Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
10 results
Search Results
Item Multi objective optimisation of thermally enhanced machining parameters of Inconel 718 using grey relational analysis(Inderscience Publishers, 2017) Ganta, V.; Kalichetty, K.S.; Dupadu, D.The present work investigates an experimental study of thermally enhanced machining of nickel-based superalloy Inconel 718 using uncoated tungsten carbide inserts. An inexpensive flame heating technique using an oxyacetylene flame is used as a heat source for thermal enhancement of workpiece. The effects of cutting parameters like cutting speed, feed rate, depth of cut and temperature of workpiece on the performance characteristics like surface roughness, tool wear and material removal rate were studied. A L27 orthogonal array with four parameters and three levels was adopted for experimental design. Multi response optimisation was done using grey relation analysis to simultaneously minimise surface roughness, tool wear and to maximise material removal rate. It was observed that at cutting speed at 85.21 m/min, feed rate at 0.048 m/min, depth of cut at 0.6 mm and workpiece temperature at 600°C were optimal cutting parameters. It is clearly shown that the above performance characteristics in thermally enhanced machining can be improved effectively through this approach. © © 2017 Inderscience Enterprises Ltd.Item Multi-objective optimisation of cryogenic turning process using Taguchi-based grey relational analysis(Inderscience Publishers, 2017) Sivaiah, P.; Dupadu, D.Cryogenic machining is a sustainable manufacturing approach; it eliminates coolant disposal cost, health problems compared to the conventional flood cooling. The present study investigates the multiple response optimisation of turning process while machining AISI 17-4 PH stainless steel under the cryogenic environment (jetting of liquid nitrogen at -196°C at the rake face of the tool) by using Taguchi-based grey relational analysis. The optimum levels of the machining parameters are cutting speed at 120.89 m/min, feed rate at 0.048 mm/rev, depth of cut 0.4 mm and physical vapour deposition (PVD) AlTiN coated tungsten carbide (WC). Taguchi-based grey relational analysis method reduced the cutting forces by 7.75%, improved the surface finish by 55.87%, and increased the material removal rate (MRR) by 154.76% and 25% increased the tool flank wear in cryogenic turning process. From the analysis of variance, it was identified that feed rate is the most influenced process parameter on turning performance characteristics. © © 2017 Inderscience Enterprises Ltd.Item Influence of cryogenic coolant on turning performance characteristics: A comparison with wet machining(Taylor and Francis Inc. 325 Chestnut St, Suite 800 Philadelphia PA 19106, 2017) Sivaiah, P.; Dupadu, D.Machining of 17-4 Precipitation Hardenable Stainless Steel (PH SS) is one of the difficult tasks because of its high cutting temperatures. Conventional cutting fluids are used to overcome the high cutting temperatures, but these are not acceptable from the health and environmental sustainable points of view. Cryogenic cooling is one of the potential techniques to overcome such problems. In the current work, comparison is made of cryogenic turning results, such as tool flank wear, cutting forces (feed force, main cutting force), cutting temperature, chip morphology and surface integrity characteristics with wet machining during machining of heat-treated 17-4 PH SS. The result showed that in cryogenic machining, a maximum of 53%, 78%, 35% and 16% reductions was observed in tool flank wear, cutting temperature, surface roughness and cutting force, respectively, when compared with wet machining. It was also evident from the experimental results that cryogenic machining significantly improved the machining performance and product quality even at high feed rates. © 2017 Taylor & Francis.Item Influence of Thermally Assisted Machining Parameters on the Machinability of Inconel 718 Superalloy(Springer Netherlands, 2017) Ganta, G.; Dupadu, D.The present study describes the effect of thermally assisted machining (TAM) parameters on the cutting force, tool wear and surface integrity characteristics (surface roughness, surface topography, and microhardness) of Inconel 718. An inexpensive flame heating technique using oxy-acetylene flame is used to heat the workpiece material. The TAM parameters such as cutting speed, feed rate, depth of cut, and workpiece temperature were selected as process parameters over cutting force, tool wear and surface integrity characteristics.The