Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
2 results
Search Results
Item Effect of current density during electrodeposition on microstructure and hardness of textured Cu coating in the application of antimicrobial Al touch surface(Elsevier Ltd, 2016) Augustin, A.; Huilgol, P.; Udupa, K.R.; Bhat, K.U.Copper is a well proven antimicrobial material which can be used in the form of a coating on the touch surfaces. Those coating can offer a good service as touch surface for very long time if only they possess good mechanical properties like scratch resistance and microhardness. In the present work the above mentioned mechanical properties were determined on the electrodeposited copper thin film; deposited on double zincated aluminium. During deposition, current density was varied from 2 A dm?2 to 10 A dm?2, to produce crystallite size in the range of 33.5 nm to 66 nm. The crystallite size was calculated from the X-ray peak broadening (Scherrer?s formula) which were later confirmed by TEM micrographs. The scratch hardness and microhardness of the coating were measured and correlated with the crystallite size in the copper coating. Both characteristic values were found to increase with the reduction in crystallite size. Reduced crystallite size (Hall–Petch effect) and preferred growth of copper films along (111) plane play a significant role on the increase in the hardness of the coating. Further, TEM analysis reveals the presence of nano-twins in the film deposited at higher current density, which contributed to a large extent to the sharp increase of coating hardness compared to the mechanism of Hall–Petch effect. The antimicrobial ability of the coated sample has been evaluated against Escherichia coli bacteria and which is compared with that of commercially available bulk copper using the colony count method. 94% of E. coli cells were died after six hours of exposure to the copper coated surface. The morphology of the copper treated cells was studied using SEM. © 2016 Elsevier LtdItem Formation of microstructural features in hot-dip aluminized AISI 321 stainless steel(University of Science and Technology Beijing, 2018) Huilgol, P.; Rajendra Udupa, K.; Udaya Bhat, K.Hot-dip aluminizing (HDA) is a proven surface coating technique for improving the oxidation and corrosion resistance of ferrous substrates. Although extensive studies on the HDA of plain carbon steels have been reported, studies on the HDA of stainless steels are limited. Because of the technological importance of stainless steels in high-temperature applications, studies of their microstructural development during HDA are needed. In the present investigation, the HDA of AISI 321 stainless steel was carried out in a pure Al bath. The microstructural features of the coating were studied using scanning electron microscopy and transmission electron microscopy. These studies revealed that the coating consists of two regions: an Al top coat and an aluminide layer at the interface between the steel and Al. The Al top coat was found to consist of intermetallic phases such as Al7Cr and Al3Fe dispersed in an Al matrix. Twinning was observed in both the Al7Cr and the Al3Fe phases. Furthermore, the aluminide layer comprised a mixture of nanocrystalline Fe2Al5, Al7Cr, and Al. Details of the microstructural features are presented, and their formation mechanisms are discussed. © 2018, University of Science and Technology Beijing and Springer-Verlag GmbH Germany, part of Springer Nature.