Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
43 results
Search Results
Item Microstructure Evolution and Mechanical and Corrosion Behavior of Accumulative Roll Bonded Mg-2%Zn/Al-7075 Multilayered Composite(Springer New York LLC barbara.b.bertram@gsk.com, 2017) Anne, G.; Ramesh, M.R.; Shivananda Nayaka, H.; Arya, S.B.; Sahu, S.Multilayered composite of Mg-2%Zn/Al-7075 was developed by accumulative roll bonding (ARB) of wrought Mg-2%Zn and aluminum 7075 alloy. The Mg-2%Zn/Al-7075 multilayered composite exhibited density of 2295 kg/m3 and an average grain size of 1 and 1.3 ?m in Mg-2%Zn and Al-7075 layers, respectively. A thorough microstructural characterization was performed on the composites by scanning electron microscope, electron backscatter diffraction (EBSD), transmission electron microscope and phase analysis by x-ray diffraction. In addition, mechanical properties were evaluated by microhardness and tensile tests. Corrosion behavior of the multilayered composite was examined using electrochemical polarization test. EBSD analysis showed the presence of ultrafine grains with high-angle grain boundaries. The composite exhibited a significant improvement in ultimate tensile strength (~1.82 times) and elongation (~1.5 times) as compared with Mg-2%Zn alloy, after four-pass ARB process. © 2017, ASM International.Item Development and properties evaluation of Mg-6% Zn/Al multilayered composites processed by accumulative roll bonding(Cambridge University Press, 2017) Anne, G.; Ramesh, M.R.; Shivananda Nayaka, H.; Arya, S.B.; Sahu, S.Accumulative roll bonding (ARB) process was used to develop Mg-6% Zn/Al and Mg-6% Zn/anodized-Al multilayered composites. Microstructural characterization was done using scanning electron microscopy, energy-dispersive X-ray spectroscopy, electron backscattered diffraction, and transmission electron microscopy. An average grain size measured in the roll-bonded layers of Al, anodized Al, and Mg-2% Zn was found to be 1.8 ?m, 1.6 ?m, and 0.6 ?m, respectively. Phases Al17Mg12, AlMg4Zn11, and Al2O3 after 5-pass of ARB were confirmed by X-ray diffraction analysis. The Mg-6% Zn/Al and Mg-6% Zn/anodized Al composites exhibited tensile strengths ?252 MPa and ?256 MPa, respectively, after a 5-pass ARB process. Hardness of the individual layers of composite increased linearly with an increase in the number of ARB passes. Fractographs of the multilayered composite illustrated the ductile failure in Al and anodized Al layers and transgranular brittle fracture in Mg-6% Zn layers. © Materials Research Society 2017.Item An experimental study of influence of wire electro discharge machining parameters on surface integrity of TiNiCo shape memory alloy(Cambridge University Press, 2017) Soni, H.; SannaYellappa, N.; Ramesh, M.R.Shape memory alloys (SMAs) are unique class of smart materials with excellent physical, mechanical and biomedical properties, which have wide applications in several fields such as aerospace, robotics, biomedical, and dental etc. These alloys are well known for exhibiting shape memory effect (SME) and pseudoelasticity (PE), it is a well-established fact that they are required to be processed into functioning parts. The conventional machining affects the internal properties of shape memory alloys and hence, it is reported that nonconventional machining techniques are more suitable. Wire electro discharge machining (WEDM) is one of the nonconventional machining processes for machining complicated shapes without hampering the internal properties of such type of materials. In the present experimental investigation, wire electro discharge machining of Ti50Ni40Co10 shape memory alloy (SMA) has been carried out and machining performances such as surface roughness (SR), and material removal rate (MRR) have been evaluated. Experimental results exposed that pulse on time, pulse off time and servo voltages are most influential process parameters on the responses. The machined surface has been characterised with respect to microstructure, microhardness, and phases formed. © Materials Research Society 2017.Item High temperature erosion behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere coating(Elsevier B.V., 2017) Mathapati, M.; Ramesh, M.R.; Doddamani, M.High temperature erosive behavior of plasma sprayed NiCrAlY-25WC-Co/cenosphere coating deposited on MDN 321 steel is investigated in the present work. Coating is characterized using Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). Microhardness, porosity, adhesion strength, fracture toughness and ductility of the coating are