Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
39 results
Search Results
Item Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating(Institute of Physics Publishing helen.craven@iop.org, 2018) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi superalloy powder (Tribaloy-T400) consists of intermetallic laves phase and primary eutectic phase of Co-rich solid solution. Processing of Tribaloy-T400 powder is carried out through high-energy ball milling (HEBM) technique to obtain a higher volume fraction of intermetallic laves phases. The feedstock is sprayed using high-velocity-oxy-fuel (HVOF) process on titanium grade-15 substrate. The coating microstructure is homogenized by microwave hybrid heating technique. Characterization of feedstock, as-sprayed and microwave fused coatings is done by using Scanning Electron Microscopy (SEM), Energy dispersive spectroscopy (EDS) and x-ray Diffraction (XRD). Porosity, surface roughness, microhardness, and bond strength are measured. Adhesive wear behavior of the coatings under the dry sliding condition is evaluated at an applied load of l0 and 20 N and temperature of 200, 400 and 600 °C Fused coating exhibit higher wear resistance than the as-sprayed coatings and substrate. The hard intermetallic laves phases which are amorphous (bulk metallic glass) in nature strengthen the coating at high temperatures. © 2018 IOP Publishing Ltd.Item Microstructure and tribological behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere/solid lubricants composite coatings(Elsevier B.V., 2018) Doddamani, M.; Mathapati, M.; Ramesh, M.R.Present investigation deal with NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2, NiCrAlY/WC-Co/Cenosphere/MoS2/CaSO4 and NiCrAlY/WC-Co/Cenosphere coatings deposited on MDN 321 steel using atmospheric plasma spraying. Tribological properties of MDN 321 steel and coatings are evaluated from room temperature (RT) to 600 °C under dry lubrication conditions using a pin on disc high-temperature tribometer. Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) and Energy Dispersive Spectroscopy (EDS) are used to characterize the coatings. Presence of cenospheres in these coatings might effectively reduce wear acting as localized regions accumulating wear debris. The result shows that wear rate of all the coatings are lower as compared to MDN 321 substrate at all the test conditions. NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2 and NiCrAlY/WC-Co/Cenosphere/MoS/CaSO4 coatings registered lower friction coefficient as compared to NiCrAlY/WC-Co/Cenosphere coating and MDN 321 substrate. Characterization of the NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2 and NiCrAlY/WC-Co/Cenosphere/MoS2/CaSO4 coatings worn out surface suggests that MoS2 provides lubrication at 200 °C and formation of CaMoO4, MoO3 through tribo chemistry reaction at higher temperature provides lubrication at 600 °C. SEM micrograph of worn surface demonstrates that the main wear mechanism is plowing and delamination. © 2018 Elsevier B.V.Item Effect of cutting parameters on tool wear, cutting force and surface roughness in machining of MDN431 alloy using Al and Fe coated tools(Institute of Physics Publishing helen.craven@iop.org, 2019) V Badiger, P.V.; Desai, V.; Ramesh, M.R.; Prajwala, B.K.; Raveendra, K.Thin solid films are used in cutting tools in order to improve its performance, reduce tool wear and improve tool life. Cathodic arc evaporation is the state of art PVD technique widely accepted in industries for the development of thin solid films. The turning cutting tool inserts are coated with AlCN/AlC and FeCrN monolayer thin solid films using cathodic arc evaporation technique. Quality characteristics of thin films are estimated using Calo and VDI3198 tests. Thickness of the coatings are found to be 1.430 and 1.475 ?m for AlCN/AlC and FeCrN coatings respectively and adhesion quality of HF1 is attained. Performance of the thin solid films are evaluated in machining MDN431 steel with range of cutting speed (59-118 m min-1), feed rate (0.062-0.125 mm/rev) and depth of cut (0.2-0.4 mm). Experiments are performed based on full factorial design and regression analysis. Optimization of the process parameters is carried out using combined techniques of desirability and Particle swarm optimisation (PSO). The objective of the study is to establish correlation between machining parameters with cutting force, tool wear and surface roughness. Optimal process parameter for least cutting force and surface roughness are obtained for coatings. ANN has been adopted to improve the coefficient of determination (CoD) and capability of predictive regression models. ANN trained model and mathematical regression models are adequate to predicted the responses, which follows the experimental data with minimum absolute error. The AlCN/AlC coatings exhibited lower cutting forces and surface roughness than FeCrN coated tools. Tool wear was reduced by 3.62 times in AlCN/AlC and 1.63 times in FeCrN coated tools compared to uncoated tool which is due to increased hardness and elastic modulus of the coating. © 2018 IOP Publishing Ltd.Item Influence of deep cryogenic treatment on performance of cemented carbide (WC-Co) inserts during dry end milling of maraging steel(Elsevier Ltd, 2019) Varghese, V.; Ramesh, M.R.; Dupadu, D.Cryogenic treatment has