Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
Search Results
Item Multi-objective optimisation of cryogenic turning process using Taguchi-based grey relational analysis(Inderscience Publishers, 2017) Sivaiah, P.; Dupadu, D.Cryogenic machining is a sustainable manufacturing approach; it eliminates coolant disposal cost, health problems compared to the conventional flood cooling. The present study investigates the multiple response optimisation of turning process while machining AISI 17-4 PH stainless steel under the cryogenic environment (jetting of liquid nitrogen at -196°C at the rake face of the tool) by using Taguchi-based grey relational analysis. The optimum levels of the machining parameters are cutting speed at 120.89 m/min, feed rate at 0.048 mm/rev, depth of cut 0.4 mm and physical vapour deposition (PVD) AlTiN coated tungsten carbide (WC). Taguchi-based grey relational analysis method reduced the cutting forces by 7.75%, improved the surface finish by 55.87%, and increased the material removal rate (MRR) by 154.76% and 25% increased the tool flank wear in cryogenic turning process. From the analysis of variance, it was identified that feed rate is the most influenced process parameter on turning performance characteristics. © © 2017 Inderscience Enterprises Ltd.Item Influence of cryogenic coolant on turning performance characteristics: A comparison with wet machining(Taylor and Francis Inc. 325 Chestnut St, Suite 800 Philadelphia PA 19106, 2017) Sivaiah, P.; Dupadu, D.Machining of 17-4 Precipitation Hardenable Stainless Steel (PH SS) is one of the difficult tasks because of its high cutting temperatures. Conventional cutting fluids are used to overcome the high cutting temperatures, but these are not acceptable from the health and environmental sustainable points of view. Cryogenic cooling is one of the potential techniques to overcome such problems. In the current work, comparison is made of cryogenic turning results, such as tool flank wear, cutting forces (feed force, main cutting force), cutting temperature, chip morphology and surface integrity characteristics with wet machining during machining of heat-treated 17-4 PH SS. The result showed that in cryogenic machining, a maximum of 53%, 78%, 35% and 16% reductions was observed in tool flank wear, cutting temperature, surface roughness and cutting force, respectively, when compared with wet machining. It was also evident from the experimental results that cryogenic machining significantly improved the machining performance and product quality even at high feed rates. © 2017 Taylor & Francis.Item Machinability studies on 17-4 PH stainless steel under cryogenic cooling environment(Taylor and Francis Inc. 325 Chestnut St, Suite 800 Philadelphia PA 19106, 2017) Sivaiah, P.; Dupadu, D.Under higher cutting conditions, machining of 17-4 precipitation hardenable stainless steel (PH SS) is a difficult task due to the high cutting temperatures as well as accumulation of chips at the machining zone, which causes tool damage and impairment of machined surface finish. Cryogenic machining is an efficient, eco-friendly manufacturing process. In the current work, cutting temperature, tool wear (flank wear (Vb) and rake wear), chip morphology, and surface integrity (surface topography, surface finish (Ra), white layer thickness (WLT)) were considered as investigative machinability characteristics under the cryogenic (liquid nitrogen), minimum quantity lubrication (MQL), wet and dry environments at varying cutting velocities while machining 17-4 PH SS. The results show that the maximum cutting temperature drop found in cryogenic machining was 72%, 62%, and 61%, respectively, in contrast to dry, wet, and MQL machining conditions. Similarly, the maximum tool wear reduction was found to be 60%, 55%, and 50% in cryogenic machining over the dry, wet, and MQL machining conditions, respectively. Among all the machining environments, better surface integrity was obtained by cryogenic machining, which could produce the functionally superior products. © 2017 Taylor & Francis.