HVOF sprayed Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings: Microstructure, microhardness and oxidation behaviour
(Elsevier Ltd, 2018) Reddy, N.C.; Kumar, B.S.A.; Reddappa, H.N.; Ramesh, M.R.; Koppad, P.G.; Kord, S.
This paper reports the development of Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings on AISI 420 stainless steel (MDN-420) and titanium alloy ASTM B265 (Ti-15) by HVOF technique. Microstructure, microhardness and high temperature oxidation behaviour of coatings were investigated. Microstructure of coatings was dense and displayed layers depicting lamellar structure. The microhardness of coatings was significantly higher than that of substrate owing to higher density and cohesive strength between individual splats of coating materials. Cyclic oxidation studies conducted on Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings showed oxide scale was composed of various oxides like NiO, NiCr2O4 and Cr2O3 phases. The formation of compact and protective NiO phase in case of Ni3Ti coatings; NiO and Cr2O3 phases in Ni3Ti+(Cr3C2+20NiCr) coatings stabilised the weight gain exhibited slow oxidation rate at higher temperatures. © 2017 Elsevier B.V.
Microstructure, mechanical and wear properties of the A357 composites reinforced with dual sized SiC particles
(Elsevier Ltd, 2019) Avinash, A.; Bontha, S.; Krishna, M.; Koppad, P.G.; Ramprabhu, T.
Current work reports on the development of A357 alloy composite which is reinforced with dual size SiC particles by stir casting route. Influence of different weight fractions (3% coarse+ 3% fine, 4% coarse + 2% fine, and 2% coarse + 4% fine) of dual size SiC particles on mechanical properties and wear resistance of A357 composites is the focus of this work. Hardness and tensile properties were studied for dual size composites and then were compared with A357 alloy. Microstructural study, fractured surface and worn surface investigation were carried out using optical and scanning electron microscopes respectively. Microstructural analysis showed fairly uniform dispersion of dual size SiC particles in A357 matrix with good interfacial bonding. Compared to A357 alloy, the composites showed improvement in hardness, yield, and tensile strength. In particular, composite with 4 wt. % of fine and 2 wt. % of large SiC particles displayed the highest tensile strength while composite with 4 wt. % of large and 2 wt. % of fine SiC particles exhibited high hardness and wear resistance among A357 alloy and dual particle size composites. The strengthening mechanisms that contributed to improvement in strength values were effective load transfer and dislocation strengthening due to thermal mismatch. © 2019 Elsevier B.V.
The effect of heat treatment on the mechanical and tribological properties of dual size SiC reinforced A357 matrix composites
(Elsevier Editora Ltda, 2020) Avinash, A.; Prabhu, T.R.; Babu, U.S.; Koppad, P.G.; Gupta, M.; Krishna, M.; Bontha, S.
In the present work, the effect of aging temperature and particle size ratio of SiC particles on the mechanical and tribological properties of A357 composites reinforced with dual particle size SiC were investigated. The composites were prepared by melt-stirring assisted permanent mold casting technique with different weight fractions (3% coarse +3% fine, 4% coarse +2% fine, and 2% coarse +4% fine) of large and small size SiC particles. These three prepared composites are referred as DPS1, DPS2 and DPS3 composites. The solutionizing temperature was maintained constant at 540 ?C for 9 h while the aging was done at 160 ?C, 180 ?C and 200 ?C (T6 treatment) for 6 h. Optical and scanning electron microscopy studies showed fairly uniform dispersion of dual size SiC particles in A357 matrix with good interfacial bonding. High-resolution transmission electron microscopy images showed formation of uniformly dispersed needle-like phase and spherical shaped -Mg2Si precipitates under peak aging conditions. Compared to T6 treated A357 alloy, the T6 treated DPS A357 composites showed improved yield strength, tensile strength, hardness and wear resistance. Among the three composites, hardness and wear resistance of T6 treated DPS2 composite was found to be significantly higher when compared to the other two composites (DPS1 and DPS3). Ratio of large particles to small particles also seems to effect the mechanical and tribological properties. Presence of more small particles was found to be good for strength and ductility whereas more large particles were found to be good for hardness and wear resistance. © 2020 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license
Al/Graphene/CNT Hybrid Composites: Hardness and Sliding Wear Studies
(Belgrade University, 2021) Manjunath Naik, H.R.; Manjunatha, L.H.; Koti, V.; Avinash, A.; Koppad, P.G.; P, S.K.
Graphene and carbon nanotubes are two carbon based materials known for their unique wear and friction properties. It would be quite interesting to understand the wear behavior of aluminium hybrid composites when these two nanosize reinforcements are incorporated into it. The hybrid composites with varying weight fractions of graphene (1, 2, 3 and 5 wt.%) and fixed CNT content of 2 wt.% were produced using powder metallurgy technique. The effect of varying graphene content on hardness and sliding wear of hybrid composites was studied. The wear tests were done as per ASTM G-99 standard with fixed sliding velocity (2 m/s) and sliding distance (1200 m) but varying applied load (10 - 30 N). Worn surface analysis was conducted using scanning electron microscope to arrive at wear mechanisms responsible for wear of aluminium and its hybrid composites. Increase in graphene content led to increase in bulk hardness with highest value of 61 RHN for hybrid composite with 3 wt.% graphene content. The wear rate of hybrid composites was found to be decreasing with enhancement in graphene content. Lower wear rate in hybrid composites was due to the formation of lubricating layer on the worn surface. © Faculty of Mechanical Engineering, Belgrade. All rights reserved