experimental results reveal that the cutting forces and surface roughness decrease with increases in cutting speed and workpiece temperature, while the workpiece temperature increases as tool wear decreases. The tool wear mechanisms observed were abrasive, adhesive, diffusion and notch wear. The XRD results of thermally assisted machining reveal that neither phase change nor broadening of the peaks were observed at different machining conditions. © 2017, Springer Science+Business Media Dordrecht.Item Machinability studies on 17-4 PH stainless steel under cryogenic cooling environment(Taylor and Francis Inc. 325 Chestnut St, Suite 800 Philadelphia PA 19106, 2017) Sivaiah, P.; Dupadu, D.Under higher cutting conditions, machining of 17-4 precipitation hardenable stainless steel (PH SS) is a difficult task due to the high cutting temperatures as well as accumulation of chips at the machining zone, which causes tool damage and impairment of machined surface finish. Cryogenic machining is an efficient, eco-friendly manufacturing process. In the current work, cutting temperature, tool wear (flank wear (Vb) and rake wear), chip morphology, and surface integrity (surface topography, surface finish (Ra), white layer thickness (WLT)) were considered as investigative machinability characteristics under the cryogenic (liquid nitrogen), minimum quantity lubrication (MQL), wet and dry environments at varying cutting velocities while machining 17-4 PH SS. The results show that the maximum cutting temperature drop found in cryogenic machining was 72%, 62%, and 61%, respectively, in contrast to dry, wet, and MQL machining conditions. Similarly, the maximum tool wear reduction was found to be 60%, 55%, and 50% in cryogenic machining over the dry, wet, and MQL machining conditions, respectively. Among all the machining environments, better surface integrity was obtained by cryogenic machining, which could produce the functionally superior products. © 2017 Taylor & Francis.Item Comparative evaluations of machining performance during turning of 17-4 PH stainless steel under cryogenic and wet machining conditions(Taylor and Francis Inc. 325 Chestnut St, Suite 800 Philadelphia PA 19106, 2018) Sivaiah, P.; Dupadu, D.Productivity in machining of 17-4 PH stainless steel is adversely affected by the premature failure of tool and poor surface finish as a consequence of high cutting temperatures. Conventional cutting fluids not only create environmental and health problems but also fail to overcome the high cutting temperatures during machining. Cryogenic cooling is an environmentally clean cooling technology for attractive management of machining zone temperatures. The present study investigates the effect of cryogenic liquid nitrogen (LN2 at ?196°C) on cutting temperatures, cutting forces (main cutting force, feed force), surface roughness, tool flank wear and chip morphology in turning of 17-4 PH stainless steel with AlTiN PVD-coated tungsten-coated carbide inserts and results were compared to wet machining. In overall, cryogenic machining reduces the cutting temperature, cutting forces, surface roughness and tool flank wear to a maximum of 73.4, 17.62, 44.29 and 55.55%, respectively. Improved chip breakability was found in cryogenic machining. © 2018 Taylor & Francis Group, LLC.Item Experimental investigation and optimization of machining parameters for sustainable machining(Taylor and Francis Inc. 325 Chestnut St, Suite 800 Philadelphia PA 19106, 2018) Varghese, V.; Ramesh, M.R.; Dupadu, D.A detailed investigation on the effects of cutting parameters and different cooling environments on machinability of austenitic stainless steel AISI 304 is presented in this study. The need for sustainable manufacturing and better surface quality urged to explore the merits of cryogenic cooling over the other conventional cooling techniques. The end milling experiments were designed based on three parameter and three-level design considering dry, wet, and cryogenic machining environments to have a comparative study. The machinability studies such as surface roughness, tool wear, cutting forces, chip morphology, and chip reduction coefficient were investigated and compared with different machining environments. The machining parameters were optimized using Taguchi-based grey relational analysis. The cryogenic machining had the most influence on milling of AISI 304 steel and resulted in the reduction of cutting forces, surface roughness, and chip reduction coefficient in comparison with the conventional wet and dry machining. © 2018, © 2018 Taylor & Francis.Item Influence of deep