Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
3 results
Search Results
Item Corrosion behavior of novel AA1050/ZnO surface composite: A potential material for ship hull(Elsevier B.V., 2020) Bajakke, P.A.; Vinayak, V.R.; Jambagi, S.C.; Deshpande, A.S.Friction stir processing is one of the effective surface treatments which was employed to process the AA1050 sheets in bare and reinforced condition. The primary objective of the investigation was to expand the applications of AA1050 as a ship hull element in shipbuilding with the least corrosion rate to withstand the harsh marine environment. The base material processed with a rotational speed of 1200 rpm resulted in the highest corrosion rate of 0.173622 mpy. The formation of Al-Fe intermetallic phases was responsible for pitting corrosion. Further, processing by embedding zinc oxide with a rotational speed of 1000 rpm exhibited ~6.68 times improvement in corrosion resistance compared to as-received material. The corrosion rate was found to be 0.003390 mpy. The Al2O3 passive film hinders the initiation and propagation of pits. This study coins a novel composite material and future investigations are emphasized on the same lines. © 2020 Elsevier B.V.Item Unidirectional flipped multiple-pass friction stir process: an innovative step in the fabrication of in situ Al-Cu composites(Springer Science and Business Media Deutschland GmbH, 2024) Bajakke, P.A.; Vinayak, V.; Jambagi, S.C.; Bhajantri, V.; Deshpande, A.S.The in situ Al-Cu composites were manufactured by powder metallurgy with state-of-the-art microwave sintering tailed by friction stir process in two different ways: unidirectional overlapped two-pass and unidirectional flipped two-pass. Novelty is claimed in the flipped process. An attempt was made to investigate the addition of copper beyond the solubility limit and the critical composition of an Al-Cu alloy (4.6 wt.%). The overlapped process enforced higher temperature, cumulative strain, and strain rate. Since Al and Cu are high-stacking fault energy metals, both dynamic recrystallization and dynamic recovery occurred and resulted in grain refinement and higher fractions of Al2Cu. The self-hard and brittle nature of Cu and Al2Cu improved strength (Al-3wt.%Cu, 231.23 MPa), hardness (Al-6wt.%Cu, 82.5 HV), and deteriorated ductility (Al-7wt.%Cu, 5.2%). The formed Al2Cu at the interface were surrounded by Al particles and formed passive films Al2O3 and Cu2O enhanced corrosion resistance (Al-5wt.%Cu, 0.00717191 mpy). The process densely compacted the material, minimized porosity, decreased dislocation density, and increased strain aided in better electrical conductivity (Al-5wt.%Cu, 145.92%IACS). The flipped process circumvented excessive heating and embrittlement of the material thereby improving strength without loss of ductility (Al-7wt.%Cu, 235.85 MPa and 25.53%). Al-3wt.%Cu with minimum corrosion current (5.681 µA/cm2) exhibited maximum resistance to corrosion (0.169852 mpy). The highest electrical conductivity was noticed for (Al-5wt.%Cu, 104.17%IACS). © The Author(s), under exclusive licence to Springer-Verlag London Ltd., part of Springer Nature 2024.Item Comparative analysis of flipped and overlapped microwave sintered plus friction stir processed in-situ Al-Cu composites(Springer Nature, 2024) Vinayak, V.R.; Bajakke, P.A.; Jambagi, S.C.; Bhajantri, V.; Deshpande, A.S.The in-situ Al-Cu composites were fabricated with Cu content more than the solubility limit (5.65%) and the critical composition of an Al-Cu alloy (4.6%). A powder metallurgy route with state-of-the-art microwave sintering and friction stir process with overlapped and flipped conditions was attempted. The overlapped friction stir resulted in a minimum area of nugget region, unidirectional material mixing, high heat input in successive passes, and brittleness in the material. This accounted for the material to exhibit high strength with low ductility. Whereas flipped friction stir leads to a maximum area of stir zone, bidirectional material mixing, and similar thermal cycles in individual passes and avoids excessive heating. This facilitated the material to possess maximum strength by retaining ductility. The newly developed in-situ Al-Cu composite material (with Cu wt% in ranges of 8–12) possesses equivalent strength, ductility, electrical conductivity, and rate of corrosion compared to copper. Notably, these attributes, combined with its cost-effectiveness, position this material as a promising alternative to copper conductors in electrical applications. From the present investigation, it is strongly recommended to choose a flipped friction stir for better properties. © Qatar University and Springer Nature Switzerland AG 2024.