Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
10 results
Search Results
Item Development and characteristics of accumulative roll bonded Mg-Zn/Ce/Al hybrid composite(Elsevier Ltd, 2017) Anne, G.; Ramesh, M.R.; Shivananda Nayaka, H.; Arya, S.B.; Sahu, S.Accumulative roll bonding (ARB) process have been used develop Mg-2%Zn/Ce/Al hybrid composite and microstructure, mechanical and corrosion properties were investigated. The electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) revealed that the grains are significantly reduced and reaches up to 1 ?m in Mg-2%Zn layer and 1.8 ?m in Al layer having high angle misorientation of grain boundaries after subjected to 5-passes of the ARB process. The Al17Mg12, AlMg4Zn11 and Al11Ce3 intermetallic phases were observed through the XRD analysis. Mechanical properties of the hybrid composite improved with increase in the number of ARB passes which is attributed to work hardening, grain refinement and uniform distribution of Ce particles. Presence of Ce in the hybrid composite restricts the phenomenon of dynamic recrystallization and prevents the grain growth during ARB process. The corrosion rate of Mg-Zn/Ce/Al hybrid composite (0.72 mm/y) improved about 3.3 times as compared to that of Mg-2%Zn alloy (2.37 mm/y). © 2017 Elsevier B.V.Item Development and properties evaluation of Mg-6% Zn/Al multilayered composites processed by accumulative roll bonding(Cambridge University Press, 2017) Anne, G.; Ramesh, M.R.; Shivananda Nayaka, H.; Arya, S.B.; Sahu, S.Accumulative roll bonding (ARB) process was used to develop Mg-6% Zn/Al and Mg-6% Zn/anodized-Al multilayered composites. Microstructural characterization was done using scanning electron microscopy, energy-dispersive X-ray spectroscopy, electron backscattered diffraction, and transmission electron microscopy. An average grain size measured in the roll-bonded layers of Al, anodized Al, and Mg-2% Zn was found to be 1.8 ?m, 1.6 ?m, and 0.6 ?m, respectively. Phases Al17Mg12, AlMg4Zn11, and Al2O3 after 5-pass of ARB were confirmed by X-ray diffraction analysis. The Mg-6% Zn/Al and Mg-6% Zn/anodized Al composites exhibited tensile strengths ?252 MPa and ?256 MPa, respectively, after a 5-pass ARB process. Hardness of the individual layers of composite increased linearly with an increase in the number of ARB passes. Fractographs of the multilayered composite illustrated the ductile failure in Al and anodized Al layers and transgranular brittle fracture in Mg-6% Zn layers. © Materials Research Society 2017.Item Tribological and corrosion properties of AM70 magnesium alloy processed by equal channel angular pressing(Cambridge University Press, 2017) Gopi, K.R.; Shivananda Nayaka, H.Wear and corrosion properties of AM70 magnesium alloy subjected to equal channel angular pressing (ECAP) were investigated using pin-on-disc dry sliding wear test and electrochemical impedance spectroscopy (EIS), respectively. Wear test was conducted with 30 and 40 N loads with sliding distance of 5000 m and at a constant speed of 3 m/s. Reduced coefficient of friction (COF) and wear mass loss of ECAP processed samples showed increased wear resistance. Worn surface analysis by scanning electron microscope (SEM) showed the presence of delamination, wear debris, and plowing. Energy dispersive X-ray spectrometer (EDS) revealed the occurrence of oxidation, and the wear mechanism was identified as abrasion and oxidation wear. EIS plots showed the improvement in corrosion resistance of ECAP processed magnesium alloy compared to initial condition due to grain refinement and homogeneous distribution of secondary particles. © Materials Research Society 2017.Item Wear Properties of ECAP-Processed AM80 Magnesium Alloy(Springer New York LLC barbara.b.bertram@gsk.com, 2017) Gopi, K.R.; Shivananda Nayaka, H.; Sahu, S.AM80 magnesium alloy was subjected to equal-channel angular pressing (ECAP), and microstructural evolution was studied using scanning electron microscope (SEM). Grain size was found to decrease up to 3 µm after four passes. An increase in number of ECAP passes led to a corresponding increase in hardness of the processed samples. Unprocessed and ECAP-processed samples were subjected to wear test using pin-on-disk wear test machine to study the wear behavior. Effects of varying loads (30 and 40 N) with sliding distances (2500 and 5000 m) were studied. The results showed reduction in wear mass loss for the ECAP-processed samples in comparison with unprocessed condition. Coefficient of friction (COF) was studied for different loads, and improvement in COF values was observed for ECAP-processed samples compared to unprocessed condition. Worn surfaces were studied using SEM and energy-dispersive x-ray spectrometer, and they exhibited plastic deformation, delamination, plowing, wear debris and oxidation in the sliding direction. X-ray diffraction analysis was conducted on the worn surfaces to identify the phases. It revealed the presence of magnesium oxide and magnesium aluminum oxide which led to