Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
12 results
Search Results
Item Electrolytic preparation of cyclic multilayer Zn-Ni alloy coating using switching cathode current densities(2010) Venkatakrishna, K.; Hegde, A.C.Cyclic multilayer alloy (CMA) coating of Zn-Ni was developed on mild steel using single bath technique, by proper manipulation of cathode current densities. The thickness and composition of the individual layers were altered precisely and conveniently by cyclic modulation of cathode current densities. Multilayer coatings, having sharp change in compositions were developed using square current pulses. Gelatin and sulphanilic acid (SA) acid were used as additives. Laminar deposits with different configurations were produced, and their corrosion behaviors were studied, in 5% NaCl solution by electrochemical methods. It was observed that the corrosion resistance of CMA coating increased progressively with number of layers (up to certain optimal numbers) and then decreased. Cyclic voltammetry study demonstrated the role of gelatin and SA in multilayer coating. The coating configuration has been optimized for the peak performance against corrosion. The substantial decrease of corrosion rate, in the case of multilayer coatings was attributed to the changed intrinsic electric properties, evidenced by Electrochemical Impedance Spectroscopy (EIS) study. The surface morphology and its roughness were examined by Atomic Force Microscopy (AFM). The surface and cross-sectional view of coatings were examined, using Scanning Electron Microscopy (SEM). X-ray photoelectron spectrum (XPS) study was carried out for surface analysis. The relative performance of pure Zn, monolithic and CMA coatings were compared and discussed. © 2010 Springer Science+Business Media B.V.Item Electrodeposition of high performance multilayer coatings of Zn-Co using triangular current pulses(2010) Yogesha, S.; Hegde, A.C.Compositionally modulated alloy (CMA) coatings of Zn-Co were electrodeposited on to mild steel from an acid chloride bath containing thiamine hydrochloride, as an additive. Electroplating was carried out galvanostatically from a single bath containing Zn2+ and Co2+ ions. Gradual change in composition in each layer was effected by triangular current pulses, cycling between two cathode current densities. Compositionally modulated alloy coatings were developed under different conditions of cyclic cathode current density and number of layers, and their corrosion resistances were evaluated by potentiodynamic polarisation and electrochemical impedance spectroscopy. The formation of multilayer and corrosion mechanism was analysed using scanning electron microscopy. The corrosion resistances of CMA and monolithic alloy coatings were compared with that of the base metal. Compositionally modulated alloy coating at optimal configuration, represented as (Zn-Co) 2•0/4•0/300, was found to exhibit ?80 times better corrosion resistance compared with monolithic (Zn-Co)3•0 alloy, deposited for the same length of time from the same bath. Improved corrosion resistance was attributed to the formation of n-type semiconductor film at the interface, supported by Mott-Schottky plots. Decrease in corrosion resistance at high degree of layering was found, and is due to lower relaxation time for redistribution of solutes in the diffusion double layer, during plating. © 2010 Maney Publishing.Item Electroplating and characterization of Zn-Ni, Zn-Co and Zn-Ni-Co alloys(2010) Eliaz, N.; Venkatakrishna, K.; Hegde, A.C.Zn-Ni, Zn-Co and Zn-Ni-Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency was higher than 90%. As the current density was increased or the bath temperature was decreased, the concentration of the nobler metal in the coating increased. Both concentrations of Ni and Co in the ternary alloy increased as the applied current density was increased. Nickel and cobalt were found to have a synergistic catalytic effect. The thickness of all coatings increased as the applied current density was increased. The hardness increased with current density to a peak value, and then decreased. The rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, while the rates of Ni and Co deposition were not. The anomalous codeposition was explained by the great difference between the exchange current densities of Zn and the iron-group metal. Potentiodynamic polarization scans and electrochemical impedance spectroscopy showed that the corrosion resistance of the ternary Zn-Ni-Co alloy coatings was approximately 10 times higher than that of Zn-Ni and 7 times higher than that of Zn-Co. The improved corrosion resistance of the ternary alloy was attributed to its surface chemistry, phase content, texture, and surface morphology. The ternary Zn-Ni-Co coating may thus replace the conventional Zn-Ni and Zn-Co coatings in a variety of applications. © 2010 Elsevier B.V.Item Development of nano-structured cyclic multilayer Zn-Ni alloy coatings using triangular current pulses(2011) Bhat, R.S.; Hegde, A.C.Cyclic multilayer alloy (CMA) deposits of Zn-Ni were developed on mild steel from sulphate bath having thiamine hydrochloride (THC) and citric acid (CA) as additives. CMA coatings were developed galvanostatically using triangular current pulses, under different conditions of cyclic cathode current density (CCCD's) and number of layers. The corrosion behaviors of the coatings were evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy methods, and