Item Ductile cast iron samples were austenitized at 927 °C and subsequently austempered for 30 minutes, 1 hour, and 2 hours at 260 °C, 288 °C, 316 °C, 343 °C, 371 °C, and 399 °C. These were subjected to a plane strain fracture toughness test. Fracture toughness was found to initially increase with austempering temperature, reach a maximum, and then decrease with further rise in temperature. The results of the fracture toughness study and fractographic examination were correlated with microstructural features such as bainite morphology, the volume fraction of retained austenite, and its carbon content. It was found that fracture toughness was maximized when the microstructure consisted of lower bainite with about 30 vol pet retained austenite containing more than 1.8 wt pet carbon. A theoretical model was developed, which could explain the observed variation in fracture toughness with austempering temperature in terms of microstructural features such as the width of the ferrite blades and retained austenite content. A plot of KIC2 against ?? (X?C?)1/2 resulted in a straight line, as predicted by the model.(Minerals, Metals and Materials Society, Dependence of Fracture Toughness of Austempered Ductile Iron on Austempering Temperature) Prasad Rao, P.; Putatunda, S.K.1998Item Ductile cast iron was austenitized at four different temperatures and subsequently austempered at six different temperatures. Plane strain fracture toughness was evaluated under all the heat treatment conditions and correlated with the microstructural features such as the austenite content and the carbon content of the austenite. Fracture mechanism was studied by scanning electron microscopy. It was found that the optimum austempering temperature for maximum fracture toughness decreased with increasing austenitizing temperature. This could be interpreted in terms of the microstructural features. A study of the fracture mechanism revealed that good fracture toughness is unlikely to be obtained when austempering temperature is less than half of the austenitizing temperature on the absolute scale. © 2002 Elsevier Science B.V. All rights reserved.(Elsevier BV, Investigations on the fracture toughness of austempered ductile irons austenitized at different temperatures) Prasad Rao, R.; Putatunda, S.K.2003