Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
3 results
Search Results
Item Tribological Performance of Fe-Based Composite Coatings Under Elevated Temperature Conditions(Springer, 2025) Chandramouli, T.V.; Joladarashi, S.; Ramesh, M.R.The present study investigated the tribological performance of Fe-based coatings reinforced with carbides onto a maraging steel substrate using the HVOF spray technique. These materials are widely used in manufacturing various components in the aerospace and energy sectors. Commercially available SS316L and 17-4PH are reinforced with WC–Co feedstock powders to deposit these composite coatings on maraging steel substrate. The dry sliding wear tests were conducted using the ball-on-disc tribometer at varying temperatures (25 and 300 °C) with 10 N normal load using an alumina ball (Al2O3) as the counter body. The study includes micro-hardness, porosity, density, bond strength, and surface roughness of the coatings. The samples subjected to wear testing were analyzed using SEM/EDS and XRD techniques, and the wear scar volume was measured using a 3D profilometer to calculate the volume metric loss. The wear rate of SS316L30%WC–Co is 64.46% lower than that of 17-4PH30%WC–Co at room temperature and 67.33% lower at 300 °C under a load of 10 N. At room temperature, the worn surface exhibited abrasive wear, while at 300 °C, adhesive wear and oxidative wear were observed owing to the formation of protective layers. Therefore, SS316L-30%WC–Co demonstrates superior wear resistance compared to 17-4PH-30%WC–Co and offers enhanced mechanical strength, particularly in challenging environments. The deposition of these coatings effectively protects the maraging steel substrate. © The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd. 2025.Item Comparison of Microstructural and Sliding Wear Resistance of HVOF Coated and Microwave Treated CoMoCrSi-WC + CrC + Ni and CoMoCrSi-WC + 12Co Composite Coatings Deposited on Titanium Substrate(Springer Science and Business Media B.V. editorial@springerplus.com, 2020) Prasad, C.D.; Joladarashi, S.; Ramesh, M.R.; Srinath, M.S.; Channabasappa, B.H.CoMoCrSi-WC + CrC + Ni and CoMoCrSi-WC + 12Co composite coatings are coated on titanium substrate by high velocity oxygen fuel method (HVOF). Prior to spraying, CoMoCrSi feedstock are processed through high energy ball milling (HEBM) in order improve the intermetallic laves phases and to reduce its particle size. The processed feedstock exhibits amorphous nature by improving laves phases and particle size of 60.12 ?m. Microwave heating energy is utilized as post heat treatment technique to improve the mechanical and metallurgical properties of as-sprayed coatings. Fused coatings reveals better properties in terms of surface roughness, porosity, microhardness and adhesion strength compared to as-sprayed coatings. Metallurgical bonding is observed in case of fused coatings due to diffusion of substrate elements. Frictional and wear behaviors have been investigated by a pin on disc apparatus at temperatures of 200 °C, 400 °C, and 600 °C under normal loads of 10 N and 20 N. Both wear trace and friction coefficients of the fused coatings are smaller than as-sprayed coatings and substrate at all test temperatures. The wear traces of fused coatings decreased with increasing the surface temperature due to the lubricant effect of cobalt oxides formed on the sliding surface. As a result, cobalt based cermet coatings are highly recommended as a durability improvement coating for the protection of sliding surface, such as high speed spindle. © 2020, Springer Nature B.V.Item Surface enhancement of SS304 for high-temperature wear resistance using laser cladded Mo-alloyed stellite 6 coatings(Elsevier B.V., 2025) Aprameya, C.R.; Joladarashi, S.; Ramesh, M.R.Severe wear often limits the high-temperature durability of SS304 components, necessitating the development of surface-engineered solutions. In this investigation, Mo-reinforced Stellite 6 claddings were developed using Laser Directed Energy Deposition (L-DED) to provide enhanced surface protection. Claddings with (3, 6, and 9 wt%) Mo reinforcement enhanced hardness by 2.9, 3.1, and 3.3 times, respectively, compared to the SS304 substrate. This improvement is attributed to Mo-induced solid solution strengthening and the formation of hard intermetallic phases. Dry sliding wear tests were conducted at RT and 600 °C under (10 and 20 N) loads. Wear characterisation of the clads was performed using OM, XRD, FE-SEM, EDX, and Raman spectroscopy. At RT, claddings primarily exhibited abrasive wear with minor plastic deformation. However, at 600 °C, the wear mechanism evolved into a combination of severe adhesive, oxidative, abrasive, and plastic deformation modes, with oxidative wear governing the tribological behavior. Stellite 6 with 9 wt% Mo clads exhibited better tribological performance than the other two variants, owing to the development of oxide glaze layers of Cr2O3, NiO, CoO2, and Co3O4. Enhanced performance of the claddings is attributed to solid solution strengthening, Cr-rich carbide formation, increased dislocation density, and the L-DED technology enabling refined microstructure and strong metallurgical bonding. These findings highlight the potential for further advancements in Mo-reinforced Stellite 6 L-DED claddings for high-temperature wear applications. © 2025 Elsevier B.V.