Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
9 results
Search Results
Item Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating(Institute of Physics Publishing helen.craven@iop.org, 2018) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi superalloy powder (Tribaloy-T400) consists of intermetallic laves phase and primary eutectic phase of Co-rich solid solution. Processing of Tribaloy-T400 powder is carried out through high-energy ball milling (HEBM) technique to obtain a higher volume fraction of intermetallic laves phases. The feedstock is sprayed using high-velocity-oxy-fuel (HVOF) process on titanium grade-15 substrate. The coating microstructure is homogenized by microwave hybrid heating technique. Characterization of feedstock, as-sprayed and microwave fused coatings is done by using Scanning Electron Microscopy (SEM), Energy dispersive spectroscopy (EDS) and x-ray Diffraction (XRD). Porosity, surface roughness, microhardness, and bond strength are measured. Adhesive wear behavior of the coatings under the dry sliding condition is evaluated at an applied load of l0 and 20 N and temperature of 200, 400 and 600 °C Fused coating exhibit higher wear resistance than the as-sprayed coatings and substrate. The hard intermetallic laves phases which are amorphous (bulk metallic glass) in nature strengthen the coating at high temperatures. © 2018 IOP Publishing Ltd.Item Effect of microwave heating on microstructure and elevated temperature adhesive wear behavior of HVOF deposited CoMoCrSi-Cr3C2 coating(Elsevier B.V., 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.This research reports the improvement of high-temperature sliding wear resistance of a grade 15 titanium alloy protected by an HVOF sprayed CoMoCrSi-Cr3C2 coating. The coatings have been tested in as-sprayed condition and after a post-deposition microwave heating step. The powder feedstock has been manufactured by high energy ball milling. X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM) equipped with the Energy Dispersive Spectroscopy (EDS) methods were used for coatings characterization. Surface roughness, microhardness, adhesion strength, and porosity of coatings were also measured. The wear test was conducted at an applied load of l0 N and 20 N with varying temperatures of 200 °C, 400 °C, and 600 °C under dry sliding conditions. Co3Mo2Si, Co7Mo6, Mo3Si, Co3Mo, and Co2Mo3 were the intermetallic laves phases generated in the CoMoCrSi feedstock during HEBM process. The microwave-fused coating exhibited metallurgical bonding, homogeneous structure, less porosity, and greater hardness as compared to as-sprayed coating. Microwave-treated coating revealed better wear property than an as-sprayed coating. This was mainly due to the intermetallic formation and metallurgical bonding in coatings. The fused coatings exhibit tribo-oxide layers during sliding action which was the main phenomenon of improving the wear resistance of the fused composite coatings. © 2019 Elsevier B.V.Item Development and Sliding Wear Behavior of Co-Mo-Cr-Si Cladding through Microwave Heating(Springer editorial@springerplus.com, 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.The aim of the present study is to improve the sliding wear resistance of pure titanium grade-2 substrate by developing CoMoCrSi (Tribaloy T400) cladding on it by using microwave hybrid heating technique. The developed cladding is characterized by microstructural features, phase analysis, measurement of microhardness by employing a scanning electron microscope (SEM), X-ray diffraction (XRD) and Vickers microhardness. The cladding and substrate are subjected to sliding wear test against alumina counterpart at elevated temperatures under dry conditions using a pin on disc tribometer. The test is performed by varying normal load and temperatures, whereas sliding speed is maintained constant. The developed clad shown partial melting of CoMoCrSi powders and obtained sound metallurgical bonding with the substrate. The high specific energy of microwave diluted the substrate atoms into cladding region which forms Cr3C2, Co3Ti, and TiC, phases confirmed