Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
8 results
Search Results
Item Tailoring surface characteristics of bioabsorbable Mg-Zn-Dy alloy using friction stir processing for improved wettability and degradation behavior(Elsevier Editora Ltda, 2021) Rokkala, U.; Bontha, S.; Ramesh, M.R.; Balla, V.K.; Srinivasan, A.; Kailas, S.V.Magnesium (Mg) and its alloys are currently under consideration for use as temporary implants. However, early degradation and maintaining mechanical integrity is a significant concern. Surface modification techniques are used to improve mechanical and corrosion properties of Mg based alloys. In the present study, friction stir processing (FSP) was used to tailor the surface characteristics of Mg-1Zn-2Dy (wt.%) alloy for temporary implant applications. The FSPed alloy was characterized using EBSD to understand the influence of FSP on crystallographic texture, grain size and grain boundaries and thereby their effect on corrosion, wettability and hardness. Results showed that the grain size of stir zone (SZ) was refined to less than 3 ?m, as a result of dynamic recrystallization (DRX) during FSP and the FSPed alloy exhibited better wettability than as-cast alloy. An increase in the hardness (11.7%) and elastic modulus (6.84%) of FSPed alloy were also observed. Electrochemical corrosion and weight loss methods were conducted in Dulbecco's Modified Eagle's Medium (DMEM) with, 10% Fetal Bovine Serum (FBS) physiological solution. The lower degradation rate (0.72 mm/yr) of FSPed alloy has been attributed to the fine grains and evenly distributed secondary phase particles. Further, the influence of grain boundary characteristics and crystallographic texture on the corrosion behavior have been investigated. © 2021 The Author(s).Item Influence of friction stir processing on microstructure, mechanical properties and corrosion behaviour of Mg-Zn-Dy alloy(Springer, 2023) Rokkala, U.; Bontha, S.; Ramesh, M.R.; Balla, V.K.In the present study, friction stir processing (FSP) was carried out on as-cast Mg-Zn-Dy alloy to tailor grain size and texture which alter the mechanical properties and corrosion behaviour. The grain size of the as-cast alloy was reduced from 60 ± 2 µm to 3 ± 0.1 µm after FSP due to dynamic recrystallization. The effect of grain size, crystallographic orientation and fine precipitates on mechanical properties were investigated using field emission scanning electron microscope (FESEM) and electron back scattered diffraction (EBSD). The ultimate tensile strength, yield strength, % elongation and hardness of FSPed alloy improved by 55%, 60%, 53% and 46% when compared to as-cast alloy. The FSPed Mg-Zn-Dy alloy exhibited a 79% decrease in corrosion rate when compared to as-cast alloy which can be attributed to grain refinement, uniform distribution of secondary precipitates and strong basal texture. The surface of FSPed sample after immersion corrosion exhibited calcium phosphate rich minerals which help in apatite formation on the sample surface. Cytotoxicity studies using MTT assay revealed more than 80% cell viability for both as-cast and FSPed alloy illustrating non-toxic nature of both the samples. The results of this study indicate that FSPed Mg-Zn-Dy alloy is a potential material for biodegradable implants due to its high strength, corrosion resistance and biocompatibility. Graphical Abstract: [Figure not available: see fulltext.]. © 2023, The Author(s), under exclusive licence to Springer Science+Business Media, LLC, part of Springer Nature.Item A study on the effect of process parameters and scan strategies on microstructure and mechanical properties of laser directed energy deposited IN718(Elsevier Ltd, 2023) Thanumoorthy, R.S.; Sekar, P.; Bontha, S.; Balan, A.S.S.The present study focuses on understanding the effect of scan strategy on the microstructure and mechanical properties of LDED fabricated IN718 built at optimized process conditions from single track analysis. Initially, single track studies were conducted by varying laser power, scan speed, and feed rate (3 levels) to optimize process parameters for bulk deposition. Based on the dilution, aspect ratio, track continuity and melt pool shape, best process parameter were chosen for depositing bulk structures. Bulk rectangular specimens were fabricated using the LDED process for different infill rotation (0°, 45°, 67°, and 90°) at optimized process conditions. Infill rotation did not show any significant change in the density of the samples. However, grain size measurement from EBSD and SEM micrographs revealed a substantial difference in grain size between samples without infill rotation (0°) and samples with infill rotation (45°, 67°, and 90°). XRD and EDS mapping revealed higher the formation of secondary