Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
2 results
Search Results
Item Soot Oxidation Activity of Redox and Non-Redox Metal Oxides Synthesised by EDTA–Citrate Method(Springer New York LLC barbara.b.bertram@gsk.com, 2017) Anjana, A.P.; Prasad Dasari, H.P.; Lee, J.-H.; Harshini, H.; Babu, G.U.B.Abstract: In the present study, redox (CeO2, SnO2, Pr6O11 and Mn3O4) and non-redox (Gd2O3, La2O3 ZrO2 and HfO2) metal oxides were successfully synthesised using the EDTA–citrate complexing method and tested for soot oxidation activity. The characterization of the metal oxides is carried out using FTIR, XRD, BET surface area, pore volume analyser, SEM and TEM. The redox nature and metal–oxygen bond information of the metal oxides are obtained from XPS analysis. In redox metal oxides, three critical parameters [lattice oxygen binding energy, reduction temperature and ?r (ionic size difference of the corresponding metal oxide oxidation states)] govern the soot oxidation activity. Among the redox metal oxide samples, Mn3O4 and Pr6O11 samples showed lower binding energy for oxygen (O?—529.4, 528.9 eV respectively), lower reduction temperature (T?—317 and 512 °C respectively) and have smaller ?r value (9 pm and 17 pm respectively). Thus, displayed a better soot oxidation activity (T50 = 484 and 482 °C respectively) than compared to other redox metal oxides. Among the non-redox metal oxides, HfO2 sample displayed higher BET surface area (21.06 m2/g), lattice strain (0.0157), smaller ionic radius (58.2 pm) and higher relative surface oxygen ratio (58%) and thus resulted in a significantly better soot oxidation activity (T50 = 483 °C) than compared to other non-redox metal oxides. Graphical Abstract: [Figure not available: see fulltext.]. © 2017, Springer Science+Business Media, LLC.Item Praseodymium doped ceria as electrolyte material for IT-SOFC applications(Elsevier Ltd, 2018) Shajahan, I.; Ahn, J.; Nair, P.; Medisetti, S.; Patil, S.; Niveditha, V.; Uday Bhaskar Babu, G.; Prasad Dasari, H.P.; Lee, J.-H.Praseodymium-doped ceria (PDC, Ce0.9Pr0.1O2) electrolyte material for intermediate temperature solid oxide fuel cells (IT-SOFCs) has been successfully synthesised by EDTA-citrate method. From X-Ray diffraction (XRD), fluorite structure along with a crystallite size of 5.4 nm is obtained for PDC nanopowder calcined at 350 °C/24 h. Raman spectroscopy confirmed the structure, presence of oxygen vacancies with the manifestation of the main peak at 457 cm?1 and with a secondary peak at 550 cm?1. From Transmission Electron Microscopy (TEM) analysis, the average particle size is around 7–10 nm and selected area electron diffraction (SAED) patterns further confirmed the fluorite structure of PDC nanopowder. The PDC nanopowder displayed a BET surface area of 65 m2/g with a primary particle size of ?13 nm (calculated from BET surface area). Dilatometer studies revealed a multi-step shrinkage behaviour with the multiple peaks at 522, 1171 and 1461 °C which may be originated due to the presence of multiple size hard agglomerates. The PDC electrolyte pellet sintered at 1500 °C displayed an ionic conductivity of 1.213E-03 S cm?1 along with an activation energy of 1.28eV. Instead of a single fluorite structure, XRD of sintered PDC pellet showed multiple structures (Fluorite structure (CeO2) and cubic structure (PrO2). © 2018 Elsevier B.V.