forged biodegradable Mg-Zn alloy by ball burnishing process: Modeling and analysis using deep neural network(Elsevier Ltd, 2021) Ramesh, S.; Anne, G.; Bhat, N.; Aithal, G.; Shivananda Nayaka, H.; Arya, S.This research investigates the feasibility of improving surface integrity of the Mg-2%Zn alloy via a novel combined process of multidirectional forging (MDF) with ball burnishing technique. Mg-2%Zn alloy was subjected to multidirectional forging up to 5 passes at 280 °C and same sample is ball burnished with depth of press of 0.3 mm, feed of 300 mm/min and force of 250 N for 1 pass. Microstructure (optical and transmission electron microscope), phases (X ray diffraction), roughness (atomic force microscope) and mechanical properties (microhardness and tensile) were analyzed for cast, MDF processed and MDF + ball burnished samples. The study also defines a new reliability simulation framework to predict the roughness and hardness of the MDF + ball burnished samples using Deep Neural Network (DNN) approach. For the analysis, depth of press, feed and number of passes served as inputs for the DNN model. After configuring and training procedure of the model, the predicted roughness and microhardness of the MDF + ball burnished were compared with the results of experimental data. A large increase of microhardness was observed for MDF-5 + BB-1 (5 pass MDF processed Mg-2%Zn alloy + Ball burnished sample), found to be 98 Hv and surface roughness of 306 nm was achieved. According to the results, the obtained R-squared value is very close to the 99.5 percentage from the model for predicting roughness and hardness which is a promising result. Corrosion behavior of the AS-1, MDF-5 and MDF-5 + BB-1 was evaluated in Hank's balanced salt solution. Corrosion rate of the MDF-5 + BB-1 samples were found to be 0.87 mm/y which is 7 times better than that of AS-1 samples (6.10 mm/y). Grain refinement and residual stresses were higher in the MDF-5 + BB-1 sample, which helped significantly to enhance corrosion resistance. © 2021 The Society of Manufacturing EngineersItem Investigation of Tribological Characteristics of Cu-Ti Alloys Processed by Multi-Axial Cryo-Forging(Springer, 2022) Ramesh, S.; Shivananda Nayaka, H.S.; Anne, G.; Arun, M.N.; Naik, G.M.Cu-XTi alloys (X = 1.5 and 4.5%) were subjected to multi-axial forging (MAF) under cryogenic condition up to three passes successfully. Characteristics of the MAF-processed alloys were analyzed using microstructural analysis, hardness and wear tests. Worn surface morphology and elemental analysis was performed by scanning electron microscopy. The hardness of samples increases with higher MAF passes due to strain hardening and grain refinement. Wear test was done for six various sliding distances (500, 1000, 1500, 2000, 2500 and 3000 m), two different loads (10 and 20 N), and two different velocities (1 and 2 m/s) using the pin-on-disk wear test rig. Wear loss of as-received samples is higher than MAF-pressed samples due to an increase in hardness, but wear loss increases as the load increases. Coefficient of friction is reduced with the increase in MAF pass, which is due to strain hardening effect. The worn surface exhibits the plastic deformation regions, delamination, plowing and formation of oxide layers, which was revealed by energy-dispersive X-ray spectroscopy analysis. Also, MAF-processed samples exhibited abrasive wear mechanism as a result of formation of oxygen layer as revealed in SEM micrographs. © 2022, ASM International.Item High-Temperature Tribological Studies on Hot-Forged Al6061–TiB2 In Situ Composites(Springer Science and Business Media Deutschland GmbH, 2022) Venkategowda, C.; Hanumanthappa, H.; Prasad, C.D.; Shanmugam, B.K.; Sreenivasa, T.N.; Kumar, M.S.R.The present investigation deals with the tribological behavior of high-temperature hot-forged Al6061–TiB2 in situ composites. Three samples of Al6061–TiB2 in situ composites were prepared with the variation in the in situ TiB2 particles. An in situ technique forms TiB2 particles by facilitating a reaction between Al–3%B and Al–10%Ti parent metals in the Al6061 melt at 800 °C. Further, approximately 5 wt% and 10 wt% TiB2 particles were created in the Al6061 composite using suitable quantities of parent alloys. At 500 °C, the Al6061 and its in situ composites were subjected to hot forging, and about 50% reduction is employed. The scanning electron microscope (SEM) and optical microscopy analysis were conducted to check the TiB2 particle dispersion and worn surfaces in the in situ composites. The TiB2 particle dispersion is found to be fairly uniform throughout the Al6061 matrix with minimal clustering. The results indicate that the friction coefficient increases initially when the temperature increases and then declines due to the oxides in the debris released from the top surfaces of the samples. The results show that the increase in the TiB2 content in the Al6061–TiB2 composites increases the composite wear rate. © 2022, The Author(s), under exclusive licence to Springer Nature Switzerland AG.Item Effect of Multi-directional Forging on the Evolution of Microstructural and Mechanical Properties of Lightweight Al-Cu-Li Alloy AA2050(Springer, 2023) Jagadeesh, C.; Shivananda Nayaka, H.S.; Ramesh, S.; Praveen, T.R.Microstructural evolution and the mechanical properties of recently developed lightweight AA2050 Al-Cu-Li alloy have been presented. A processing route of multi-directional forging (MDF) at 170 °C followed by artificial aging at 150 °C was employed. Systematic EBSD analysis revealed significant grain refinement with grain size reducing from 74.3 ± 12 to 22.1 ± 2.8 µm after 12 passes of MDF. Transformation of deformation bands into subgrains with dynamic recrystallization has led to grain refinement. TEM results show the presence of large dislocation clusters and deformation bands in MDF processed samples with a large number of fine precipitates in peak aged MDF processed samples. XRD analysis shows variation in peak intensities and occurrence of peak shifts due to induced lattice strain upon MDF. A substantial increase in microhardness and strength was observed with a minor trade-off with ductility after 12th MDF pass. Further, enhancement in strengths and microhardness were observed in post-MDF aged samples. Experimental results show the combined effect of strain hardening, grain size reduction, and precipitate hardening which influence the material strength. A combination of MDF and artificial aging has shown great potential to enhance the strength and ductility of AA2050. © 2023, ASM International.