Item Cu-44Ni-5Cr alloy has been subjected to thermomechanical treatment which consisted of plastic deformation of as-quenched material by 50, 65 and 80% reduction in thickness followed by ageing in the interval of 500 to 650 °C for various durations of time. Progress in age-hardening was studied by means of hardness measurement and X-ray diffraction studies. The wavelength of composition modulation and strain amplitude were measured. It was found that age-hardening was a result of interaction between spinodal decomposition and recovery processes. Prior deformation was found to enhance the kinetics of both spinodal decomposition and coarsening. It was concluded that this resulted from increased vacancy concentration and increased coherency strain in the cold-worked material. © 1994 Chapman & Hall.(Kluwer Academic Publishers, Effect of thermomechanical treatment on the phase transformation in Cu-44Ni-5Cr alloy) Raghavendra Bhat, R.; Prasad Rao, P.1994Item Progress in spinodal decomposition of a Cu-32Ni-2Cr alloy subjected to quench?age and quench?work?age treatments have been studied through hardness measurements as well as by X-ray diffraction techniques. It is found that recovery processes occur during early stages of aging which are interpreted in terms of the migration of matrix dislocations to interfaces. The kinetics of spinodal decomposition is found to be enhanced by prior deformation. Thermomechanical treatment results in a substantial increase in strength.(Publ by Carl Hanser Verlag GmbH & Co, Thermomechanical treatment of spinodal Cu-32Ni-2Cr alloy) Bhat, R.Raghavendra; Prasad Rao, P.1994