  • No Thumbnail Available
    Item
    The effect of the addition of strontium and cerium modifiers on microstructure and mechanical properties of hypereutectic Al-Si (LM30) alloy
    (ASTM International, 2013) Vijayan, V.; Ravi, M.; Prabhu, K.
    The present work deals with the melt treatment of LM30 hypereutectic Al-Si alloy using cerium and strontium and the assessment of its effect on microstructure and properties of the alloy. The addition of cerium simultaneously modified both primary and eutectic silicon, leading to an increase in ultimate tensile strength, as well as the wear resistance of the alloy. It was found that the coefficient of thermal expansion of the alloy decreased on modification of the microstructure. © 2013 by ASTM International.
  • No Thumbnail Available
    Item
    Effect of chilling and cerium addition on microstructure and cooling curve parameters of Al-14%Si alloy
    (Maney Publishing maney@maney.co.uk, 2015) Vijayan, V.; Prabhu, K.
    Al-14%Si alloys, with and without cerium, were cast at varying cooling rates by solidifying them in a crucible and against chills. The effect of melt treatment and chilling on microstructure and cooling curve parameters of the alloy was assessed. Ce treated alloys solidified in clay graphite crucible at a slow cooling rate showed refinement of primary silicon and the formation of Al-Si-Ce ternary intermetallic compound. The addition of Ce to the alloy solidified against chills resulted in simultaneous refinement and modification of primary and eutectic silicon. Nucleation temperatures of both primary and eutectic silicon decreased on addition of cerium. The formation of the intermetallic compound decreased with increase in cooling rate, leading to the modification of the eutectic silicon. The increase in the degree of modification of the eutectic Si was associated with the decrease in the volume fraction of the intermetallic compound formed. © 2015 Canadian Institute of Mining, Metallurgy and Petroleum Published by Maney on behalf of the Institute.
  • No Thumbnail Available
    Item
    The effect of simultaneous refinement and modification by cerium on microstructure and mechanical properties of Al-8% Si alloy
    (Taylor and Francis Ltd. maney@maney.co.uk, 2016) Vijayan, V.; Prabhu, K.N.
    The effect of cerium melt treatment on microstructure and mechanical properties of gravity die cast Al-8% Si alloy was studied. The addition of Ce transformed the large columnar ?-Al grains into fine equiaxed grains and modified the acicular eutectic Si into fine fibrous form. The addition of Ce resulted in the formation of needle-shaped complex Ce intermetallic along the grain boundaries. Electrical conductivity measurements are used for the first time to reveal the effect of Ce addition on modification of the eutectic Si. The electrical conductivity of the alloy increased with Ce melt treatment. Scanning Electron Microscopy results suggests that the Ce particles did not heterogeneously nucleate the ?-Al grains, instead the fine equiaxed grains were formed through an invariant reaction between the liquid melt and Ce phase. The ultimate tensile strength, % elongation and hardness of the alloy significantly improved due to simultaneous modification and refinement. © 2016 Informa UK Limited, trading as Taylor & Francis Group.
  • No Thumbnail Available
    Item
    Thermal Analysis of Cerium-Treated Chill-Cast Al-23 Si Alloy
    (Springer New York LLC barbara.b.bertram@gsk.com, 2018) Vijayan, V.; Prabhu, K.N.
    The influence of elemental cerium addition on the cooling curve parameters and microstructure of hypereutectic Al-23Si alloy was investigated in this work. The cooling rate of the treated and untreated alloy samples was varied by solidifying the melt against chills of different materials in a stainless-steel tube. The cooling curve was recorded and nucleation temperatures of various phases in the alloy were measured. The results show that the chilling improves the effectiveness of the modifier. The two main phases of the alloy, primary silicon and eutectic silicon, were nucleated at temperatures of about 661.2 and 571.6 °C, respectively. The addition of Ce to slowly cooled alloys resulted in an increase in undercooling temperature of both the phases, with a decrease in its nucleation temperature, whereas the same additions increased the nucleation temperatures in chilled alloys. Based on the thermal analysis results, a relation between thermal analysis parameter (? TG) and silicon particle size of the alloy was proposed. © 2018, ASM International.