Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item Elevated Temperature Solid Particle Erosion Performance of Plasma-Sprayed Co-based Composite Coatings with Additions of Al2O3 and CeO2(Springer New York LLC barbara.b.bertram@gsk.com, 2017) Nithin, H.S.; Desai, V.; Ramesh, M.R.In this paper, investigation into solid particle erosion behavior of atmospheric plasma-sprayed composite coating of CoCrAlY reinforced with Al2O3 and CeO2 oxides on Superni 76 at elevated temperature of 600 °C is presented. Alumina particles are used as erodent at two impact angles of 30° and 90°. The microstructure, porosity, hardness, toughness and adhesion properties of the as-sprayed coatings are studied. The effects of temperature and phase transformation in the coatings during erosion process are analyzed using XRD and EDS techniques. Optical profilometer is used for accurate elucidation of erosion volume loss. CoCrAlY/CeO2 coating showed better erosion resistance with a volume loss of about 50% of what was observed in case of CoCrAlY/Al2O3/YSZ coating. Lower erosion loss is observed at 90° as compared to 30° impact angle. The erosion mechanism evaluated using SEM micrograph revealed that the coatings experienced ductile fracture exhibiting severe deformation with unusual oxide cracks. Reinforced metal oxides provide shielding effect for erodent impact, enabling better erosion resistance. The oxidation of the coating due to high-temperature exposure reforms erosion process into oxidation-modified erosion process. © 2017, ASM International.Item Elevated temperature solid particle erosion behaviour of carbide reinforced CoCrAlY composite coatings(Institute of Physics Publishing helen.craven@iop.org, 2018) Nithin, H.S.; Desai, V.; Ramesh, M.R.CoCrAlY+WC-Co and CoCrAlY+Cr3C2-NiCr coatings are deposited on nickel based alloy using atmospheric plasma spray technique. Mechanical properties such as microhardness, adhesion strength and fracture toughness of coatings are evaluated. Elevated temperature solid particle erosion behaviour of these coatings are investigated at 600 °C using alumina erodent at 30 and 90° impact angle. Coatings are characterized utilizing Scanning electron microscope (SEM), x-ray diffraction (XRD) and Energy dispersive spectroscopy (EDS). CoCrAlY+WC-Co coating shows higher hardness, adhesion strength and fracture toughness than CoCrAlY+Cr3C2-NiCr coating. CoCrAlY+WC-Co coating exhibited approximately 3 times higher erosion resistance than CoCrAlY+Cr3C2-NiCr coating at 90° and 30° impact angles. SEM images of eroded surfaces of coatings reveals the combination of ductile and brittle fracture. CoCrAlY+Cr3C2-NiCr coating shows severe cracks, craters, carbide pull out and chipping than CoCrAlY+WC-Co coating. High temperature erosion is a combination of simultaneous building up of material by oxidation and removal of material by erosion process. Thus reforming the erosion process to oxidation modified erosion process. © 2018 IOP Publishing Ltd.Item Cyclic Oxidation and Hot Corrosion Behavior of Plasma-Sprayed CoCrAlY + WC-Co Coating on Turbine Alloys(Springer New York LLC barbara.b.bertram@gsk.com, 2018) Nithin, H.S.; Vijay, D.; Ramesh, M.R.Components in energy-producing systems suffer a variety of degradation processes such as oxidation and molten salt-induced corrosion as a consequence of complex multi-component gaseous environment. Coatings provide a composition that will grow the protective scale at high temperatures having long-term stability. Plasma spraying was used to deposit CoCrAlY + WC-Co composite coatings on turbine alloys of Hastelloy X and AISI 321. The thermocyclic oxidation behavior of coated alloys was investigated in static air and in molten salt (Na2SO4-60%V2O5) environment at 700 °C. The thermogravimetric technique was used to approximate the kinetics of oxidation in 50 cycles, each cycle consisting of heating and cooling. X-ray diffraction and SEM/EDAX techniques are used to characterize the oxide scale formed. Coated alloys showed a lower corrosion rate as compared to uncoated alloys. The coatings subjected to oxidation and hot corrosion showed slow scale growth kinetics. Preferential oxidation of Co, Cr, W and its spinel blocks the transport of oxygen and corrosive species into the coating by providing a barrier, thereby making the oxidation rate to reach steady state. As compared to the substrate alloys, coatings show better hot corrosion resistance. © 2018, ASM International.Item Hot Corrosion Behaviour of Refractory and Rare Earth Oxide Reinforced CoCrAlY APS Coatings at 700 °C(Springer, 2018) Nithin, H.S.; Desai, V.; Ramesh, M.R.This paper investigates cyclic hot corrosion of plasma sprayed CoCrAlY + Al2O3 + YSZ (C1) and CoCrAlY + CeO2 (C2) composite coatings on MDN 321 and Superni 76 substrates in molten salt (Na2SO4-60%V2O5) environment exposed to 700 °C. Weight change technique is used to evaluate the corrosion performance. Both C1 and C2 coatings showed better corrosion resistance than uncoated alloy. Both the coatings showed linear weight gain during the initial cycles and parabolic weight gain nature with subsequent hot corrosion cycles. The parabolic rate constant (Kp) of C1 and C2 coating was observed to be in the range 0.29–0.32 × 10?10 g2 cm?4 s?1 and 1.0–1.13 × 10?10 g2 cm?4 s?1 respectively. In C1 coating, the globular and continuously packed structure on the corroded surface having CoO, Cr2O3, CoCr2O4 and CoAl2O4 spinel oxides provided superior hot corrosion resistance. While in case of C2 coating, the outward growth of CeVO4 irregular crystals as a corrosion product of CeO2 and V2O5 salt deteriorated the oxide scales resulting in higher corrosion rate. © 2018, The Indian Institute of Metals - IIM.