were compared with that of monolayer Zn-Ni alloy of same thickness. At optimal configuration, CMA coating represented as, (Zn-Ni)2.0/5.0/300 was found to exhibit ?40 times better corrosion resistance compared to monolayer alloy, (Zn-Ni)3.0. Cyclic voltammetry study demonstrated that THC and CA have improved the appearance of the deposit by complexation with metal ions. The corrosion protection efficacy of CMA coatings was attributed to the difference in phase structure of the alloy in successive layers, evidenced by XRD analysis. The formation of multilayer and corrosion mechanism was analyzed by Scanning Electron Microscopy (SEM) study. © 2011 Allerton Press, Inc.Item Optimization of deposition conditions for development of high corrosion resistant Zn-Fe multilayer coatings(2011) Yogesha, S.; Hegde, A.C.Composition modulated multilayer alloy (CMMA) coating of Zn-Fe was developed galvanostatically on mild steel through single bath technique (SBT), using thiamine hydrochloride as additive. Electrodeposits with different coating matrices were developed, using square current pulses. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) methods were used to assess the corrosion performance of the coatings. The cyclic cathode current densities (CCCDs) and number of layers were optimized, for highest corrosion resistance. Experimental results showed that CMMA Zn-Fe coating, developed at 2.0-4.0 A/dm2, having 300 layers is ?30 times higher corrosion resistant than corresponding monolithic alloy of same thickness. The corrosion resistance increased with number of layers up to a certain number of layers; and then decreased. The better corrosion resistance was attributed to the dielectric barrier at the interface, evidenced by dielectric spectroscopy. The formation of multilayer and corrosion mechanism was analyzed using scanning electron microscopy (SEM). © 2011 Elsevier B.V. All rights reserved.Item Development of multilayer Sn-Ni alloy coating by pulsed sonoelectrolysis for enhanced corrosion protection(Royal Society of Chemistry, 2016) Shetty, S.; Mohamed, M.J.; Bhat, D.; Hegde, A.C.Multilayer Sn-Ni alloy coating has been developed electrochemically on mild steel using an ultrasound effect, as a tool to modulate mass transfer process at electrical double layer, during deposition. Sn-Ni coatings having alternate layers of alloys of different compositions were developed on a nano/micrometric scale by pulsing sonicator ON (tON) and OFF (tOFF), periodically. The composition modulated multilayer alloy (CMMA) Sn-Ni coatings have been deposited by inducing the ultrasound field periodically at optimal current density. Corrosion performances of ultrasound-assisted multilayer Sn-Ni alloy coatings have been evaluated by electrochemical methods. Corrosion data revealed that CMMA Sn-Ni coating, developed using pulsed ultrasonic field and having 150 layers, represented as (Sn-Ni)2/2/150, is the most corrosion resistant, compared to its monolayer alloy coatings developed by both with/without ultrasound effect. Corrosion protection efficacy of multilayer coatings was found to be decreased at high degree of layering due to diffusion of layers. Improved corrosion resistance of multilayer Sn-Ni coatings is attributed to an increase in the number of layers, or interfaces separating alloys of the same metals, but of different composition, surface morphologies and phase structures, supported by energy dispersive spectroscopy, field emission scanning electron microscopy and X-ray diffraction study, respectively. The better corrosion protection of CMMA Sn-Ni coatings, compared to monolayer counterparts, is attributed to an increase in the number of layers, hence phase boundaries between layers, and experimental results are discussed. © 2018 The Royal Society of Chemistry.Item Electrodeposition of Sn-Ni Alloy Coatings for Water-Splitting Application from Alkaline Medium(Springer Boston, 2017) Shetty, S.; Hegde, A.C.In this work, Sn-Ni alloy coatings were developed onto the surface of copper from a newly formulated electrolytic bath by a simple and cost-effective electrodeposition technique using gelatin as an additive. The electrocatalytic behavior of coatings deposited at different current densities (c.d.’s) for water-splitting applications, in terms of hydrogen evolution reaction (HER) and oxygen evolution reaction (OER), has been researched. The experimental results showed that the electrocatalytic activity of Sn-Ni coatings has a close relationship with its composition, surface morphology, and phase structure depending on the c.d. used, supported by scanning electron microscopy (SEM-EDX) and X-ray diffraction (XRD) analyses. Cyclic voltammetry and chronopotentiometry techniques have demonstrated that Sn-Ni alloy deposited at 4.0 A dm?2 (having 37.6 wt pct Ni) and 1.0 A dm?2 (having 19.6 wt pct Ni) exhibit, respectively, the highest electrocatalytic behavior for HER and OER in 1.0-M KOH solution. Sn-Ni alloy coatings were found to be stable under working conditions of electrolysis, confirmed by electrochemical corrosion tests. High electrocatalytic activity of Sn-Ni alloy coatings for both HER and OER is specific to their composition, surface morphology, and active surface area. © 2016, The Minerals, Metals & Materials Society and ASM International.Item Electrochemical studies on the corrosion resistance of Zn–Ni–Co coating from acid chloride bath(Springer, 2020) Bhat, R.S.; Manjunatha, K.B.; Prasanna