Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
3 results
Search Results
Item Synthesis, characterization & impedance studies of some new nano filtration membranes(Trans Tech Publications Ltd ttp@transtec.ch, 2010) Padaki, M.; Hegde, C.; Isloor, A.M.In the recent years membrane technology has gained significant attention from polymer chemists all around the world due to their attractive features such as efficiency, low costs, low energy costs and as effective solutions to longstanding problems in the chemical industries. Membrane technologies have been widely applied in the separation of liquids and even gases. Many separation problems can be solved economically by nanofiltration alone or in combination with other separation processes. This study aimed to synthesize polysulfone based nanofiltration membranes using DIPS (diffusion induced phase separation) technique. Newly synthesized polymer membranes were subjected to Infra red spectral and water uptake studies. Membranes were also characterized using electrochemical spectroscopy for their proton conducting property. Their surface morphology is visualized by SEM. © (2010) Trans Tech Publications.Item Synthesis and desalination performance of Ar+-N+ irradiated polysulfone based new NF membrane(2011) Hegde, C.; Isloor, A.M.; Padaki, M.; Wanichapichart, P.; Liangdeng, Y.In the last few years, membrane technology has gained more attention from polymer chemists throughout the globe. Nowadays, surface modification of membrane is very useful in biotechnology and food science. In the present investigation, we have synthesized polysulfone based composite nanofiltration (NF) membranes, and characterized these membranes by FT-IR, SEM and membrane performance studies. Surface plasma treatment was carried out by irradiation with argon and nitrogen beams in suitable conditions. It was observed that nitrogen beam caused surface roughness that was more severe than the Ar beam. After irradiation, water contact angle was slightly increased. For pure water permeability, flux increased linearly with the operating pressure. However, for the salt solution, the flux was decreased marginally and salt rejection increased after irradiation due to surface modification. The modification effect was characterized in terms of contact angle, AFM employed roughness measurement and dielectric property. It revealed that irradiated NF membranes showed higher salt rejection and lower flux as compared to the nonmodified membranes. Accordingly, the roughness of the membrane surface intensively affected the performance of RO membrane. © 2010 Elsevier B.V.Item New CPS-PPEES blend membranes for CaCl2 and NaCl rejection(Techno Press technop2@chollian.net, 2012) Hegde, C.; Isloor, A.M.; Padaki, M.; A.F., A.F.; Lau, L.W.Carboxylated polysulfone (CPS), poly (1,4-phenylene ether ethersulfone) (PPEES), membranes were prepared and used for the separation of NaCl and CaCl2 in efficient way with less energy consumption. In this work, nanofiltration and reverse osmosis membranes were employed to the salt rejection behavior of the different salt solutions. The influence of applied pressure (1-12 bar), on the membrane performance was assessed. In CM series of membranes, CM1 showed maximum of 97% water uptake and 36% water swelling, whereas, CM4 showed 75% water uptake and 28% water swelling. In RCM series, RCM1 showed 85% water uptake and 32% water swelling whereas, in RCM4 it was 68% for water uptake and 20% for water swelling. Conclusively reverse osmosis membranes gave better rejection whereas nanofiltration membrane showed enhanced flux. CM1 showed 58% of rejection with 12L/(m2h) flux and RCM1 showed 55% of rejection with 15L/(m2h) flux for 0.1wt.% NaCl solution. Whereas, in 0.1wt.% CaCl22 solution, membrane CM11 showed 78% of rejection with 12L/(m2h) flux and RCM1 showed 63% rejection with flux of 9L/(m2h).