Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
6 results
Search Results
Item HVOF sprayed Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings: Microstructure, microhardness and oxidation behaviour(Elsevier Ltd, 2018) Reddy, N.C.; Kumar, B.S.A.; Reddappa, H.N.; Ramesh, M.R.; Koppad, P.G.; Kord, S.This paper reports the development of Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings on AISI 420 stainless steel (MDN-420) and titanium alloy ASTM B265 (Ti-15) by HVOF technique. Microstructure, microhardness and high temperature oxidation behaviour of coatings were investigated. Microstructure of coatings was dense and displayed layers depicting lamellar structure. The microhardness of coatings was significantly higher than that of substrate owing to higher density and cohesive strength between individual splats of coating materials. Cyclic oxidation studies conducted on Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings showed oxide scale was composed of various oxides like NiO, NiCr2O4 and Cr2O3 phases. The formation of compact and protective NiO phase in case of Ni3Ti coatings; NiO and Cr2O3 phases in Ni3Ti+(Cr3C2+20NiCr) coatings stabilised the weight gain exhibited slow oxidation rate at higher temperatures. © 2017 Elsevier B.V.Item Cyclic Oxidation and Hot Corrosion Behavior of Plasma-Sprayed CoCrAlY + WC-Co Coating on Turbine Alloys(Springer New York LLC barbara.b.bertram@gsk.com, 2018) Nithin, H.S.; Vijay, D.; Ramesh, M.R.Components in energy-producing systems suffer a variety of degradation processes such as oxidation and molten salt-induced corrosion as a consequence of complex multi-component gaseous environment. Coatings provide a composition that will grow the protective scale at high temperatures having long-term stability. Plasma spraying was used to deposit CoCrAlY + WC-Co composite coatings on turbine alloys of Hastelloy X and AISI 321. The thermocyclic oxidation behavior of coated alloys was investigated in static air and in molten salt (Na2SO4-60%V2O5) environment at 700 °C. The thermogravimetric technique was used to approximate the kinetics of oxidation in 50 cycles, each cycle consisting of heating and cooling. X-ray diffraction and SEM/EDAX techniques are used to characterize the oxide scale formed. Coated alloys showed a lower corrosion rate as compared to uncoated alloys. The coatings subjected to oxidation and hot corrosion showed slow scale growth kinetics. Preferential oxidation of Co, Cr, W and its spinel blocks the transport of oxygen and corrosive species into the coating by providing a barrier, thereby making the oxidation rate to reach steady state. As compared to the substrate alloys, coatings show better hot corrosion resistance. © 2018, ASM International.Item Plasma sprayed Cr3C2-NiCr/fly ash cenosphere coating: Cyclic oxidation behavior at elevated temperature(Institute of Physics Publishing helen.craven@iop.org, 2018) Doddamani, M.; Mathapati, M.; Ramesh, M.R.Oxidation is one of the major degradation phenomena observed in components subjected to higher temperatures like in thermal power plants (boiler tubes), steam and gas turbines blades etc. Developing protective coatings for such components mitigate oxidation. In the present study, plasma spray technique is utilized to deposit the Cr3C2-NiCr/Cenospheres coating on MDN 321 steel substrate. Thermo cyclic oxidation test is conducted at 600 °C (20 cycles) on both the coating and MDN 321 steel substrate. The thermogravimetric methodology is employed to estimate the oxidation kinetics. Energy Dispersive Spectroscopy (EDS), x-ray Diffraction (XRD), Scanning Electron Microscope (SEM) and x-ray mapping technique is employed to characterize the oxidized samples. Cr3C2-NiCr/Cenosphere coating displayed lower rate of oxidation as compared to substrate implying its suitability in high-temperature applications. Protective oxides like Al2O3, Cr2O3, and NiCr2O4 are observed on the uppermost layer of the coating lowering the oxidation rate in the developed coating. © 2018 IOP Publishing Ltd.Item High-temperature wear and frictional behavior of partially oxidized Al with NiCr composite coating(Institute of Physics Publishing helen.craven@iop.org, 