Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item Review of microstructure evolution in hypereutectic Al-Si alloys and its effect on wear properties(2014) Vijayan, V.; Prabhu, K.Al-Si alloys with silicon content more than 13 % are termed as hypereutectic alloys. In recent years, these alloys have drawn the attention of researchers due to their ability to replace cast iron parts in the transportation industry. The properties of the hypereutectic alloy are greatly dependent on the morphology, size and distribution of primary silicon crystals in the alloy. Mechanical properties of the hypereutectic Al-Si alloy can be improved by the simultaneous refinement and modification of the primary and eutectic silicon and by controlling the solidification parameters. In this paper, the effect of solidification rate and melt treatment on the evolution of microstructure in hypereutectic Al-Si alloys are reviewed. Different types of primary silicon morphology and the conditions for its nucleation and growth are explained. The paper discusses the effect of refinement/modification treatments on the microstructure and properties of the hypereutectic Al-Si alloy. The importance and effect of processing variables and phosphorus refinement on the silicon morphology and wear properties of the alloy is highlighted. © 2013 Indian Institute of Metals.Item The effect of the addition of strontium and cerium modifiers on microstructure and mechanical properties of hypereutectic Al-Si (LM30) alloy(ASTM International, 2013) Vijayan, V.; Ravi, M.; Prabhu, K.The present work deals with the melt treatment of LM30 hypereutectic Al-Si alloy using cerium and strontium and the assessment of its effect on microstructure and properties of the alloy. The addition of cerium simultaneously modified both primary and eutectic silicon, leading to an increase in ultimate tensile strength, as well as the wear resistance of the alloy. It was found that the coefficient of thermal expansion of the alloy decreased on modification of the microstructure. © 2013 by ASTM International.Item Effect of chilling and cerium addition on microstructure and cooling curve parameters of Al-14%Si alloy(Maney Publishing maney@maney.co.uk, 2015) Vijayan, V.; Prabhu, K.Al-14%Si alloys, with and without cerium, were cast at varying cooling rates by solidifying them in a crucible and against chills. The effect of melt treatment and chilling on microstructure and cooling curve parameters of the alloy was assessed. Ce treated alloys solidified in clay graphite crucible at a slow cooling rate showed refinement of primary silicon and the formation of Al-Si-Ce ternary intermetallic compound. The addition of Ce to the alloy solidified against chills resulted in simultaneous refinement and modification of primary and eutectic silicon. Nucleation temperatures of both primary and eutectic silicon decreased on addition of cerium. The formation of the intermetallic compound decreased with increase in cooling rate, leading to the modification of the eutectic silicon. The increase in the degree of modification of the eutectic Si was associated with the decrease in the volume fraction of the intermetallic compound formed. © 2015 Canadian Institute of Mining, Metallurgy and Petroleum Published by Maney on behalf of the Institute.Item The Effect of Chilling and Ce Addition on the Microstructure and Mechanical Properties of Al-23Si Alloy(Springer New York LLC barbara.b.bertram@gsk.com, 2017) Vijayan, V.; Prabhu, K.The present work involves the study of the effect of varying concentration of Ce addition on microstructure and mechanical properties of Al-23%Si alloys. Melt-treated alloys were solidified in copper, brass, stainless steel molds to assess the effect of cooling rate. The effect on microstructure was assessed by measuring the fineness of primary silicon and eutectic silicon particle characteristics. The Ce melt treatment transformed the coarse and irregular primary silicon into refined polyhedral silicon crystals, and the effect was more significant at higher cooling rates. Although the melt treatment had refined the eutectic silicon at lower cooling rates, it did not show any considerable effect on the eutectic silicon at higher cooling rates. The mechanical properties of the alloy increased significantly with increase in cooling rates and cerium concentration. Analysis of the results and literature reveals that the refined primary silicon was formed as a result of an invariant reaction between Ce compounds and primary silicon at higher temperatures. © 2016, ASM International.