Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
Search Results
Item Tribological behaviour of monolayer and multilayer Ti-based thin solid films deposited on alloy steel(Institute of Physics Publishing helen.craven@iop.org, 2019) V Badiger, P.V.; Desai, V.; Ramesh, M.R.; Joladarashi, S.; Gourkar, H.The fretting wear and adhesive wear resistance of Ti-based thin solid films deposited on MDN121 steel substrate are evaluated. Plasma-assisted cathodic arc evaporation technique is used to develop the TiC-C monolayer coating and Ti/TiN/TiCN/TiN/TiCN multilayer coatings used in the study. FESEM-EDS, nanoindentation, Raman spectroscopy, optical profiler, and confocal microscope are used to characterise the coatings and wear tracks. Diamond-like carbon is observed in the microstructure of both the coatings. During the fretting analysis, the coefficient of friction (COF) is reduced by 68.49% in the case of the TiC-C monolayer coating and 42.46% in the Ti multilayer coatings as compared to the substrate. The volumetric wear loss of the TiC-C monolayer coating is lower than the multilayer coating. The wear surface morphology reveals the abrasive form of the fretting wear mechanism in both the monolayer and multilayer coatings whereas the galling failure in the substrate. During adhesive wear, the COF is reduced by 71.73% in the monolayer coating and 59.33% in the multilayer coatings compared to the substrate. The monolayer coating exhibits low friction and low wear rate as compared to the multilayer coating. © 2018 IOP Publishing Ltd.Item Development and Sliding Wear Behavior of Co-Mo-Cr-Si Cladding through Microwave Heating(Springer editorial@springerplus.com, 2019) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.The aim of the present study is to improve the sliding wear resistance of pure titanium grade-2 substrate by developing CoMoCrSi (Tribaloy T400) cladding on it by using microwave hybrid heating technique. The developed cladding is characterized by microstructural features, phase analysis, measurement of microhardness by employing a scanning electron microscope (SEM), X-ray diffraction (XRD) and Vickers microhardness. The cladding and substrate are subjected to sliding wear test against alumina counterpart at elevated temperatures under dry conditions using a pin on disc tribometer. The test is performed by varying normal load and temperatures, whereas sliding speed is maintained constant. The developed clad shown partial melting of CoMoCrSi powders and obtained sound metallurgical bonding with the substrate. The high specific energy of microwave diluted the substrate atoms into cladding region which forms Cr3C2, Co3Ti, and TiC, phases confirmed by phase analysis. The cladding obtained better porosity and microhardness are 1.5 ± 0.2% ?m and 760 ± 35 Hv respectively. The substrate exhibits low microhardness of 182 ± 25 Hv. The cladding exhibits 6 times of lower volume loss and 70.14% of less wear rate with respect to the substrate. The cladding experienced least coefficient of friction is 0.55 compared with the substrate. The worn surfaces of cladding and substrate are examined. The detailed mechanism of wear is discussed in this paper. © 2019, Springer Nature B.V.