oxidation wear in the sliding direction. Wear mechanism was found to be abrasive and oxidation wear. © 2017, ASM International.Item Numerical Simulation of Shot Peening Process on Equal Channel Angular Pressed Magnesium Alloy(Springer Netherlands rbk@louisiana.edu, 2018) Praveen, T.R.; Gopi, K.R.; Shivananda Nayaka, H.This paper presents the numerical simulation of inducing residual stresses on equal channel angular pressed (ECAP) magnesium alloy by shot peening process. Mg-Al-Mn (AM) series magnesium alloy was ECAP processed up to 4 passes using route BC. Microstructures were analysed and grain size reduced from 100 µm for the as-received sample to 3 µm for ECAP 4 pass sample. Tensile test was carried out and maximum tensile strength was found in ECAP 2 pass sample and decreased with higher ECAP passes. Grain refinement was characterized by optical microscopy, electron backscatter diffraction analysis (EBSD) and X-ray diffraction (XRD). Material (tensile) behaviour of 2 pass sample was implemented for finite element modelling. A finite element method was used to estimate the intensity of residual stresses developed due to shot peening in ECAP processed AM80 alloy. Simulation was done with different boundary condition such as impact velocity, geometry of shot-peen media, angle of impact and multiple impacts. The results are presented and the relationship between process parameters and the intensity of residual stresses are discussed. Increase in velocity of shot peening media showed an increase in the magnitude of residual stresses. Change in geometry of shot media altered the contact area between target and shot media during impact which influenced the magnitude of residual stresses and coverage area. The magnitude of residual stresses varied with the angle of impact and the multiple repeated impacts showed that the effective depth of residual stresses increased with the number of impacts. © 2018, Springer Science+Business Media B.V., part of Springer Nature.Item Investigation of microstructure and mechanical properties of the Cu-3% Ti alloy processed by multiaxial cryo-forging(Cambridge University Press, 2018) Ramesh, S.; Shivananda Nayaka, H.; Gopi, K.R.; Sahu, S.; Kuruveri, U.B.A Cu-3%Ti (wt%) alloy was processed by multiaxial forging (MAF) at cryogenic temperature up to 3 cycles, imposing a total strain of 1.6. Microstructure and mechanical properties of the unprocessed and cryo-forged samples were analyzed. X-ray diffraction results showed deviation in peak broadening and peak intensity of the cryo-forged samples in comparison to that of unprocessed, which are due to texture modification caused by grain refinement during the MAF process. Microstructural analysis showed reduction in grain size from 80 m in the as-received condition to 250 nm after 3 cycles. Electron backscatter diffraction results indicated the transformation of high angle grain boundaries to low angle grain boundaries in all 3 cycles when compared to the as-received condition. Reduction in ductility was observed after 1 cycle, but with an increase in the number of cycles, both strength and ductility increased. After 3 cycles, ultimate tensile strength and hardness reached 1126 MPa and 427 Hv as compared to 528 MPa and 224 Hv for the as-received condition. Fractography analysis showed decrement in dimple size after 1 cycle, in comparison to that of the as-received condition. However, it kept on increasing for higher number of cycles. © © Materials Research Society 2018.Item Effects of combined multiaxial forging and rolling process on microstructure, mechanical properties and corrosion behavior of a Cu-Ti alloys(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.; Sahu, S.; Arya, S.Combined multiaxial forging (MAF) and rolling was performed on Cu-3% Ti (wt%) alloy at room temperature with emphasis on microstructural evolution, improvement in mechanical properties, and corrosion resistance. Microstructural changes were confirmed from various characterization techniques, and co-related with mechanical properties. TEM analysis revealed high shear band density in the 3 pass MAF + 90% rolled sample appearing due to high strain. EBSD analysis revealed transformation to low angle grain boundaries from high angle grain boundaries. Maximum microhardness and UTS reached to 340 HV and 960 MPa, respectively in the processed samples. Significant grain refinement was observed in MAF processed Cu-3%Ti alloy, and after combined MAF + rolling, higher dislocation density and refinement of shear bands were observed. In addition, potentio-dynamic polarization test was used to study the corrosion behavior of the alloy. Scanning electron microscope (SEM) was used to analyze the corroded surface morphology. © 2019 IOP Publishing Ltd.Item Strength enhancement of magnesium alloy through equal channel angular pressing and laser shock peening(Elsevier B.V., 2020) Praveen, T.R.; Shivananda Nayaka, H.; Swaroop, S.; Gopi, K.R.AM80 magnesium alloy was processed by Equal Channel Angular Pressing up to 2 passes