laves phases with infill rotation as a result of higher cooling rate. Similarly, melt pool shape and arrangement showed significant variation with different infill angles. Samples with 0° and 90° infill rotation exhibited strong crystallographic texture along the build direction. There was a significant variation in the microhardness and tensile strength of the build with variation in infill rotation. This variation in mechanical properties were attributed to grain size, LAGB's fraction, secondary phases, and crystallographic texture. © 2023 Elsevier B.V.Item Effect of equiaxed grains and secondary phase particles on mechanical properties and corrosion behaviour of CMT- based wire arc additive manufactured AZ31 Mg alloy(Elsevier Ltd, 2023) Manjhi, S.K.; Sekar, P.; Bontha, S.; Balan, A.S.S.Wire arc additive manufacturing (WAAM) has drawn tremendous attention for manufacturing large and complex components of lightweight material at a moderate cost due to its high deposition rate and energy efficiency. Generally, WAAM-Mg alloy comprises columnar and columnar dendrite grains due to high cooling rates and thermal gradients responsible for anisotropic mechanical properties. To overcome this challenge, in this work, CMT-WAAM, which generally uses comparatively low heat input (33% lower than conventional WAAM), was used to deposit AZ31 Mg thin wall. The metallurgical characterization of the deposited thin wall of the top (T), middle (M) and bottom (B) sections reveals equiaxed grains of average sizes ∼ 58, ∼ 63 and ∼ 38 µm, respectively. In addition, TEM results exhibit the formation of secondary phase particles, i.e., β-Mg17Al12 and ɳ-Al8Mn5. Further, the ultimate tensile strength (UTS) and % elongation (% EL) in the travel direction (UTS = 224 MPa, % EL= 23.47%) are superior to that obtained in the build direction (UTS = 217 MPa, % EL = 20.82%). The corrosion resistance of WAAMed AZ31 Mg alloy is higher than wrought (cold rolled) AZ31 Mg alloy in Hank's balanced salt solution (HBSS). The results of this study reveal the potential of CMT-WAAM to deposit different grades of Mg with desired microstructure, mechanical properties and corrosion resistance. © 2023 CIRPItem Hybrid additive manufacturing of ER70S6 steel and Inconel 625: A study on microstructure and mechanical properties(Elsevier Ltd, 2023) Rodrigues, J.P.; Thanumoorthy, R.S.; Manjhi, S.K.; Sekar, P.; Arumuga Perumal, D.A.; Bontha, S.; Balan, A.S.S.Hybrid Additive Manufacturing (HAM) is currently being explored because of its potential to achieve trade-off between build capacity and feature resolution. The present study aims at fabricating ER70S6-Inconel 625 (IN625) bimetallic clad using hybrid Wire Arc Additive Manufacturing (WAAM) and Laser Directed Energy Deposition (LDED) processes. Microstructure evaluation was performed at the cross section of bimetallic clad for distinct materials as well as the interface. WAAM built ER70S6 revealed equiaxed ferritic grains, whereas laser deposited IN625 region showed columnar dendrites with under developed secondary arms. However, the first layer of IN625 exhibited columnar dendrite with secondary arms due to the influence of diffused Fe from the base ER70S6 steel under the action of concentrated laser heat source, which was revealed by energy dispersive spectroscopy (EDS) maps. The measured microhardness across the cross section of the deposit showed values corresponding to inherent material system. The interface did not reveal presence of any intermetallic phases which was confirmed by hardness results and X-Ray diffraction. Shear test revealed superior bond strength between the two materials, maintaining average strength of 452 MPa. The fractography images exhibited fine dimples along with cleavages indicating mixed fracture characteristics. This additive manufacturing method explores a new dimension in multi-material fabrication which, when customized for different materials, serve critical areas in the aerospace and defence sector. © 2023 Elsevier LtdItem Effect of deposition strategy and post processing on microstructure and mechanical properties of serviced Inconel 625 parts repaired using laser directed energy deposition(Elsevier Ltd, 2024) Chaurasia, J.K.; Jinoop, A.N.; Paul, C.P.; Bindra, K.S.; Balla, V.K.; Bontha, S.In the present work, an attempt is made to understand and explore the repair capabilities of the Laser Directed Energy Deposition (LDED) process on Nickel based superalloy Inconel 625 (IN625). Samples were extracted from a wrought plate of IN625 and then were subjected to a fatigue test to mimic a component in service for repairing. Further, deposition was carried out on these fatigued tensile sample surfaces i.e., Top, Top & bottom, One side and Both sides. The samples were also