Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
6 results
Search Results
Item Microstructure and Adhesion Strength of Ni3Ti Coating Prepared by Mechanical Alloying and HVOF(Pleiades Publishing compmg@maik.ru, 2018) Reddy, N.C.; Ajay Kumar, B.S.; Ramesh, M.R.; Koppad, P.G.In the present work we report the development of Ni3Ti intermetallic compound by high energy ball milling of Ni and Ti powders. The ball milled powders were taken at various intervals (4, 6, 8, 10, and 11 h) to analyze the formation of NixTix intermetallic compounds. The ball milled powders were analyzed using scanning electron microscopy and X-ray diffraction. The layered shaped powder particles of Ni3Ti phase were formed after 11 h of ball milling, which was confirmed by X-ray peaks. Further High-Velocity Oxy-Fuel (HVOF) process was used to coat Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) on MDN 420 steel. Both the coated materials displayed excellent cohesion with minimal porosity less than 2%. The tensile adhesion strength test was carried out on these coatings to check the bond strength. Out of the two the Ni3Ti coating showed excellent bond strength of 41.04 MPa compared to that of Ni3Ti + (Cr3C2 + 20NiCr) coating. © 2018, Pleiades Publishing, Ltd.Item Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating(Institute of Physics Publishing helen.craven@iop.org, 2018) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi superalloy powder (Tribaloy-T400) consists of intermetallic laves phase and primary eutectic phase of Co-rich solid solution. Processing of Tribaloy-T400 powder is carried out through high-energy ball milling (HEBM) technique to obtain a higher volume fraction of intermetallic laves phases. The feedstock is sprayed using high-velocity-oxy-fuel (HVOF) process on titanium grade-15 substrate. The coating microstructure is homogenized by microwave hybrid heating technique. Characterization of feedstock, as-sprayed and microwave fused coatings is done by using Scanning Electron Microscopy (SEM), Energy dispersive spectroscopy (EDS) and x-ray Diffraction (XRD). Porosity, surface roughness, microhardness, and bond strength are measured. Adhesive wear behavior of the coatings under the dry sliding condition is evaluated at an applied load of l0 and 20 N and temperature of 200, 400 and 600 °C Fused coating exhibit higher wear resistance than the as-sprayed coatings and substrate. The hard intermetallic laves phases which are amorphous (bulk metallic glass) in nature strengthen the coating at high temperatures. © 2018 IOP Publishing Ltd.Item Microstructure and tribological behavior of flame sprayed and microwave fused CoMoCrSi/CoMoCrSi-Cr3C2 coatings(Institute of Physics Publishing helen.craven@iop.org, 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.This present work deals with the investigation of dry sliding wear behavior of CoMoCrSi and CoMoCrSi-Cr3C2 depositing on titanium substrate through Flame spray process, subsequently fused by the microwave hybrid heating process. Prior to the deposition of the coating, CoMoCrSi powder is milled by using high energy ball milling (HEBM) process and later 30% of Cr3C2 powder is added. Microstructural features and phase analysis of milled powders, as-coated and microwave fused coatings are inspected by using SEM with EDS and XRD process respectively. The coatings before and after fusing are tested for microhardness and bond strength by using a Vickers microhardness and universal tensile machines respectively. Dry sliding wear behavior of coatings before and after fusing is conducted against alumina counter face at ambient and elevated temperatures, also normal load is varied. The wear mechanism of both coatings is examined by employing XRD, SEM-EDS techniques. The fused coatings exhibit lower friction and better wear resistance compared with as-deposited coatings. The detailed results of each test of their coatings are discussed in this paper. © 2018 IOP Publishing Ltd.Item Effect of microwave heating on microstructure and elevated temperature adhesive wear behavior of HVOF deposited CoMoCrSi-Cr3C2 coating(Elsevier B.V., 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.This research reports the improvement of high-temperature sliding wear resistance of a grade 15 titanium alloy protected by an HVOF sprayed CoMoCrSi-Cr3C2 coating. The coatings have been tested in as-sprayed condition and after a post-deposition microwave heating step. The powder feedstock has been manufactured by high energy ball milling. X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM) equipped with the Energy Dispersive Spectroscopy (EDS) methods were used for coatings characterization. Surface roughness, microhardness, adhesion strength, and porosity of coatings were also measured. The wear test was conducted at an applied load of l0 N and 20 N with varying temperatures of 200 °C, 400 °C, and 600 °C under dry sliding