by phase analysis. The cladding obtained better porosity and microhardness are 1.5 ± 0.2% ?m and 760 ± 35 Hv respectively. The substrate exhibits low microhardness of 182 ± 25 Hv. The cladding exhibits 6 times of lower volume loss and 70.14% of less wear rate with respect to the substrate. The cladding experienced least coefficient of friction is 0.55 compared with the substrate. The worn surfaces of cladding and substrate are examined. The detailed mechanism of wear is discussed in this paper. © 2019, Springer Nature B.V.Item High-Temperature Oxidation Studies of Plasma-Sprayed NiCrAlY/TiO2 and NiCrAlY/Cr2O3/YSZ Cermet Composite Coatings on MDN-420 Special Steel Alloy(Springer, 2021) Madhu Sudana Reddy, G.; Prasad, C.D.; Shetty, G.; Ramesh, M.R.; Rao, T.N.; Patil, P.The plasma spray process was used to form 70%NiCrAlY + 30%TiO2 and 70%NiCrAlY + 25%Cr2O3 + 5%YSZ cermet coatings on MDN-420 special steel alloy. Cyclic oxidation testing was conducted on coated and uncoated specimens at 700°C under a static air environment. Thermogravimetric analysis was applied to establish the oxidation kinetics. X-ray diffraction (XRD), scanning electron microscopy (SEM)/energy-dispersive x-ray spectroscopy (EDS), and electron probe microanalysis (EPMA) techniques were used to analyze the oxidized products. The NiCrAlY + Cr2O3 + YSZ coating was found to be most resistive when compared with the NiCrAlY + TiO2 coating in the aggressive oxidation environment. Net weight loss was observed for bare MDN-420 alloy due to sputtering. The oxidation resistance of the coatings was due to formation of Cr2O3, NiCr2O4, NiO, and Al2O3 phases. © 2021, ASM International.Item Elevated temperature erosion performance of plasma sprayed NiCrAlY/TiO2coating on MDN 420 steel substrate(Institute of Physics, 2022) Reddy G, M.S.; Prasad, C.D.; Patil, P.; Naresh, N.; Ramesh, M.R.The current study deals with the erosion behaviour of a plasma-sprayed 70% NiCrAlY + 30% TiO2 coating on MDN 420 steel substrate at extreme temperatures. The coating was characterized by using an optical microscope, Scanning Electron Microscopy and X-ray diffraction methods. The coating's porosity, microhardness, surface roughness, and adhesion strength were all examined. The solid particle erosion experiments were carried out at temperatures of 300 °C, 500 °C, and 700 °C, with impact angles of 30° and 90°. The tests were conducted by using the alumina as an erodent in the hot air jet erosion testing machine. The erosion volume loss of coated and uncoated samples was measured using an optical profilometer. It is observed that erosion resistance of the coating was found to be more when compared to the substrate for the different test temperatures chosen. As the temperature increases, the erosion resistance of the coating also found increased from 300 °C to 700 °C at both impact angles of 30° and 90°. The morphology of the eroded coating surface reveals that the generalized behaviour of the coating is ductile in nature. © 2022 IOP Publishing Ltd.Item Investigation of thermally sprayed NiCrAlY/TiO2and NiCrAlY/Cr2O3/YSZ cermet composite coatings on titanium alloys(Institute of Physics, 2022) Madhu Sudana Reddy, G.; Prasad, C.D.; Patil, P.; Shetty, G.; Ramesh, M.R.; Nageswara Rao, T.The present work investigates the hot corrosion behavior of thermally sprayed 65 pct NiCrAlY + 35 pct TiO2 and 65 pct NiCrAlY + 30 pct Cr2O3 + 5 pct YSZ coatings on titanium 15 alloys. The coatings on the titanium 15 alloy substrates exhibit a near-uniform, dense, and adherent microstructure with a porosity of 2.7 to 2.9%. Thermogravimetric studies are made to examine the hot corrosion performance of coatings in a molten salt environment of Na2SO4 + 60%V2O5 at the temperature of 700 °C for 50 cycles. One cycle is carried out by heating for a period of one hour and cooling the sample at ambient conditions. The corrosion products are analyzed based on scanning electron microscopy, energy dispersive analysis, and X-ray diffraction techniques to study the morphology, phase composition, and abundance of the high-temperature corrosion constituents. The bare titanium-15 alloy, 65 