solution-treated at 1200 °C for 90 mins. Microstructure and mechanical properties were evaluated and then compared between the different deposition strategies and sample heat-treatment conditions. Tensile properties were compared for all the three sample conditions viz. wrought alloy, as repaired and solution treated. Results indicate sound deposition with minimal porosity in all the four deposition strategies using the LDED process with a mean deposit height of 1.02 ± 0.25 mm. Microstructural analysis revealed mixed dendrite and columnar structure in the case of as-deposited samples whereas, solution treated samples exhibited recrystallized equiaxed grains with the presence of annealing twins. The as-deposited samples show a ductile mode of failure with a maximum ultimate strength of 830 MPa, yield strength of 350 MPa and elongation of 72%. For solution treated samples, a maximum ultimate tensile strength of 620 MPa, yield strength of 270 MPa and elongation of 73% were observed. The strength of the material was found to be highly influenced by the solution treatment. © 2023 Elsevier LtdItem Effect of Build Orientation on Anisotropy in Tensile Behavior of Laser Powder Bed Fusion Fabricated SS316L(Springer, 2024) Thanumoorthy, R.S.; Chaurasia, J.K.; Anil Kumar, V.A.; Pradeep, P.I.; Balan, A.A.S.; Rajasekaran, B.; Sahu, A.; Bontha, S.In the present study, Stainless steel 316L (SS316L) cylindrical specimens were fabricated at two different build orientations and two different laser powers using Laser powder bed fusion process (LPBF). Microstructural characterization such as XRD, SEM, EBSD analysis and tensile testing were carried out on fabricated specimens in stress relieved condition to understand the anisotropic behavior of LPBF printed specimens. Horizontally oriented specimens showed higher tensile strength when compared to vertically oriented specimens for both laser powers. XRD and EBSD phase maps did not reveal the presence of any secondary phases. However, build orientation and laser power affected the crystallite size of the samples. Bimodal grain structure comprising coarse columnar grains and fine equiaxed grains were observed from the micrographs. With variation in build orientation, there was a significant change in the average grain size of the specimens. High dislocation density was observed in horizontally oriented samples built at low laser power because of dislocation annihilation that can occur at high temperatures. However, EBSD analysis revealed random weak crystallographic texture which does not vary significantly with laser power or build orientation. Variation in grain size, grain morphology, sub-grain features and dislocation density are the reasons for the anisotropic tensile behavior observed in LPBF printed SS316L coupons in stress relieved condition. © ASM International 2023.Item Tailoring the Microstructure and Mechanical Properties of Laser Powder-Directed Energy-Deposited Inconel 625 Using Scan Strategies(Springer, 2025) Aromal, S.S.; Malathesh, P.B.; Thanumoorthy, R.S.; Agasti, S.K.; Praharaj, A.K.; Anil Kumar, V.A.; Sudarshan Rao, G.S.; Bontha, S.The current study is focused on the influence of different scan strategies on the microstructural evolution, crystallographic texture, and mechanical properties of the Inconel 625 (IN625) fabricated using the laser powder-directed energy deposition (LP-DED) process. Prior to the deposition of the bulk specimens, an optimized set of process parameters (laser power (P), scan speed (v), and feed rate (f)) was selected through analysis of single-track deposits. The single tracks were thoroughly analyzed based on the aspect ratio, track stability, dilution, and shape of the melt pool. Further, six rectangular blocks of IN625 with different scan strategies (unidirectional ? 0°, bidirectional ? 0°, 45°, 67°, 90°, and spiral) were fabricated using the optimized process parameters for deposition. Samples with a 0° unidirectional scan strategy exhibited higher yield strength values but lower ductility. Notably, the sample with a scan orientation of 67° exhibited superior isotropic properties that are required to bear intense multi-axial loads when compared to other samples. The results indicated that the sample with a 67° scan orientation has the best combination of both strength and ductility. This can be attributed to finer cells/grains, which occur due to fragmentation of cells/grains during their growth across the successive layers, a higher fraction of low-angle grain boundaries (LAGBs), and variation of vector length within a layer. EBSD analysis revealed that samples with a 67° scan orientation exhibited a random crystallographic texture (MUD = 2.2), which suggests isotropic behavior compared to other samples. © ASM International 2025.