Shankara, R.; Venkatakrishna, K.; Hegde, A.C.Anticorrosive deposits are a valuable approach to defending against corrosion from mild steel structures/machinery equipment. The Zn–Ni–Co coating has been deposited on low carbon steel surfaces using environment friendly optimized acidic chloride bath with ZnCl2·6H2O, NiCl2·6H2O, CoCl2·6H2O, sulphanilic acid (C6H7NO3S) and gelatin (C6H8O6). The standard Hull cell technique has been adopted for the optimization of bath components and experimental conditions, for the superior corrosion resistant coating. The corrosion test with potentiodynamic polarization method was performed to investigate the role of pH on the film quality and corrosion performances of the films. Further, the effect of current densities on corrosion resistance, thickness and hardness, have been investigated. Cyclic voltammetry technique has been used to test the electrochemical properties of the Zn–Ni–Co coating in acidic solutions. The results revealed that the increase in the current density favoured the increase in Ni and Co content in the deposit, showed higher corrosion resistance and higher cathodic current efficiency. The structural and morphological characteristics of the alloy coating have been obtained through scanning electron microscopy and X-ray diffraction techniques. The atomic force microscope was used to examine the topographic structure of the coating. X-ray Photoelectron spectroscopy was used to determine the chemical composition of alloy coatings and verified by energy dispersive X-ray analysis. The results indicate that a new and low-cost chloride bath for Zn–Ni–Co coating exhibit superior corrosion resistance properties and can be implement in various industrial applications such as automobiles, machine tools etc.[Figure not available: see fulltext.]. © 2020, Springer-Verlag GmbH Germany, part of Springer Nature.Item Compositionally Modulated Multilayered Zn-Co Deposits for Better Corrosion Resistance(Springer, 2020) Bhat, R.S.; Venkatakrishna, K.; Nayak, J.; Hegde, A.C.Zn-Co compositionally modulated multilayer alloy (CMMA) deposits have been developed onto mild steel using single bath technique. Multilayer alloy coatings have been galvanostatically produced using square current pulses. The switched cathode current density and number of layers have been designed for improved corrosion resistance. Experimental data revealed that multilayer coating with 120 layers at 10/30 mA/cm2 demonstrated ~ 125 times higher resistance to corrosion than monolayer alloy coating of the same thickness. The improved corrosion resistance of multilayer coatings is due to small changes in the wt.% cobalt, leading to change in the phase structure of deposit in alternate layers. The defects and failures occurring in a single layer in the deposition process are covered by the alternatively deposited coating layers. Therefore, the direction of the corrosive agent is extended or blocked. Further, the better corrosion resistances afforded by Zn-Co CMMA coatings were explained through changes in electronic properties at the interface, supported by Mott-Schottky’s plot. However, the decrease of corrosion resistance at a high degree of layering is attributed to the less relaxation time for redistribution of solutes in the diffusion layer, during plating. Potentiodynamic polarization and electrochemical impedance data showed its good protection ability. The enhanced corrosion resistance of multilayered deposits is due to small change in cobalt content, leading to alter the phase structure of the alternate-layers of the deposits. The structural morphology and the topographical structure of the coating were analyzed by scanning electron microscopy and atomic force microscopy. Evaluation of the chemical composition of the alloy coatings was carried out by x-ray photoelectron spectroscopy. © 2020, ASM International.Item Electrodeposition of Zn–Co Coating and its Electrochemical Performance(Pleiades journals, 2022) Bhat, R.S.; Manjunatha, K.B.; Venkatakrishna, K.; Hegde, A.C.Abstract: We report the acid chloride bath based electroplating of Zn–Co alloy on low carbon steel (LCS). As additives, the sulphanilic acid (SA) and gelatin were used for electroplating. The bath exhibited an anomalous co-deposition with a higher deposition of Zn over nobler Co. The role of bath composition, current density, partial current density, pH, and temperature on thickness, hardness, and corrosion resistance of deposit was studied. The corrosion behavior in 3.5 wt % sodium chloride solution and electrochemical behavior in acid chloride solutions of Zn–Co alloy coatings were studied using the potentiodynamic polarization method and cyclic voltammetry technique respectively. Mott–Schottky plot with positive slope confirms the development of n-type semiconductor layer at the interface of substrate and coating, which results in superior corrosion resistance of coatings. The colorimetric method has been used to estimate the composition of the deposit and further verified by energy dispersive X-ray spectroscopy (EDX) technique. The surface features and the topographical structure of the alloy film were obtained by scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques. The results indicate that the Zn–Co alloy films exhibited superior corrosion resistance with the lowest corrosion rate (138 µm y–1). Hence this alloy coating will find suitable applications in automobile and aerospace industries. © 2022, Pleiades Publishing, Ltd.