quantified. Solid particle erosion test is conducted at 200, 400 and 600 °C with 30 and 90° impact angles using alumina erodent. Optical profilometer is used to evaluate erosion volume loss. Erosion resistance of the coating is observed to be higher than the substrate for the test temperatures chosen and noted to be more prominent at lower impact angle and higher temperature. High temperature stability of mullite, alumina and oxide layer assists in increasing erosion resistance of coating. The eroded coating surface morphology reveals the brittle mode of material removal. © 2017 Elsevier B.V.Item Microstructure and Adhesion Strength of Ni3Ti Coating Prepared by Mechanical Alloying and HVOF(Pleiades Publishing compmg@maik.ru, 2018) Reddy, N.C.; Ajay Kumar, B.S.; Ramesh, M.R.; Koppad, P.G.In the present work we report the development of Ni3Ti intermetallic compound by high energy ball milling of Ni and Ti powders. The ball milled powders were taken at various intervals (4, 6, 8, 10, and 11 h) to analyze the formation of NixTix intermetallic compounds. The ball milled powders were analyzed using scanning electron microscopy and X-ray diffraction. The layered shaped powder particles of Ni3Ti phase were formed after 11 h of ball milling, which was confirmed by X-ray peaks. Further High-Velocity Oxy-Fuel (HVOF) process was used to coat Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) on MDN 420 steel. Both the coated materials displayed excellent cohesion with minimal porosity less than 2%. The tensile adhesion strength test was carried out on these coatings to check the bond strength. Out of the two the Ni3Ti coating showed excellent bond strength of 41.04 MPa compared to that of Ni3Ti + (Cr3C2 + 20NiCr) coating. © 2018, Pleiades Publishing, Ltd.Item Elevated temperature solid particle erosion behaviour of carbide reinforced CoCrAlY composite coatings(Institute of Physics Publishing helen.craven@iop.org, 2018) Nithin, H.S.; Desai, V.; Ramesh, M.R.CoCrAlY+WC-Co and CoCrAlY+Cr3C2-NiCr coatings are deposited on nickel based alloy using atmospheric plasma spray technique. Mechanical properties such as microhardness, adhesion strength and fracture toughness of coatings are evaluated. Elevated temperature solid particle erosion behaviour of these coatings are investigated at 600 °C using alumina erodent at 30 and 90° impact angle. Coatings are characterized utilizing Scanning electron microscope (SEM), x-ray diffraction (XRD) and Energy dispersive spectroscopy (EDS). CoCrAlY+WC-Co coating shows higher hardness, adhesion strength and fracture toughness than CoCrAlY+Cr3C2-NiCr coating. CoCrAlY+WC-Co coating exhibited approximately 3 times higher erosion resistance than CoCrAlY+Cr3C2-NiCr coating at 90° and 30° impact angles. SEM images of eroded surfaces of coatings reveals the combination of ductile and brittle fracture. CoCrAlY+Cr3C2-NiCr coating shows severe cracks, craters, carbide pull out and chipping than CoCrAlY+WC-Co coating. High temperature erosion is a combination of simultaneous building up of material by oxidation and removal of material by erosion process. Thus reforming the erosion process to oxidation modified erosion process. © 2018 IOP Publishing Ltd.Item Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating(Institute of Physics Publishing helen.craven@iop.org, 2018) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi superalloy powder (Tribaloy-T400) consists of intermetallic laves phase and primary eutectic phase of Co-rich solid solution. Processing of Tribaloy-T400 powder is carried out through high-energy ball milling (HEBM) technique to obtain a higher volume fraction of intermetallic laves phases. The feedstock is sprayed using high-velocity-oxy-fuel (HVOF) process on titanium grade-15 substrate. The coating microstructure is homogenized by microwave hybrid heating technique. Characterization of feedstock, as-sprayed and microwave fused coatings is done by using Scanning Electron Microscopy (SEM), Energy dispersive spectroscopy (EDS) and x-ray Diffraction (XRD). Porosity, surface roughness, microhardness, and bond strength are measured. Adhesive wear behavior of the coatings under the dry sliding condition is evaluated at an applied load of l0 and 20 N and temperature of 200, 400 and 600 °C Fused coating exhibit higher wear resistance than the as-sprayed coatings and substrate. The hard intermetallic laves phases which are amorphous (bulk metallic glass) in nature strengthen the coating at high temperatures. © 2018 IOP Publishing Ltd.Item Microstructure and tribological behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere/solid lubricants composite coatings(Elsevier B.V., 2018) Doddamani, M.; Mathapati, M.; Ramesh, M.R.Present investigation deal with NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2, NiCrAlY/WC-Co/Cenosphere/MoS2/CaSO4 and NiCrAlY/WC-Co/Cenosphere coatings deposited on MDN 321 steel using atmospheric plasma spraying. Tribological properties of MDN 321 steel and coatings are evaluated from room temperature (RT) to 600 °C under dry lubrication conditions using a pin on disc high-temperature tribometer. Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) and Energy Dispersive Spectroscopy (EDS) are used to characterize the coatings. Presence of cenospheres in these coatings might effectively reduce wear acting as localized regions accumulating wear debris. The result shows that wear rate of all the coatings are lower as compared to MDN 321 substrate at all the test conditions. NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2 and NiCrAlY/WC-Co/Cenosphere/MoS/CaSO4 coatings registered lower friction coefficient as compared to NiCrAlY/WC-Co/Cenosphere coating and MDN 321 substrate. Characterization of the NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2 and NiCrAlY/WC-Co/Cenosphere/MoS2/CaSO4 coatings worn out surface suggests that MoS2 provides lubrication at 200 °C and formation of CaMoO4, MoO3 through tribo chemistry reaction at higher temperature provides lubrication at 600 °C. SEM micrograph of worn surface demonstrates that the main wear mechanism is plowing and delamination. © 2018 Elsevier B.V.Item Plasma sprayed Cr3C2-NiCr/fly ash cenosphere coating: Cyclic oxidation behavior at elevated temperature(Institute of Physics Publishing helen.craven@iop.org, 2018) Doddamani, M.; Mathapati, M.; Ramesh, M.R.Oxidation is one of the major degradation phenomena observed in components subjected to higher temperatures like in thermal power plants (boiler tubes), steam and gas turbines blades etc. Developing protective coatings for such components mitigate oxidation. In the present study, plasma spray technique is utilized to deposit the Cr3C2-NiCr/Cenospheres coating on MDN 321 steel substrate. Thermo cyclic oxidation test is conducted at 600 °C (20 cycles) on both the coating and MDN 321 steel substrate. The thermogravimetric methodology is employed to estimate the oxidation kinetics. Energy Dispersive Spectroscopy (EDS), x-ray Diffraction (XRD), Scanning Electron Microscope (SEM) and x-ray mapping technique is employed to characterize the oxidized samples. Cr3C2-NiCr/Cenosphere coating displayed lower rate of oxidation as compared to substrate implying its suitability in high-temperature applications. Protective oxides like Al2O3, Cr2O3, and NiCr2O4 are observed on the uppermost layer of the coating lowering the oxidation rate in the developed coating. © 2018 IOP Publishing Ltd.Item Microstructure and tribological characteristics of APS sprayed NiCrBSi/flyash cenosphere/Cr2O3 and NiCrBSi/flyash cenosphere/Mo composite coatings at elevated temperatures(Institute of Physics Publishing helen.craven@iop.org, 2019) Nagabhushana, N.; Rajanna, S.; Mathapati, M.; Ramesh, M.R.; Koppad, P.G.; Reddy, N.C.In the present investigation NiCrBSi/flyash/Cr2O3 and NiCrBSi/flyash/Mo composite coatings are developed using atmospheric plasma spray technique on superni 76 alloy. Coatings are characterized in terms of microstructure, phase analysis, and microhardness. Tribological properties of the coatings are evaluated using a pin on disc tribometer. Test is conducted under dry sliding conditions at room temperature, 200 °C, 400 °C, and 600 °C respectively. Microstructure and worn surfaces of the coatings are analyzed by utilizing Scanning Electron Microscope (SEM) where in phase analysis is carried out using x-ray diffractometer (XRD). XRD results revealed the presence of ?-Ni as primary phase along with Ni3B, Cr7C3, SiO2 and Al2O3 as minor phases in both the NiCrBSi/flyash/Cr2O3 and NiCrBSi/flyash/Mo coatings. Among the two coatings, Mo composite coating exhibited lower porosity and higher microhardness. The friction coefficient of both the coatings decreased with increasing temperature. The wear rate is found to decrease at lower temperatures but increased at a higher temperature (>400 °C) for Cr2O3 composite coating wherein Friction coefficient is decreased with increase in the temperature for Mo composite coatings. The worn surface analysis conducted revealed abrasive wear at lower temperatures while the transition from abrasive to adhesive is observed at higher temperatures. © 2019 IOP Publishing Ltd.