Item Rotating bending fatigue tests were carried out on austempered ductile iron containing 1.5 wt% nickel and 0.3 wt% molybdenum. The ductile iron was austenitized at 900 or 1050 °C and then austempered at 280 or 400 °C for different lengths of time to obtain different microstructures. The fatigue strength was correlated with the amount of retained austenite and its carbon content, which were both determined by X-ray diffraction technique. While the tensile strength decreased with increasing retained austenite content, the fatigue strength was found to increase. Carbide precipitation was found to be detrimental to fatigue strength. Lower austenitizing temperature resulted in better fatigue strength. © 1994 Chapman & Hall.(Kluwer Academic Publishers, Effect of microstructure on the fatigue strength of an austempered ductile iron) Shanmugam, P.; Prasad Rao, P.; Rajendra Udupa, K.; Venkataraman, N.1994Item Austempered ductile iron containing 0.9 Ni and 0.3 Mo and subject to low stress dry sand abrasive testing shows that wear behaviour is very sensitive to heat treatment conditions. It is concluded that large retained austenite content promotes wear resistance.(Inst of Engineers (India), Low stress dry sand abrasive wear behaviour of austempered ductile iron) Prasad Rao, P.1995Item An alloy containing 49 at.% aluminium was heat treated at different temperatures within the ? + ? two-phase field to get five different volume fractions of lamellar constituent. Creep studies were carried out on these samples at five different temperatures in the interval between 1023 and 1223 K, by impression creep technique using four levels of stresses at each temperature. For a given temperature and stress, steady state impression velocity decreased with increasing volume fraction of lamellar constituent. Activation energy for steady state creep increased linearly with lamellar content from 185 kJ/mol at 22 vol.% to 362 kJ/mol at 100 vol.%. The stress exponent was found to be around 1.2 in all the cases. The results show that a fully lamellar structure has a superior behaviour where creep is an important factor.(Carl Hanser Verlag, Effect of microstructure on the impression creep of two-phase titanium aluminide) Prasad Rao, P.; Swamy, K.Shivananda1995