cryogenic treatment on performance of cemented carbide (WC-Co) inserts during dry end milling of maraging steel(Elsevier Ltd, 2019) Varghese, V.; Ramesh, M.R.; Dupadu, D.Cryogenic treatment has developed as a technique to improve the life of the cutting tool, especially tungsten carbide inserts. The present study investigates the effect of cryogenic treatment of cemented carbide (WC-Co) inserts at the different soaking period of 18 h (CT-18), 24 h (CT-24) and 32 h (CT-32) at a sub-zero temperature of ?196 °C. The soaking period plays a crucial role in improving the wear resistance of the cryogenically treated tools. It is vital to determine the critical soaking period for the cryogenic treatment of cemented carbides. The mechanical and metallurgical characterization of cryogenically treated cemented carbide insert is carried out to understand the changes in the microstructure, grain size, chemical composition, microhardness and electrical conductivity after cryogenic treatment. The end milling experiments on maraging steel under dry environment are carried out using cryogenically treated inserts at different holding time and untreated inserts (UT). The machining performance of treated and untreated inserts are compared with respect to tool wear, surface roughness and cutting forces. The results revealed that cryogenic treatment is effective in resisting tool wear even at high spindle speeds. The cryogenically treated inserts exhibited higher tool life, better surface finish and lower cutting forces during machining at different spindle speeds. The optimum soaking time for cryogenic treatment of WC-Co inserts is found to be 24 h (CT-24) beyond which there is no improvement in microhardness and wear resistance. © 2018Item Investigation on the performance of AlCrN and AlTiN coated cemented carbide inserts during end milling of maraging steel under dry, wet and cryogenic environments(Elsevier Ltd, 2019) Varghese, V.; K, A.; Ramesh, M.R.; Dupadu, D.The present study investigates the machining performance of AlCrN and AlTiN coated cemented carbide inserts during end milling of MDN 250 maraging steel. The mechanical and metallurgical characterization is carried out to determine the properties of the PVD coatings developed. The end milling experiments under dry, wet and cryogenic environment is carried out using coated uncoated inserts (UC) at different spindle speeds to evaluate the machining performance in terms of tool life, surface roughness and cutting forces. The coated inserts showed higher tool life, better surface finish, and low cutting forces during machining at different spindle speeds. It is found that the AlCrN coating had a better wear resistance and machining performance in comparison with AlTiN coating. The cryogenic environment reduced the surface roughness & cutting force and improved the tool life of the cutting tool compared to conventional dry and wet environment. It is revealed that coated tools along with cryogenic cooling can be employed for high-speed machining applications. © 2019 The Society of Manufacturing EngineersItem Experimental investigation of cryogenic end milling on maraging steel using cryogenically treated tungsten carbide-cobalt inserts(Springer, 2019) Varghese, V.; Ramesh, M.R.; Dupadu, D.The cryogenic machining and cryogenic treatment have already emerged as the sustainable manufacturing process of the future generation. The cryogenic treatment improves the cutting tool life, but the high cutting temperature developed during high-speed machining reduces the effect of cryogenic treatment of cutting tool. This study investigates the possible improvements in cutting tool life by combining cryogenic cooling and cryogenic treatment. The authors believe that these two techniques can replace conventional machining approaches using dry and wet machining conditions using coated carbide tools. The tungsten carbide-cobalt inserts are cryogenically treated (CT) at a soaking temperature of ? 195.8 °C for a period of 24 h and are used to evaluate milling performance under dry, wet, and cryogenic cutting environments. The machining experiments are conducted on maraging steel MDN 250 using one factor at a time approach by varying spindle speed and keeping feed rate and depth of cut as constant. The cutting force, surface roughness, tool wear, and subsurface microhardness are some of the machining responses evaluated and compared with an untreated cutting tool (UT). The tool life improved up to 24% during cryogenic machining using CT tools at a spindle speed of 270 rpm. © 2019, Springer-Verlag London Ltd., part of Springer Nature.