Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item HVOF sprayed Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings: Microstructure, microhardness and oxidation behaviour(Elsevier Ltd, 2018) Reddy, N.C.; Kumar, B.S.A.; Reddappa, H.N.; Ramesh, M.R.; Koppad, P.G.; Kord, S.This paper reports the development of Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings on AISI 420 stainless steel (MDN-420) and titanium alloy ASTM B265 (Ti-15) by HVOF technique. Microstructure, microhardness and high temperature oxidation behaviour of coatings were investigated. Microstructure of coatings was dense and displayed layers depicting lamellar structure. The microhardness of coatings was significantly higher than that of substrate owing to higher density and cohesive strength between individual splats of coating materials. Cyclic oxidation studies conducted on Ni3Ti and Ni3Ti+(Cr3C2+20NiCr) coatings showed oxide scale was composed of various oxides like NiO, NiCr2O4 and Cr2O3 phases. The formation of compact and protective NiO phase in case of Ni3Ti coatings; NiO and Cr2O3 phases in Ni3Ti+(Cr3C2+20NiCr) coatings stabilised the weight gain exhibited slow oxidation rate at higher temperatures. © 2017 Elsevier B.V.Item Microstructure and Adhesion Strength of Ni3Ti Coating Prepared by Mechanical Alloying and HVOF(Pleiades Publishing compmg@maik.ru, 2018) Reddy, N.C.; Ajay Kumar, B.S.; Ramesh, M.R.; Koppad, P.G.In the present work we report the development of Ni3Ti intermetallic compound by high energy ball milling of Ni and Ti powders. The ball milled powders were taken at various intervals (4, 6, 8, 10, and 11 h) to analyze the formation of NixTix intermetallic compounds. The ball milled powders were analyzed using scanning electron microscopy and X-ray diffraction. The layered shaped powder particles of Ni3Ti phase were formed after 11 h of ball milling, which was confirmed by X-ray peaks. Further High-Velocity Oxy-Fuel (HVOF) process was used to coat Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) on MDN 420 steel. Both the coated materials displayed excellent cohesion with minimal porosity less than 2%. The tensile adhesion strength test was carried out on these coatings to check the bond strength. Out of the two the Ni3Ti coating showed excellent bond strength of 41.04 MPa compared to that of Ni3Ti + (Cr3C2 + 20NiCr) coating. © 2018, Pleiades Publishing, Ltd.Item Hot corrosion behaviour of HVOF sprayed Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) coatings in presence of Na2SO4-40%V2O5 at 650 °c(IOP Publishing Ltd custserv@iop.org, 2019) Reddy, N.C.; Koppad, P.G.; Reddappa, H.N.; Ramesh, M.R.; Babu, E.R.; Varol, T.Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) coatings were deposited on gas turbine based ASTM B265 titanium (Ti-15) and AISI 420 stainless steel (MDN-420) substrate materials using HVOF technique. Thermocyclic hot corrosion tests were carried out at 650 °C in molten salt environment of Na2SO4-40%V2O5 for about 50 cycles. Thermogravimetric analysis was carried out to study the hot corrosion kinetics of uncoated and coated titanium and stainless steel substrates. The weight gain per unit area showed that the coated substrate materials displayed better resistance to hot corrosion when compared with that of uncoated substrate materials. The surface morphology of uncoated and coated substrate materials were analysed using scanning electron microscopy and elemental analysis. The formation of different types of oxides and compounds were analysed using x-ray diffraction. The uncoated substrates surface showed microspalling at several regions while coated substrates surface were composed of protective oxide layers. The presence of ternary NiCr2O4 protective oxides on the surface of Ni3Ti + (Cr3C2 + 20NiCr) coated substrates leads to reduction in the diffusion of corrosive species inside the coating. © 2019 IOP Publishing Ltd.Item Effect of carbon nanotubes on microhardness and adhesion strength of high-velocity oxy-fuel sprayed NiCr–Cr3C2 coatings(SAGE Publications Ltd, 2022) Manjunatha, M.; Gaikwad, G.; Natarajan, J.; Koppad, P.G.NiCr–Cr3C2 coatings are widely used for high temperature and tribological applications due to their high hardness, oxidation, and wear resistance properties. In the present investigation, an attempt is made to further enhance the hardness and adhesion strength of NiCr–Cr3C2 coatings by reinforcing them with multi-walled carbon nanotubes. The carbon nanotubes (3–7 wt%) with varying weight percentages were mixed with NiCr–Cr3C2 using a planetary ball rolling mill and sprayed on SA213 T12 (T12 alloy steel tube) using a high-velocity oxy-fuel spraying process. The microstructures of mixed powder, coating cross-section, and fractured coating surface were characterized using a scanning electron microscope while X-ray diffraction was used for phase identification in the fractured coating surface. The coated samples were subjected to microhardness and adhesion strength tests according to ASTM E384 and ASTM D4541-09 standards. Out of all coatings, NiCr–Cr3C2/7% carbon nanotube composite coating showed the lowest porosity of 1.17%, highest microhardness, and adhesion strength of 563.8 HV and 55.8 MPa, respectively. A fracture analysis after a pull-off adhesion test revealed adhesion failure for NiCr–Cr3C2 coating and combined adhesion/cohesion failure for NiCr–Cr3C2/7% carbon nanotube composite coating. © IMechE 2021.