under route BC and C, to study the effect of change in microstructure. Microstructures were examined under optical microscope. Samples processed by route BC showed heterogeneous grain structure with good tensile strength compared to that processed by route C. Tensile tests of 2-pass equal channel angular pressed samples showed high tensile strength under route BC. Laser shock peening without coating was carried out on route BC sample for further grain refinement on the surface. Laser pulses with power density of 8 GW cm?2, under different percentages of cover, were used to peen the surface at high strain rate. Microstructures were analysed through scanning and transmission electron microscope, and fine grains of less than 100 nm were observed. Tensile tests indicated that the laser shock peened samples had increased strength and ductility. Fracture details from tensile tested specimens, were examined under SEM. Mixed mode of brittle and ductile fractures was observed in ECAP processed samples. Fracture surface of Laser shock peening without coating treated on equal channel angular pressed samples showed small dimples near the peened surface and intensity of dimples increased with increase in percentage of cover. Wear test was carried out on before and after Laser shock peening without coating processed samples, on pin-on-disc wear test machine. Increase in friction coefficients and wear rate was observed due to roughness induced by peening effect and it decreased after increase in sliding distance due to increase in hardness. Nano indentation experiments were carried out to examine the mechanical characterization at nano level, and it expose the effect of LSPwC in terms of increase in hardness at peened region. © 2020Item Influence of Ball Burnishing Process on Equal Channel Angular Pressed Mg-Zn-Si Alloy on the Evolution of Microstructure and Corrosion Properties(Springer Science and Business Media B.V., 2021) Ramesh, S.; Anne, G.; Kumar, G.; Jagadeesh, C.; Shivananda Nayaka, H.In the present study, Mg-4Zn-1Si alloy was subjected to equal channel angular pressing (ECAP) up to 4 passes at 300 °C, followed by ball burnishing using 0.3 mm depth of press, 300 mm/min feed and 1 pass successfully. The effect of ECAP and ECAP + ball burnishing process on microstructure, mechanical properties (tensile and hardness) and corrosion behavior was systematically investigated. After 4 pass ECAP, initial coarse grains (210 ?m) were refined and average grain size is 6 ?m and after ball burnishing, the grain size is found to be 3.3 ?m. Microstructure evolution is discussed using optical images, scanning electron microscope images and transmission electron microscope images. For ECAP samples, maximum strength and hardness was recorded at 3 pass. Both strength and hardness decreased for 4 pass ECAP processed samples, even though grain size decreased, this is because of texture modification in the material. ECAP 4 pass + ball burnished samples exhibited 48.5% enhancement of microhardness as compared to 4 pass ECAP samples. Corrosion resistance of the samples decreased with increase in the number of ECAP passes, this is due to strain-induced grain refinement with more crystalline defects in samples. Combined process of ECAP and ball burnishing effectively reduces the Icorr and this consequently reduces corrosion rate of the Mg–4Zn-1Si alloy. © 2020, Springer Nature B.V.Item Effect of Equal Channel Angular Pressing on Properties Evaluation of Biodegradable Mg-Zn-Mn Alloy(Springer Science and Business Media Deutschland GmbH, 2021) Ramesh, S.; Kumar, G.; Jagadeesh, C.; Anne, G.; Shivananda Nayaka, H.Equal channel angular pressing (ECAP) was used to process Mg-4Zn-1Mn alloy at 300 °C using route Bc up to 4 pass with a cumulative strain of 3.2. Optical microscope (OM), microstructures results shows homogenized sample grain size was 260 µm, after 4 pass ECAP grain size was decreased to 6 µm. Electron back-scattered diffraction (EBSD) shows the misorientation angle converted from low-angle grain boundaries (LAGB) to high-angle grain boundaries (HAGB). Dislocation density and fine grains were observed from transmission electron microscope (TEM) images. Strength has been increased from 156 to 218 MPa and hardness increased to 68 Hv after 4 pass of ECAP. Fractography analysis revealed that dimple size decreases as ECAP passes increased. XRD analysis shows the peak broadening and intensity variation, because of grain refinement. The corrosion behavior of the homogenized and ECAP-processed samples were investigated by electrochemical tests using simulated body fluids (SBF) at 37 ± 1 °C. The lower corrosion resistance of ECAP-processed Mg-4Zn-1Mn alloy attributed to the strain-induced crystalline defects, subgrain boundaries and high-density dislocations. Enhanced strength and ductility combined with lower corrosion resistance of ECAP-processed Mg-4Zn-1Mn has greater potentials for biomedical implants. © 2021, The Author(s), under exclusive licence to Springer Nature Switzerland AG.