Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item Comparative investigation of HVOF and flame sprayed CoMoCrSi coating(American Institute of Physics Inc. subs@aip.org, 2020) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.Present studies deals with comparison of high velocity oxy fuel and flame spray coating process by developing CoMoCrSi (Tribaloy T400) coating on a titanium grade-15 substrate. Prior to coating, feedstock is processed to obtain higher fraction intermetallics through high energy ball milling technique under controlled atmosphere. Processed feedstock material is sprayed on a Ti-15 substrate through HVOF and Flame spray process. The coated specimens are subjected to metallurgical and mechanical characterization using optical microscope, scanning electron microscope, energy dispersive spectroscopy, x-ray diffraction, Vickers mico hardness tester and bond strength using pull off test method. HVOF sprayed coating exhibits superior properties compared to Flame sprayed coating in terms of surface roughness, porosity, micro hardness and adhesion strength. The detailed studies of two coating systems is discussed. © 2020 Author(s).Item Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating(Institute of Physics Publishing helen.craven@iop.org, 2018) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi superalloy powder (Tribaloy-T400) consists of intermetallic laves phase and primary eutectic phase of Co-rich solid solution. Processing of Tribaloy-T400 powder is carried out through high-energy ball milling (HEBM) technique to obtain a higher volume fraction of intermetallic laves phases. The feedstock is sprayed using high-velocity-oxy-fuel (HVOF) process on titanium grade-15 substrate. The coating microstructure is homogenized by microwave hybrid heating technique. Characterization of feedstock, as-sprayed and microwave fused coatings is done by using Scanning Electron Microscopy (SEM), Energy dispersive spectroscopy (EDS) and x-ray Diffraction (XRD). Porosity, surface roughness, microhardness, and bond strength are measured. Adhesive wear behavior of the coatings under the dry sliding condition is evaluated at an applied load of l0 and 20 N and temperature of 200, 400 and 600 °C Fused coating exhibit higher wear resistance than the as-sprayed coatings and substrate. The hard intermetallic laves phases which are amorphous (bulk metallic glass) in nature strengthen the coating at high temperatures. © 2018 IOP Publishing Ltd.Item Effect of microwave heating on microstructure and elevated temperature adhesive wear behavior of HVOF deposited CoMoCrSi-Cr3C2 coating(Elsevier B.V., 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.This research reports the improvement of high-temperature sliding wear resistance of a grade 15 titanium alloy protected by an HVOF sprayed CoMoCrSi-Cr3C2 coating. The coatings have been tested in as-sprayed condition and after a post-deposition microwave heating step. The powder feedstock has been manufactured by high energy ball milling. X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM) equipped with the Energy Dispersive Spectroscopy (EDS) methods were used for coatings characterization. Surface roughness, microhardness, adhesion strength, and porosity of coatings were also measured. The wear test was conducted at an applied load of l0 N and 20 N with varying temperatures of 200 °C, 400 °C, and 600 °C under dry sliding conditions. Co3Mo2Si, Co7Mo6, Mo3Si, Co3Mo, and Co2Mo3 were the intermetallic laves phases generated in the CoMoCrSi feedstock during HEBM process. The microwave-fused coating exhibited metallurgical bonding, homogeneous structure, less porosity, and greater hardness as compared to as-sprayed coating. Microwave-treated coating revealed better wear property than an as-sprayed coating. This was mainly due to the intermetallic formation and metallurgical bonding in coatings. The fused coatings exhibit tribo-oxide layers during sliding action which was the main phenomenon of improving the wear resistance of the fused composite coatings. © 2019 Elsevier B.V.Item Comparison of Microstructural and Sliding Wear Resistance of HVOF Coated and Microwave Treated CoMoCrSi-WC + CrC + Ni and CoMoCrSi-WC + 12Co Composite Coatings Deposited on Titanium Substrate(Springer Science and Business Media B.V. editorial@springerplus.com, 2020) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi-WC + CrC + Ni and CoMoCrSi-WC + 12Co composite coatings are coated on titanium substrate by high velocity oxygen fuel method (HVOF). Prior to spraying, CoMoCrSi feedstock are processed through high energy ball milling (HEBM) in order improve the intermetallic laves phases and to reduce its particle size. The processed feedstock exhibits amorphous nature by improving laves phases and particle size of 60.12 ?m. Microwave heating energy is utilized as post heat treatment technique to improve the mechanical and metallurgical properties of as-sprayed coatings. Fused coatings reveals better properties in terms of surface roughness, porosity, microhardness and adhesion strength compared to as-sprayed coatings. Metallurgical bonding is observed in case of fused coatings due to diffusion of substrate elements. Frictional and wear behaviors have been investigated by a pin on disc apparatus at temperatures of 200 °C, 400 °C, and 600 °C under normal loads of 10 N and 20 N. Both wear trace and friction coefficients of the fused coatings are smaller than as-sprayed coatings and substrate at all test temperatures. The wear traces of fused coatings decreased with increasing the surface temperature due to the lubricant effect of cobalt oxides formed on the sliding surface. As a result, cobalt based cermet coatings are highly recommended as a durability improvement coating for the protection of sliding surface, such as high speed spindle. © 2020, Springer Nature B.V.