developed as a technique to improve the life of the cutting tool, especially tungsten carbide inserts. The present study investigates the effect of cryogenic treatment of cemented carbide (WC-Co) inserts at the different soaking period of 18 h (CT-18), 24 h (CT-24) and 32 h (CT-32) at a sub-zero temperature of ?196 °C. The soaking period plays a crucial role in improving the wear resistance of the cryogenically treated tools. It is vital to determine the critical soaking period for the cryogenic treatment of cemented carbides. The mechanical and metallurgical characterization of cryogenically treated cemented carbide insert is carried out to understand the changes in the microstructure, grain size, chemical composition, microhardness and electrical conductivity after cryogenic treatment. The end milling experiments on maraging steel under dry environment are carried out using cryogenically treated inserts at different holding time and untreated inserts (UT). The machining performance of treated and untreated inserts are compared with respect to tool wear, surface roughness and cutting forces. The results revealed that cryogenic treatment is effective in resisting tool wear even at high spindle speeds. The cryogenically treated inserts exhibited higher tool life, better surface finish and lower cutting forces during machining at different spindle speeds. The optimum soaking time for cryogenic treatment of WC-Co inserts is found to be 24 h (CT-24) beyond which there is no improvement in microhardness and wear resistance. © 2018Item Microstructure and tribological characteristics of APS sprayed NiCrBSi/flyash cenosphere/Cr2O3 and NiCrBSi/flyash cenosphere/Mo composite coatings at elevated temperatures(Institute of Physics Publishing helen.craven@iop.org, 2019) Nagabhushana, N.; Rajanna, S.; Mathapati, M.; Ramesh, M.R.; Koppad, P.G.; Reddy, N.C.In the present investigation NiCrBSi/flyash/Cr2O3 and NiCrBSi/flyash/Mo composite coatings are developed using atmospheric plasma spray technique on superni 76 alloy. Coatings are characterized in terms of microstructure, phase analysis, and microhardness. Tribological properties of the coatings are evaluated using a pin on disc tribometer. Test is conducted under dry sliding conditions at room temperature, 200 °C, 400 °C, and 600 °C respectively. Microstructure and worn surfaces of the coatings are analyzed by utilizing Scanning Electron Microscope (SEM) where in phase analysis is carried out using x-ray diffractometer (XRD). XRD results revealed the presence of ?-Ni as primary phase along with Ni3B, Cr7C3, SiO2 and Al2O3 as minor phases in both the NiCrBSi/flyash/Cr2O3 and NiCrBSi/flyash/Mo coatings. Among the two coatings, Mo composite coating exhibited lower porosity and higher microhardness. The friction coefficient of both the coatings decreased with increasing temperature. The wear rate is found to decrease at lower temperatures but increased at a higher temperature (>400 °C) for Cr2O3 composite coating wherein Friction coefficient is decreased with increase in the temperature for Mo composite coatings. The worn surface analysis conducted revealed abrasive wear at lower temperatures while the transition from abrasive to adhesive is observed at higher temperatures. © 2019 IOP Publishing Ltd.Item High-temperature wear and frictional behavior of partially oxidized Al with NiCr composite coating(Institute of Physics Publishing helen.craven@iop.org, 2019) Medabalimi, S.R.; Ramesh, M.R.; Kadoli, R.The influence of composite coating in improving wear and frictional behavior from room temperature to 600 °C was investigated. Partially oxidized Al powder was prepared with a flame spray process by spraying pure Al powder into distilled water. The composite powder is the mixture of 30 weight percent of partially oxidized Al and 70 weight percent of NiCr alloy powder. The composite powder was subsequently coated on MDN321 steel by air plasma spray process. The composite coatings are characterized with respect to adhesion strength, porosity, micro-hardness, and density. Wear and frictional behavior of coatings are evaluated under disc speed of 1 and 2 m s-1, loads of 10, 20 and 30 N and 3000 m sliding distance. The test results indicated that at room temperature, frictional heat generated due to applied load produce three-body abrasion at the interface caused to increase the wear and friction in the coating. The oxide film formed at high temperature due to plastic deformation avoids surface degradation at the interface and reduce the wear and friction. The worn surfaces at 600 °C consist phases of ?