Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
7 results
Search Results
Item Processing of cenosphere/HDPE syntactic foams using an industrial scale polymer injection molding machine(Elsevier Ltd, 2016) Bharath Kumar, B.R.; Doddamani, M.R.; Zeltmann, S.E.; Gupta, N.; Ramesh, M.R.; Ramakrishna, S.Rapid production of high quality components is the key to cost reduction in industrial applications. The present work is the first attempt of manufacturing syntactic foams, hollow particle filled lightweight composites, using an industrial scale injection molding machine. High density polyethylene (HDPE) is used as the matrix material and fly ash cenospheres are used as the filler. Development of syntactic foams with cenospheres serves dual purpose of beneficial utilization of industrial waste fly ash and reduction in the cost of the component. The pressure and temperature used in the injection molding process are optimized to minimize fracture of cenospheres and obtain complete mixing of cenospheres with HDPE. The optimized parameters are used for manufacturing syntactic foams with 20, 40 and 60 wt.% cenospheres. With increasing cenosphere content, density and strength reduce and modulus increases. Surface modification of constituents results in rise in strength with increasing filler content. A theoretical model based on a differential scheme is used to estimate the properties of cenospheres by conducting parametric studies because of inherent difficulties in direct measurement of cenosphere properties. The potential for using the optimized injection molding process is demonstrated by casting several industrial components. © 2015 Elsevier Ltd.Item High temperature erosion behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere coating(Elsevier B.V., 2017) Mathapati, M.; Ramesh, M.R.; Doddamani, M.High temperature erosive behavior of plasma sprayed NiCrAlY-25WC-Co/cenosphere coating deposited on MDN 321 steel is investigated in the present work. Coating is characterized using Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). Microhardness, porosity, adhesion strength, fracture toughness and ductility of the coating are quantified. Solid particle erosion test is conducted at 200, 400 and 600 °C with 30 and 90° impact angles using alumina erodent. Optical profilometer is used to evaluate erosion volume loss. Erosion resistance of the coating is observed to be higher than the substrate for the test temperatures chosen and noted to be more prominent at lower impact angle and higher temperature. High temperature stability of mullite, alumina and oxide layer assists in increasing erosion resistance of coating. The eroded coating surface morphology reveals the brittle mode of material removal. © 2017 Elsevier B.V.Item High-Temperature Erosive Behavior of Plasma Sprayed Cr3C2-NiCr/Cenosphere Coating(Springer New York LLC barbara.b.bertram@gsk.com, 2018) Mathapati, M.; Doddamani, M.; Ramesh, M.R.This research examines the deposition of Cr3C2-NiCr/cenosphere and Cr3C2-NiCr coatings on MDN 321 steel through the process of plasma spray. In this process, the solid particle erosion test is established at 200, 400, 600 °C with 30° and 90° impact angles. Alumina erodent is adopted to investigate the erosive behavior of the coating at higher temperatures. The properties of the Cr3C2-NiCr/cenosphere coating are established based on the microhardness, the adhesive strength, the fracture toughness, and the ductility. To quantify volume loss as a result of erosion, an optical profilometer is used. At higher temperature, decrease in the erosion volume loss of Cr3C2-NiCr/cenosphere and Cr3C2-NiCr coatings is observed. The erosion-resistive property of Cr3C2-NiCr/cenosphere coating is higher than that of MDN 321 steel by 76%. This property is influenced by high-temperature stability of mullite, alumina, and protective oxide layer that is formed at elevated temperatures. The morphology of eroded coating discloses a brittle mode of material removal. © 2018, ASM International.Item Microstructure and tribological behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere/solid lubricants composite coatings(Elsevier B.V., 2018) Doddamani, M.; Mathapati, M.; Ramesh, M.R.Present investigation deal with NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2, NiCrAlY/WC-Co/Cenosphere/MoS2/CaSO4 and NiCrAlY/WC-Co/Cenosphere coatings deposited on MDN 321 steel using atmospheric plasma spraying. Tribological properties of MDN 321 steel and coatings are evaluated from room temperature (RT) to 600 °C under dry lubrication conditions using a pin on disc high-temperature tribometer. Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) and Energy Dispersive Spectroscopy (EDS) are used to characterize the coatings. Presence of cenospheres in these coatings might effectively reduce wear acting as localized regions accumulating wear debris. The result shows that wear rate of all the coatings are lower as compared to MDN 321 substrate at all the test conditions. NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2 and NiCrAlY/WC-Co/Cenosphere/MoS/CaSO4 coatings registered lower friction coefficient as compared to NiCrAlY/WC-Co/Cenosphere coating and MDN 321 substrate. Characterization of the NiCrAlY/WC-Co/Cenosphere/MoS2/CaF2 and NiCrAlY/WC-Co/Cenosphere/MoS2/CaSO4 coatings worn out surface suggests that MoS2 provides lubrication at 200 °C and formation of CaMoO4, MoO3 through tribo chemistry reaction at higher temperature provides lubrication at 600 °C. SEM micrograph of worn surface demonstrates that the main wear mechanism is plowing and delamination. © 2018 Elsevier B.V.Item Plasma sprayed Cr3C2-NiCr/fly ash cenosphere coating: Cyclic oxidation behavior at elevated temperature(Institute of Physics Publishing helen.craven@iop.org, 2018) Doddamani, M.; Mathapati, M.; Ramesh, M.R.Oxidation is one of the major degradation phenomena observed in components subjected to higher temperatures like in thermal power plants (boiler tubes), steam and gas turbines blades etc. Developing protective coatings for such components mitigate oxidation. In the present study, plasma spray technique is utilized to deposit the Cr3C2-NiCr/Cenospheres coating on MDN 321 steel substrate. Thermo cyclic oxidation test is conducted at 600 °C (20 cycles) on both the coating and MDN 321 steel substrate. The thermogravimetric methodology is employed to estimate the oxidation kinetics. Energy Dispersive Spectroscopy (EDS), x-ray Diffraction (XRD), Scanning Electron Microscope (SEM) and x-ray mapping technique is employed to characterize the oxidized samples. Cr3C2-NiCr/Cenosphere coating displayed lower rate of oxidation as compared to substrate implying its suitability in high-temperature applications. Protective oxides like Al2O3, Cr2O3, and NiCr2O4 are observed on the uppermost layer of the coating lowering the oxidation rate in the developed coating. © 2018 IOP Publishing Ltd.Item Microstructure and tribological characteristics of APS sprayed NiCrBSi/flyash cenosphere/Cr2O3 and NiCrBSi/flyash cenosphere/Mo composite coatings at elevated temperatures(Institute of Physics Publishing helen.craven@iop.org, 2019) Nagabhushana, N.; Rajanna, S.; Mathapati, M.; Ramesh, M.R.; Koppad, P.G.; Reddy, N.C.In the present investigation NiCrBSi/flyash/Cr2O3 and NiCrBSi/flyash/Mo composite coatings are developed using atmospheric plasma spray technique on superni 76 alloy. Coatings are characterized in terms of microstructure, phase analysis, and microhardness. Tribological properties of the coatings are evaluated using a pin on disc tribometer. Test is conducted under dry sliding conditions at room temperature, 200 °C, 400 °C, and 600 °C respectively. Microstructure and worn surfaces of the coatings are analyzed by utilizing Scanning Electron Microscope (SEM) where in phase analysis is carried out using x-ray diffractometer (XRD). XRD results revealed the presence of ?-Ni as primary phase along with Ni3B, Cr7C3, SiO2 and Al2O3 as minor phases in both the NiCrBSi/flyash/Cr2O3 and NiCrBSi/flyash/Mo coatings. Among the two coatings, Mo composite coating exhibited lower porosity and higher microhardness. The friction coefficient of both the coatings decreased with increasing temperature. The wear rate is found to decrease at lower temperatures but increased at a higher temperature (>400 °C) for Cr2O3 composite coating wherein Friction coefficient is decreased with increase in the temperature for Mo composite coatings. The worn surface analysis conducted revealed abrasive wear at lower temperatures while the transition from abrasive to adhesive is observed at higher temperatures. © 2019 IOP Publishing Ltd.Item Hot corrosion behavior of plasma sprayed FeCrNiC and FeCrNiC/Cenosphere coatings on ASTM-SA213-T22 steel(Elsevier Ltd, 2022) Hanumanthlal, S.; Siddaraju, C.; Ramesh, M.R.; Thirtha Prasada, H.P.; Somasundaram, B.The steel alloys tubes used to manufacture boilers which are used in high temperature environment in thermal power plants are often subjected to high temperature corrosion. Therefore, to protect the surface of boiler tubes, protective coatings are used to counter the corrosion. In this work FeCrNiC and FeCrNiC/Cenosphere coatings deposited on T22 boiler tube steel using atmospheric plasma spraying. Thermocyclic hot corrosion studies were examined in a liquid salt condition of Na2SO4-60%V2O5 for 17 cycles of 51 h at 600 °C on uncoated and coated steel. Thermogravimetric practice was utilized to build up the kinetics of hot corrosion of uncoated and coated steel. As-coated samples are studied for microstructure and microhardness. The X-ray diffraction(XRD), Scanning electron microscopy(SEM)/Energy dispersive spectroscopy(EDX), and X-ray mapping characterization techniques were used to analyse the corrosion products. It was observed that FeCrNiC/Cenosphere coated steel showed better hot corrosion resistance than the uncoated steels. Parabolic rate constant values of coated steel are lower in comparison to the uncoated steels. Better resistance is provided by high-temperature stability of mullite, alumina, defensive glassy oxide layer of silicon, titanium and spinels of chromium and carbon that is formed at elevated temperatures. © 2021