Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
2 results
Search Results
Item Isolation of microcrystalline cellulose from Musa paradisiaca (banana) plant leaves: physicochemical, thermal, morphological, and mechanical characterization for lightweight polymer composite applications(Springer Science and Business Media B.V., 2024) Indra Reddy, M.I.; Sethuramalingam, P.; Sahu, R.K.Natural cellulose owing to its remarkable microstructural and physiochemical behaviour, and its eco-friendliness have attracted significant interest among the researchers. Therefore, in this work, microcrystalline cellulose (MCC) is extracted from the Musa paradisiaca plant leaf (MPPL) debris which is accumulated in large quantity and treated as waste material. The purified micro-cellulose is obtained by subjecting the MPPL raw material to alkali treatment followed by acid hydrolysis, bleaching and slow pyrolysis. From the FT-IR spectra of the cleaned cellulose, it is observed that its amorphous phase is eliminated. The crystallinity index is found to be 87.42% and this value is attributed to the sodium chlorite bleaching. The particle size analyzer results show that the micro-cellulose found to have a bimodal distribution with an average size of 35.97 μm and standard deviation 16.53. It is evident from SEM that the microcrystalline cellulose is of semi-spherical in shape and found to be aggregated with uneven distribution. Further, TGA analysis is carried out in this work and the results show that the microcrystalline cellulose can exhibit high heat resistance up to 297 °C. Surface roughness values (Ra) for MPPL MCC is 58.41 μm. The properties are well suited for futuristic polymer composite applications such as filler addition in biofilm for packaging industries and coating material in pharma industries. © The Polymer Society, Taipei 2024.Item Comprehensive Characterization of Novel Jute Fabrics with Musa Paradisiaca Leaf Agro-Waste Based Micro Cellulosic Fillers Reinforced Epoxy Composites For Lightweight Applications(Korean Fiber Society, 2025) Indra Reddy, M.I.; Sethuramalingam, P.; Sahu, R.K.For lightweight, sustainable, high-strength products, hybrid bio-epoxy composites materials were the most excellent choice for the production industry. The investigation proceeds in developing a four-stacked sequence jute-woven mats reinforced with epoxy composite and added with micro-cellulose fillers. The extraction of micro cellulose from Musa paradisiaca plant leaf (MPPL) was carried out through a series of processes, including alkali treatment, acid hydrolysis, bleaching, and slow pyrolysis. The composite was fabricated using the conventional hand lay-up method and compression molding. The microcellulose was added to the stacked composite at varying weight percentages (0, 2.5, 5, 7.5, and 10%). Thermo-mechanical and water intake characterization were investigated using ASTM. The findings revealed that incorporating 5% MPPL cellulose into the jute-stacked layer sequence resulted in improved hardness (95 HRRW), tensile modulus (3407.69 MPa), tensile strength (79.74 MPa), flexural modulus (2195.752 MPa), flexural strength (56.87 MPa), and crystallinity index (72.7%). However, a reduction in impact strength (23.27 kJ/m2) was noted compared to the unfilled composite. The higher thermal degradation (480 °C) behavior of the filler-reinforced composite makes them a suitable material for applications in high-temperature environments. Fractographical morphology was also investigated to reveal the bonding behavior, voids formations, agglomeration of fillers, and fracture behavior. Thus, this distinguishable composite characterization will aid the manufacturing industries in producing high-strength biodegradable materials. © The Author(s), under exclusive licence to the Korean Fiber Society 2025.