conditions. Co3Mo2Si, Co7Mo6, Mo3Si, Co3Mo, and Co2Mo3 were the intermetallic laves phases generated in the CoMoCrSi feedstock during HEBM process. The microwave-fused coating exhibited metallurgical bonding, homogeneous structure, less porosity, and greater hardness as compared to as-sprayed coating. Microwave-treated coating revealed better wear property than an as-sprayed coating. This was mainly due to the intermetallic formation and metallurgical bonding in coatings. The fused coatings exhibit tribo-oxide layers during sliding action which was the main phenomenon of improving the wear resistance of the fused composite coatings. © 2019 Elsevier B.V.Item Comparison of Microstructural and Sliding Wear Resistance of HVOF Coated and Microwave Treated CoMoCrSi-WC + CrC + Ni and CoMoCrSi-WC + 12Co Composite Coatings Deposited on Titanium Substrate(Springer Science and Business Media B.V. editorial@springerplus.com, 2020) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi-WC + CrC + Ni and CoMoCrSi-WC + 12Co composite coatings are coated on titanium substrate by high velocity oxygen fuel method (HVOF). Prior to spraying, CoMoCrSi feedstock are processed through high energy ball milling (HEBM) in order improve the intermetallic laves phases and to reduce its particle size. The processed feedstock exhibits amorphous nature by improving laves phases and particle size of 60.12 ?m. Microwave heating energy is utilized as post heat treatment technique to improve the mechanical and metallurgical properties of as-sprayed coatings. Fused coatings reveals better properties in terms of surface roughness, porosity, microhardness and adhesion strength compared to as-sprayed coatings. Metallurgical bonding is observed in case of fused coatings due to diffusion of substrate elements. Frictional and wear behaviors have been investigated by a pin on disc apparatus at temperatures of 200 °C, 400 °C, and 600 °C under normal loads of 10 N and 20 N. Both wear trace and friction coefficients of the fused coatings are smaller than as-sprayed coatings and substrate at all test temperatures. The wear traces of fused coatings decreased with increasing the surface temperature due to the lubricant effect of cobalt oxides formed on the sliding surface. As a result, cobalt based cermet coatings are highly recommended as a durability improvement coating for the protection of sliding surface, such as high speed spindle. © 2020, Springer Nature B.V.Item Elevated temperature tribological performance of non-equiatomic CoCrNiTiWx high entropy alloy coatings developed by mechanical alloying and high-velocity oxy-fuel spray(Elsevier B.V., 2024) Addepalli, S.N.; Joladarashi, S.; Ramesh, M.R.High entropy alloys (HEA) have applications in multiple fields owing to their exceptional mechanical and physical properties. In the current study, mechanical alloyed CoCrNiTiWx (x; a molar fraction, x = 0.5 and 1.5) HEA feedstock powders were deposited on maraging steel substrate using high-velocity oxy-fuel spray (HVOF). The phase evolution and the microstructure of the milled powders and as-sprayed coatings were analysed by X-ray diffraction (XRD) and scanning electron microscope (SEM). The tribological behaviour of CoCrNiTiW0.5 and CoCrNiTiW1.5 HEA coatings at elevated temperatures was studied extensively using a Pin-on-Disc tribometer. The CoCrNiTiW0.5 and CoCrNiTiW1.5 HEA coatings retained the BCC solid solution phases formed during the milling stage. However, additional oxide and intermetallic phases were formed owing to the in-flight oxidation and high temperatures experienced during the HVOF deposition. The deposited coatings exhibited a lamellar structure and good mechanical bonding with the substrate. The porosities of CoCrNiTiW0.5 and CoCrNiTiW1.5 HEA coatings were found to be 1.69 ± 0.32 % and 1.51 ± 0.37 % respectively.Consequently, the CoCrNiTiW0.5 and CoCrNiTiW1.5 HEA coatings displayed average microhardness values of 863 ± 52 HV0.3 and 1025 ± 39 HV0.3, respectively. Further, the wear rates of coatings exhibited a significant reduction at elevated temperatures, owing to the formation of TiO2, NiCr2O4 oxide tribofilms for CoCrNiTiW0.5, and CoCr2O4, NiWO4, WO3 oxides for CoCrNiTiW1.5. The specific wear rate of CoCrNiTiW0.5 HEA coating dropped by 73.6 % from 22.7 ± 2.6 × 10−6 mm3/N-m to 5.99 ± 1.9 × 10−6 mm3/N-m, while CoCrNiTiW1.5 dropped by 78.8 % from 11.86 ± 3.5 × 10−6 mm3/N-m to 2.51 ± 1.5 × 10−6 mm3/N-m, with a rise in the temperature from RT to 600 °C. Likewise, The frictional coefficients of CoCrNiTiW0.5 HEA dropped from 0.504 ± 0.015 to 0.397 ± 0.005, while CoCrNiTiW1.5 HEA dropped from 0.578 ± 0.025 to 0.471 ± 0.004, with a rise in temperature from RT to 600 °C. At room temperature, the wear mechanisms of the as-sprayed CoCrNiTiWx coatings were dominated by adhesive wear. However, at elevated temperatures, a shift towards oxidative wear was observed. © 2023 Elsevier B.V.