Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
3 results
Search Results
Item Polysulfone/N-phthaloylchitosan novel composite membranes for salt rejection application(2011) Padaki, M.; Isloor, A.M.; Wanichapichart, P.N-phthaloylchitosan (CS) was synthesized by the reaction of chitosan with phthalic anhydride in dimethyl formamide. Different compositions of polysulfone (PSf) and N-phthaloylchitosan were used to prepare novel polysulfone/N-phthaloylchitosan (PSf/CS) composite membranes by phase inversion method. The composition ratios between the former and the latter were 80:20, 85:15, 90:10, and 95:5. Water flux results revealed that, PSf:CS 80:20 membrane is found to have greatest effective pore area while PSf:CS 95:05 membrane has the smallest value. The pore area is found to be larger with the increase in CS composition. In addition, its water swelling property increases with the increase of CS composition. Water flux results are in consistent with dielectric constant value. Use of known molecular weight of polyethylene glycol rejection study, revealed that, PSf:CS 95:05 membrane possessed the smallest pore size among these membranes. In conclusion, change of ratio between PSf and CS, considerably affects membrane pore size and hydrophilicity. For salt filtration, membrane PSf:CS 95:05 showed 93%, 76.11% and 70.12% rejection of MgSO4, Na2SO4, and NaCl, respectively. © 2011 Elsevier B.V.Item Synthesis, characterization and desalination study of novel PSAB and mPSAB blend membranes with Polysulfone (PSf)(2012) Padaki, M.; Isloor, A.M.; A.F., A.F.; Abdullah, M.S.The present paper describes the synthesis of poly sulphonyl amino benzamide (PSAB) and methyalated poly sulphonyl amino benzamide (mPSAB) polymer, using terephthalic acid chloride and substituted 4-amino-1-benzensulphonmide in N-methyl-. 2-pyrrolidone. Polymers were characterized by FT-IR, NMR and GPC. Polysulfone composite membranes were prepared using these novel poymers by DIPS (Diffusion Induced Phase Seperation) method. These composite membranes are useful for water purification with special emphasis on sea water desalination. Newly prepared membranes were studied for salt rejection, water flux, molecular weight cut off by PEG solution, effect of the pH on water swelling and salt rejection and flux decline was also studied. 30 to 70% of the salt rejection was observed in all membranes. Effect of the dilution on salt rejection was studied using different concentration of NaCl solution varying from 1000. ppm to 3500. ppm. All the membranes showed 80% rejection for PEG having 1000. Da molecular weight. Contact angle and water swelling was measured to determine hydrophilicity of the membrane. Water swelling and salt rejection in different pH was also studied. © 2012 Elsevier B.V.Item Integration of Zwitterionic Polymer Nanoparticles in Interfacial Polymerization for Ion Separation(American Chemical Society, 2020) Gnani Peer Mohamed, G.P.S.; Isloor, A.M.; Bavarian, M.; Nejati, S.A thin-film nanocomposite (TFN) membrane was developed by integrating zwitterionic polymeric nanoparticles into the active layer of the membranes. High surface area zwitterionic polymeric nanoparticles (370 m2/g) were developed through distillation-precipitation polymerization (DPP). Sodium 4-vinylbenzenesulfonate (SVBS) was used as the monomer and N,N?-methylenebis(acrylamide) (MBAAm) utilized as the cross-linking agent. l-cysteine (l-Cys) was tethered to these matrices through thiol-ene reaction. The as-synthesized zwitterionic P(MBAAm-co-SVBS)@l-Cys nanoparticles were dispersed into the organic solution of trimesoyl chloride (TMC) to be integrated into the polyamide (PA) selective layer of thin film nanofiltration membranes. The PA layer was synthesized by interfacial polymerization through the reaction of 2% (w/v) of piperazine (PIP) in the aqueous phase and 0.15% (w/v) of the TMC solution. The fabricated TFN membranes exhibited pure water permeability (Jw) of 11.4 L/m2h bar and salt rejection value of 97.6% and 16.9%, for sodium sulfate and sodium chloride, respectively. The fabricated membranes demonstrated metal ion removal efficiencies of 99.48% and 95.67% for Pb2+ and Cd2+ ions, respectively. © © 2020 American Chemical Society.