pct NiCrAlY + 35 pct TiO2 coating and 65 pct NiCrAlY + 35 pct Cr2O3 + 5 pct YSZ coating produced a weight gain of 307.92 mg cm-2, 42.16 mg cm-2 and 44.02 mg cm-2 respectively after the period of 50 cycles. The effective resistance of the coatings is due to the formation of Ni3V2O8, NiCr2O4, Cr2O3 & AlV2O4 phases. © 2022 IOP Publishing Ltd.Item High-Temperature Tribological Studies on Hot-Forged Al6061–TiB2 In Situ Composites(Springer Science and Business Media Deutschland GmbH, 2022) Venkategowda, C.; Hanumanthappa, H.; Prasad, C.D.; Shanmugam, B.K.; Sreenivasa, T.N.; Kumar, M.S.R.The present investigation deals with the tribological behavior of high-temperature hot-forged Al6061–TiB2 in situ composites. Three samples of Al6061–TiB2 in situ composites were prepared with the variation in the in situ TiB2 particles. An in situ technique forms TiB2 particles by facilitating a reaction between Al–3%B and Al–10%Ti parent metals in the Al6061 melt at 800 °C. Further, approximately 5 wt% and 10 wt% TiB2 particles were created in the Al6061 composite using suitable quantities of parent alloys. At 500 °C, the Al6061 and its in situ composites were subjected to hot forging, and about 50% reduction is employed. The scanning electron microscope (SEM) and optical microscopy analysis were conducted to check the TiB2 particle dispersion and worn surfaces in the in situ composites. The TiB2 particle dispersion is found to be fairly uniform throughout the Al6061 matrix with minimal clustering. The results indicate that the friction coefficient increases initially when the temperature increases and then declines due to the oxides in the debris released from the top surfaces of the samples. The results show that the increase in the TiB2 content in the Al6061–TiB2 composites increases the composite wear rate. © 2022, The Author(s), under exclusive licence to Springer Nature Switzerland AG.Item Effect of Mo- and SiC-Reinforced NiCr Microwave Cladding on Microstructure, Mechanical and Wear Properties(Springer, 2023) Sharanabasava, H.; Prasad, C.D.; Ramesh, M.R.A microwave hybrid heating technique was applied to produce the NiCr-Mo-SiC composite cladding on Titan-31. The developed claddings were tested for microstructural features, phase analysis, microhardness, and surface roughness parameters using scanning electron microscopy (SEM), X-ray diffraction (XRD), Vickers Microhardness, and 3D optical profilometers, respectively. Using a static alumina indenter on microwave clads, the linear reciprocator ball on plate wear test was performed. Both friction and wear track metrics have been studied. A dense microstructure without observable holes or fractures has been achieved, together with a homogeneous distribution of hard phases and strong metallurgical bonding. Cladding is typically three times tougher than the underlying metal. Due to the formation of hard carbide phases, which increased hardness and internal lubricity, cladding has a lower coefficient of friction than the substrate. © 2023, The Institution of Engineers (India).Item Characterization and Wear Behavior of NiCrMoSiC Microwave Cladding(Springer, 2024) Sharanabasava, H.; Prasad, C.D.; Ramesh, M.R.A microwave hybrid heating technique has been employed to develop NiCr-Mo-SiC composite cladding on titanium alloy (Grade-5/Ti-6Al-4 V/Titan-31). The developed claddings have been characterized for microstructural features, phase analysis, microhardness measurements, and 3D optical profile parameters by employing scanning electron microscopy, x-ray diffraction, Vickers microhardness tester, and 3D optical profilometer, respectively. Microwave clads have been subjected to linear reciprocator ball on plate wear test with static alumina indenter. Wear track parameters and friction coefficients have been studied. A dense microstructure with uniform distribution of hard phases and good metallurgical bonding with no visible pores and cracks has been obtained. Cladding exhibits nearly 2 times higher hardness than the base alloy. Coefficient of friction studies revealed that higher molybdenum content enhances internal lubricity. © 2023, ASM International.