Electrolytic Synthesis and Characterization of Electrocatalytic Ni-W Alloy
(Springer New York LLC barbara.b.bertram@gsk.com, 2015) Elias, L.; Scott, K.; Hegde, A.
Inspired by the more positive (about 0.38 V nobler) discharge potential of hydrogen on Ni-W alloy compared to that on both Ni and W, a Ni-W alloy has been developed electrolytically as an efficient electrode material for water electrolysis. The deposition conditions, for peak performance of the electrodeposits for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) in 1.0 M KOH medium have been optimized. Electrocatalytic activity of the coatings, deposited at different current densities (c.d.’s) for water splitting reactions of HER and OER was tested by cyclic voltammetry and chronopotentiometry. It was found that Ni-W alloys deposited, at 4.0 A/dm2 (having about 12.49 wt.% W) and 1.0 A/dm2 (having about 0.95 wt.% W) are good electrode materials as cathode (for HER) and anode (for OER), respectively. A dependency of the electrocatalytic activity for HER and OER with relative amount of Ni and W, in the deposit was found. The variation of electrocatalytic activity with W content showed the existence of a synergism between high-catalytic property of W (due to low hydrogen overvoltage) and Ni (having increased adsorption of OH? ions), for hydrogen (as cathode) and oxygen (as anode) evolution, respectively. Electrocatalytic activities of the coatings, developed at different c.d.’s were explained in the light of their phase structure, surface morphology, and chemical composition, confirmed by XRD, FESEM, and EDX analysis. The effect of c.d. on thickness, hardness, composition, HER, and OER was analyzed, and results were discussed with possible mechanisms. © 2015, ASM International.
Impact of copper doping on the electrochemical response of MnSe2 as anode for lithium-ion battery
(Springer, 2024) Mukesh, P.; Lakshmi Sagar, G.; Brijesh, K.; Kumawat, S.; Hegde, A.; Kumar, A.; Nagaraja, H.S.
Transition Metal Chalcogenides (TMC), due to their unique physicochemical properties, are studied in various fields and have potent applications in energy storage applications. This work is based on the synthesis and characterization of copper-doped manganese di-selenide and the effect of its doping on electrochemical performance as anode material for lithium-ion battery applications using the solvothermal method. The characterization techniques used are X-ray diffraction, Raman spectroscopy, field-emission scanning electron microscopy, XPS, UV–visible absorption spectroscopy, and electrochemical analysis. The XRD data confirms the formation of MnSe2 exhibiting Cubic crystal geometry. The FESEM images show the micro-cube-like structure with agglomerated nanocluster nanostructures on the surface with a dimension of 100–200 nm. The doping of the copper has decreased the band gap of the MnSe2, as studied by the UV–visible absorption spectrum. The electrochemical performance is analyzed as anode material for lithium-ion batteries. The charge/discharge measurements show a specific capacity of 706 mAh g−1 as the initial discharge capacity and 336 mAh g−1 as the initial charge capacity at 0.1 A g−1 current density. Meanwhile, 3% Copper-doped MnSe2 showed a better specific capacity of 878 mAh g−1 as the initial discharge capacity and 461 mAh g−1 as the initial charge capacity at 0.1 A g−1 current density. Cyclic stability, rate capability, and electrochemical impedance spectroscopy were performed, and it shows that 3% copper-doped MnSe2 has good stability and better conductivity and charge kinetics, indicating copper doping has enhanced the electrochemical performance of pristine MnSe2. © The Author(s), under exclusive licence to Springer Science+Business Media, LLC, part of Springer Nature 2024.
Synergistic boost in Fe3O4 anode performance for li-ion batteries via Zn and Cu double doping and multi-walled carbon nanotube composite integration
(Elsevier B.V., 2024) Kumar, A.; Mukesh, P.; Lakshmi Sagar, G.; Hegde, A.; Nagaraja, H.S.
In this study, a novel nanocomposite material comprising pure Fe3O4 (FO), doped Zn0.5Cu0.5Fe2O4-3 (ZCFO-3), and Zn0.5Cu0.5Fe2O4-3@ Multi-walled carbon nanotube (ZCFO-3@MWCNT) nanocomposite material is carefully prepared using a simple one-step hydrothermal process. Comprehensive surface and morphological analysis are conducted using X-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), and High-resolution transmission electron microscopy (HRTEM), while compositional studies are investigated through Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The electrochemical performance is fully analyzed through Cyclic voltammetry (CV), Electrochemical impedance spectroscopy (EIS), rate capability tests, discharge/charge capacity, and cyclic stability evaluations. Among these three nanomaterials, ZCFO-3@MWCNT nanocomposite at 100 mA g−1 current density reveals the best performance, with a discharge capacity of 1974 mAh g–1, ZCFO-3 and FO reveal 1340 mAh g–1 and 1317 mAh g–1 respectively. After 800 cycles at 500 mA g−1 current density, ZCFO-3@MWCNT stays strong with a discharge capacity of 646 mAh g–1, while ZCFO-3 manages only 362 mAh g–1 and FO only 111 mAh g–1. After 1200 cycles at 500 mA g−1, the nanocomposite still delivers 518 mAh g–1. This study suggests that ZCFO-3@MWCNT could be a promising anode material for lithium-ion batteries. © 2024 Elsevier B.V.