2019) Medabalimi, S.R.; Ramesh, M.R.; Kadoli, R.The influence of composite coating in improving wear and frictional behavior from room temperature to 600 °C was investigated. Partially oxidized Al powder was prepared with a flame spray process by spraying pure Al powder into distilled water. The composite powder is the mixture of 30 weight percent of partially oxidized Al and 70 weight percent of NiCr alloy powder. The composite powder was subsequently coated on MDN321 steel by air plasma spray process. The composite coatings are characterized with respect to adhesion strength, porosity, micro-hardness, and density. Wear and frictional behavior of coatings are evaluated under disc speed of 1 and 2 m s-1, loads of 10, 20 and 30 N and 3000 m sliding distance. The test results indicated that at room temperature, frictional heat generated due to applied load produce three-body abrasion at the interface caused to increase the wear and friction in the coating. The oxide film formed at high temperature due to plastic deformation avoids surface degradation at the interface and reduce the wear and friction. The worn surfaces at 600 °C consist phases of ?-Al2O3, NiO, and Cr3O. These phases are contributing to improving the wear resistance of the coating more than 4-times compared to uncoated steels under varying load and sliding velocities. The coefficient of friction reduced with increase in temperature due to generated oxides act as lubricants at the interface. © 2019 IOP Publishing Ltd.Item Developing partially oxidized NiCr coatings using the combined flame spray and plasma spray process for improved wear behaviour at high temperature(Elsevier Ltd, 2021) Medabalimi, S.R.; Ramesh, M.R.; Kadoli, R.The powders of NiCrBSiFe and NiCr are partially oxidized using a flame spray process and are deposited on MDN321 steel substrate using a plasma spray process. The effect of partial oxidization on microstructure, microhardness, density, bond strength, and porosity of the coatings is analyzed. The friction and wear behaviour of the coatings was assessed using a pin-on-disc tribometer by varying loads (10, 20 and 30 N), sliding velocities (1, 2 m/s) and temperatures (RT, 200, 400 and 600 °C). Worn surfaces of NiCrBSiFe and NiCr coatings consist of oxide phases of SiO2, NiO, Cr2O3 and NiCr2O4 at elevated temperatures. These phases contributed to reducing the wear rate by five folds in coated steels compared to uncoated steels at 600 °C. The wear rate in coating decreases with an increase in temperature. The coefficient of friction was reduced gradually with the temperature in coatings and substrate. The wear rate coefficient of NiCr coating was 1.7 times higher than the NiCrBSiFe coating. © 2021 Elsevier B.V.Item Cyclic Oxidation and Hot-Corrosion Behavior of HVOF-Sprayed NiCrAl Coating on Industrial Boiler Tube Steels(Springer, 2024) Ramesh, M.R.; Medabalimi, S.; Rupanagudi, R.S.; Prasad, C.D.; Sollapur, S.B.At high temperatures, coatings provide a protective scale development on surfaces to maintain long-term stability. In the current study, ASTM-SA210-Grade A1 (GrA1) and ASTM-SA213-T-11 (T11) boiler tube steels were coated with NiCrAl alloy with high-velocity oxy-fuel (HVOF) to prevent oxidation and hot corrosion. For hot corrosion and oxidation, 50 cycles at 900°C were taken into account. Additionally, tests of hot-corrosion behavior were conducted in an atmosphere containing molten salt (Na2SO4-60%V2O5), while tests of oxidation behavior were conducted in static air. The kinetics of oxidation were calculated using the thermogravimetric method. Using XRD, EPMA, and SEM/EDAX methods, the produced oxide scales were characterized. The oxidation rate of NiCrAl-coated steels was found to be lower than that of uncoated steels. The coated steels subjected to oxidation in air exhibit slow scale growth kinetics and oxides of α-Al2O3 and Cr2O3 on the outermost surface, while accelerated oxidation caused by the molten salt exhibits metastable Al2O3. Along the nickel-rich splat boundary, Cr and Al were formed a preferential oxidation, which prevents other oxygen from entering the coating via pores and voids, resulting in steady-state oxidation. © The Minerals, Metals & Materials Society 2024.