Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
2 results
Search Results
Item Ultrasound induced multilayer Ni-Co alloy coatings for better corrosion protection(Elsevier B.V., 2017) Shetty, A.R.; Hegde, A.Ultrasound induced multilayer Ni-Co alloy coatings have been developed galvanostatically by periodic modulation of ultrasound effect, parallel to the process of conventional electroplating. Multilayer Ni-Co alloy having alternative layers of different composition were developed by turning the sonicator probe, ON and OFF periodically, while keeping the current density (c.d.) constant. The deposition conditions, in terms of pulsing power density (p.d.) and degree of layering have been optimized for the highest performance of coating against corrosion, evaluated by electrochemical testing methods. Corrosion data revealed that under optimal conditions, multilayer Ni-Co alloy coating having 150 layers, represented as (Ni-Co)2/2/150 is about 11 times more corrosion resistant than its homogeneous coating, represented as (Ni-Co)4.0 A dm ? 2, deposited from the same bath for same duration of time. Improved corrosion resistance of multilayer Ni-Co alloy coatings was attributed to an increase in the number of interfaces, separating the layers of alloys of different composition, affected due to periodic pulsing of the sonicator. The dependence of corrosion behaviors at different combination of c.d. and p.d., on surface morphology, composition and phase structures were analyzed, using scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS) and X-ray diffraction (XRD) technique, respectively. Experimental results are compared, and discussed. © 2017 Elsevier B.V.Item Effect of TiO2 on electrocatalytic behavior of Ni-Mo alloy coating for hydrogen energy(KeAi Communications Co., 2018) Shetty, A.R.; Hegde, A.Ni-Mo-TiO2 composite coating has been developed through electrodeposition method by depositing titanium dioxide (TiO2) nanoparticles parallel to the process of Ni-Mo alloy coating. The experimental results explaining the increased electrocatalytic activity of Ni-Mo alloy coating on incorporation of TiO2 nanoparticles into its alloy matrix is reported here. The effect of addition of TiO2 on composition, morphology and phase structure of TiO2 – composite coating is studied with special emphasis on its electrocatalytic activity for hydrogen evolution reaction (HER) in 1.0 M KOH solution. The electrocatalytic activity of alloy coatings were validated using cyclic voltammetry (CV) and chronopotentiometry (CP) techniques. Under optimal condition, TiO2 – composite alloy coating represented as (Ni-Mo-TiO2)2.0 A dm?2 is found to exhibit the highest electrocatalytic activity for HER compared to its binary alloy counterpart. The increased electrocatalytic activity of (Ni-Mo-TiO2)2.0 A dm?2 composite coating was attributed to the increased Mo content, porosity and roughness of coating, affected due to addition of TiO2 nanoparticles, supported by SEM, EDX, XRD and AFM study. The increased electrocatalytic activity of (Ni-Mo-TiO2)2.0 A dm?2 coating was found due to decreased Rct and increased Cdl values, demonstrated by EIS study. Better electrocatalytic activity of (Ni-Mo-TiO2)2.0 A dm?2 coating, compared to (Ni-Mo)2.0 A dm?2 coating has been explained through mechanism. Experimental study revealed that (Ni-Mo-TiO2)2.0 A dm?2 composite coating follows Volmer-Heyrovsky mechanism, compared to Tafel mechanism in case of (Ni-Mo-TiO2)2.0 A dm?2 coating, assessed on the basis of Tafel slopes. © 2018