-Al2O3, NiO, and Cr3O. These phases are contributing to improving the wear resistance of the coating more than 4-times compared to uncoated steels under varying load and sliding velocities. The coefficient of friction reduced with increase in temperature due to generated oxides act as lubricants at the interface. © 2019 IOP Publishing Ltd.Item Characterisation and performance evaluation of TiSiN &tiAlSiN coatings by RF magnetron sputtering deposition during end milling of maraging steel(Institute of Physics Publishing helen.craven@iop.org, 2019) Varghese, V.; Ramesh, M.R.; Dupadu, D.; Shaik, H.Monolayer nanostructured thin films of TiSiN & TiAlSiN were deposited on WC-Co milling inserts using RF magnetron sputtering for metal cutting. The alloy targets of TiSi (80/20 at%) & TiAlSi (34/56/10 at%) were used for the deposition in an Ar + N atmosphere. The deposition time and parameters are optimized to develop a uniform and homogenous coating. The mechanical and metallurgical properties are characterized to analyze the wear resistance of the coating. The machinability studies on MDN 250 maraging steel is carried out using TiSiN and TiAlSiN coated WC-Co inserts under dry and wet environment. The machining responses such as surface roughness, cutting force, tool wear and tool life are analyzed by varying spindle speed. The results showed that TiAlSiN coating had a higher wear resistance and machining performance compared to the TiSiN coating owing to the high hardness and plasticity index of the coating. © 2020 IOP Publishing Ltd.Item Evaluation of Wear Behaviour of Metal Injection Moulded Nickel Based Metal Matrix Composite(Springer Netherlands rbk@louisiana.edu, 2019) Veeresh Nayak, V.N.; Ramesh, M.R.; Desai, V.; Kumar Samanta, S.K.Metal injection moulding (MIM) is a near-net shape manufacturing technology for producing intricate parts, cost-effectively. MIM comprises combined techniques of plastic injection moulding and powder metallurgy. The present study focused on the development of the binder and fabrication of defect free MIM component. A wax-based binder system consisting of paraffin wax (PW), low density polyethylene (LDPE), polyethylene glycol (PEG-600) and stearic acid was established for MIM of NiCrSiB (70% Wt.) + Cr3C2-NiCr (30% Wt.) nickel based metal matrix composite (NMMC) powder. The feedstock was characterised through rheological properties at different temperatures. Injection temperature was determined from the rheological investigation of the feedstock having the 56% powder loading and 44% binder by volume. Sintering process was carried out with the temperature cycle in the range of 1250–1300 ?C under hydrogen purged atmosphere. The MIM components showed good and acceptable shrinkage in linear dimensions. The mechanical properties and wear behaviour of NMMC was studied using a pin-on-disc apparatus with alumina disc.Tests were performed under dry sliding conditions at room temperature and elevated temperatures of 200 and 400 ?C. Results shows that wear rate is maximum at 400 ?C for 40 N and lowest at room temperature for 10 N. Further wear mechanism was analysed using scanning electron microscope (SEM). © 2018, Springer Science+Business Media B.V., part of Springer Nature.Item Tribological behaviour of monolayer and multilayer Ti-based thin solid films deposited on alloy steel(Institute of Physics Publishing helen.craven@iop.org, 2019) V Badiger, P.V.; Desai, V.; Ramesh, M.R.; Joladarashi, S.; Gourkar, H.The fretting wear and adhesive wear resistance of Ti-based thin solid films deposited on MDN121 steel substrate are evaluated. Plasma-assisted cathodic arc evaporation technique is used to develop the TiC-C monolayer coating and Ti/TiN/TiCN/TiN/TiCN multilayer coatings used in the study. FESEM-EDS, nanoindentation, Raman spectroscopy, optical profiler, and confocal microscope are used to characterise the coatings and wear tracks. Diamond-like carbon is observed in the microstructure of both the coatings. During the fretting analysis, the coefficient of friction (COF) is reduced by 68.49% in the case of the TiC-C monolayer coating and 42.46% in the Ti multilayer coatings as compared to the substrate. The volumetric wear loss of the TiC-C monolayer coating is lower than the multilayer coating. The wear surface morphology reveals the abrasive form of the fretting wear mechanism in both the monolayer and multilayer coatings whereas the galling failure in the substrate. During adhesive wear, the COF is reduced by 71.73% in the monolayer coating and 59.33% in the multilayer coatings compared to the substrate. The monolayer coating exhibits low friction and low wear rate as compared to the multilayer coating. © 2018 IOP Publishing Ltd.Item Microstructure and tribological behavior of flame sprayed and microwave fused CoMoCrSi/CoMoCrSi-Cr3C2 coatings(Institute of Physics Publishing helen.craven@iop.org, 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.This present work deals with the investigation of dry sliding wear behavior of CoMoCrSi and CoMoCrSi-Cr3C2 depositing on titanium substrate through Flame spray process, subsequently fused by the microwave hybrid heating process. Prior to the deposition of the coating, CoMoCrSi powder is milled by using high energy ball milling (HEBM) process and later 30% of Cr3C2 powder is added. Microstructural features and phase analysis of milled powders, as-coated and microwave fused coatings are inspected by using SEM with EDS and XRD process respectively. The coatings before and after fusing are tested for microhardness and bond strength by using a Vickers microhardness and universal tensile machines respectively. Dry sliding wear behavior of coatings before and after fusing is conducted against alumina counter face at ambient and elevated temperatures, also normal load is varied. The wear mechanism of both coatings is examined by employing XRD, SEM-EDS techniques. The fused coatings exhibit lower friction and better wear resistance compared with as-deposited coatings. The detailed results of each test of their coatings are discussed in this paper. © 2018 IOP Publishing Ltd.